Effects of the Treated Chemicals on the Flexual and Physical Properties of Fire Retardant Treated Particleboards

내화처리(耐火處理) 파티클 보오드의 휨강도(强度)와 물리적(物理的) 성질(性質)에 미치는 약제(藥劑)의 영향(影響)

This research was performed to investigate the manufacturing possibility of the particleboard treated with commercial fire retardant chemicals. Laboratory test boards at this investigation were made from particles treated by soaking into 5, 10, 15, and 20 percent concentration solutions of ammonium sulfate and Minalith before resin was applied. According to the results, MOR (modulus of repture) and MOE (modulus of elasticity) in flexure exceeded type 100 (100 kgf/$cm^2$, $1.5{\times}10^4\;kgf/cm^2$) of the Korean Industrial Standard (KS F 3104). Except for 15 and 20 percent chemicals concentrations of Minalith, every internal bond stress values met type 100 (1.5 kgf/$cm^2$) of KS F 3104. However thickness swelling values of fire retardant treated particleboards were not reached in the Standard (12%).

본(本) 연구(硏究)는 내화처리(耐火處理) 파티클보오드의 휨강도(强度)와 물리적(物理的) 성질(性質)을 조사검토(調査檢討)함으로써 내화처리(耐火處理) 파티클보오드의 제조가능성(製造可能性)을 구명(究明)하고져 실시하였다. 본(本) 연구(硏究)에서는 목재(木材)파티클을 5, 10, 15, 그리고 20%농도(濃度)의 황산암모늄과 미나리스(Minalith) 용액(溶液)에 침적(沈積)시킨후 건조(乾燥)시켜서 제조(製造)하였다. 제조(製造)된 파티클보드의 휨강도(强度)와 물리적(物理的) 성질(性質)을 조사(調査)한 결과(結果)에 따르면 휨강도(强度)에서 파괴계수(破壞係數)와 탄성계수(彈性係數)는 한국공업표준규격(韓國工業標準規格) KS F 3104의 type 100수준(水準) (100kgf/$cm^2$, $1.5{\times}10^4kgf/cm^2$)을 만족 시켰으나 두께팽창율(膨脹率)은 모두 이 규격수준(規格水準)(12%)에 이르지 못하였다. 또한 박리저항(剝離抵抗)은 미나리스의 15와 20%농도(濃度)의 경우를 제외(除外)하고는 모두 한국공업표준규격(韓國工業標準規格) KS F 3104의 type 100 수준(水準)(1.5kgf/$cm^2$을 능가(凌駕)하였다.