• Carbon letters
• /
• 제2권2호
• /
• pp.99-104
• /
• 2001

Partial mesophase (PM) pitch precursor was prepared from fluidized catalytic cracking-decant oils (FCC-DO) by chemical reaction in the presence of $Br_2$. The PM pitch heated-treatment at $420^{\circ}C$ for 9 h exhibited the softening point of $297^{\circ}C$ with 23% yield, and 55% anisotropic content. The PM pitch precursor was melt-spun through circular nozzle by pressurized $N_2$, stabilized at $310^{\circ}C$, carbonized at $700^{\circ}C$, $1000^{\circ}C$, and $1200^{\circ}C$. The enough stabilization introduced 16.4% of the oxygen approximately. The stacking height ($L_{c002}$) and interlayer spacing ($d_{002}$) of the as-spun fibers were 4.58 nm and $3.45{\AA}$ and the value became minimum and maximum at $700^{\circ}C$ respectively in the carbonization procedure. The tensile strength increased with an increase in the heat treatment temperature exhibiting highest value of 750 MPa at $1200^{\circ}C$ carbonization.

• Korean Chemical Engineering Research
• /
• 제54권6호
• /
• pp.830-837
• /
• 2016

그라파이트 폼의 압축강도를 향상시키기 위하여 메조페이스 핏치를 공기분위기에서 산화안정화 한 후 다양한 불소 부분압으로 처리하였다. 불소화 처리된 메조페이스 핏치의 불소/탄소 표면화학 조성은 불소 부분압에 따라서 약 23.75%~61.48%의 범위를 가진다. 불소화 메조페이스 핏치기반 그라파이트 폼의 압축강도는 겉보기 밀도의 증가에 비례하여 증가되었다. 불소/탄소 표면화학 조성이 35.93%의 값을 갖는 메조페이스 핏치로부터 제조된 그라파이트 폼의 압축강도는 최대 $2.93{\pm}0.06MPa$의 값을 보여 주었으며, 이 값은 미처리된 메조페이스 핏치로부터 제조된 그라파이트 폼과 비교하여 27.95% 증가되었다. 이러한 결과는 표면에너지가 큰 불소 작용기로 인한 메조페이스 핏치간의 계면결합력이 그 압축강도를 증가시켰기 때문으로 여겨진다.