Preparation of Partial Mesophase Pitch-based Carbon Fiber from FCC-DO

Partial mesophase (PM) pitch precursor was prepared from fluidized catalytic cracking-decant oils (FCC-DO) by chemical reaction in the presence of $Br_2$. The PM pitch heated-treatment at $420^{\circ}C$ for 9 h exhibited the softening point of $297^{\circ}C$ with 23% yield, and 55% anisotropic content. The PM pitch precursor was melt-spun through circular nozzle by pressurized $N_2$, stabilized at $310^{\circ}C$, carbonized at $700^{\circ}C$, $1000^{\circ}C$, and $1200^{\circ}C$. The enough stabilization introduced 16.4% of the oxygen approximately. The stacking height ($L_{c002}$) and interlayer spacing ($d_{002}$) of the as-spun fibers were 4.58 nm and $3.45{\AA}$ and the value became minimum and maximum at $700^{\circ}C$ respectively in the carbonization procedure. The tensile strength increased with an increase in the heat treatment temperature exhibiting highest value of 750 MPa at $1200^{\circ}C$ carbonization.