• 동력기계공학회지
• /
• 제15권1호
• /
• pp.39-44
• /
• 2011

This study was to investigate the effects of stress ratio and anisotropy on Fatigue Crack Propagation(FCP) behavior of rolled magnesium alloy AZ31B. The experimental materials were a Mg-Al-Zn magnesium alloy. The FCP test was conducted on compact tension specimen by a servo-hydraulic fatigue testing machine in air at room temperature. Compact tension specimens were prepared from the extruded parallel and vertical rolling direction. The test condition was frequency of 10Hz and sinusoidal load stress ratios are 0.1 and 0.7. The FCP rates was automatically measured by a compliance method. In the case of the FCP of AZ31B, the FCP of both direction of LT and TL by anisotropy of specimens are almost same value. In lower stress ratio, the FCP of the LT, TL specimens are increased in lower ${\Delta}K$ region but higher ${\Delta}K$ regions are almost same value. Finally, the result of observed the surface crack, it expressed the quasi-cleavage fracture in lower ${\Delta}K$ region and straight mark on the aspect of the facet in high ${\Delta}K$ region.

• 한국해양공학회지
• /
• 제27권1호
• /
• pp.37-42
• /
• 2013

The presence of a crack can increase the local stress or strain, which can cause inelastic deformation and significantly reduce the life of a component or structure. Therefore, in this study, the fatigue crack growth (FCG) behaviors of friction stir welded Al 2024-T3 and Al 7075-T6 specimens were examined, with fatigue cracks growing parallel to the dynamically recrystallized zone at variable ${\Delta}K$ values and an R ratio of 0.3. In addition, the FCG values of the base metal Al 2024-T3 and Al 7075-T6 were tested under the same conditions and parameters as comparative groups. The results showed that compared with the base metal Al 2024 specimen, which had the best fatigue property, the welded specimen had only 88% of the fatigue cycles.

• 소성∙가공
• /
• 제12권5호
• /
• pp.493-497
• /
• 2003

The present investigation aims at visualizing the crack tip stress field using a mechanoluminescence material. The well known compound $SrAl_2O_4$:$Eu^{2+}$ was adopted as a mechanolurninescence material. Two more trivalent rare-earth elements such as Dy and Nd were taken into consideration as codopants to provide the appropriate trap levels. Samples of a variety of compositions were prepared by varing $Eu^{2+}$, $Dy^{3+}$, and $Nd^{3+}$ doping contents, for which the combinatorial chemistry method was used. In order to search for the optimum composition for the highest mechanoluminescence, the luminescence induced by a compressive device including a CCD camera. In parallel, a compact tension specimen was prepared by mixing the luminescence powders of optimum composition and epoxy resin. Crack initiation from the mechanically machined sharp note tip and its growth during loading were found to be associated with the extent of light emission from $SrAl_2O_4$.

• Geomechanics and Engineering
• /
• 제13권6호
• /
• pp.977-995
• /
• 2017

It is well accepted that rock failure mechanism influence the cutting efficiency and determination of optimum cutting parameters. In this paper, an attempt was made to research the factors that affect the failure mechanism based on discrete element method (DEM). The influences of cutting depth, hydrostatic pressure, cutting velocity, back rake angle and joint set on failure mechanism in rock-cutting are researched by PFC2D. The results show that: the ductile failure occurs at shallow cutting depths, the brittle failure occurs as the depth of cut increases beyond a threshold value. The mean cutting forces have a linear related to the cutting depth if the cutting action is dominated by the ductile mode, however, the mean cutting forces are deviate from the linear relationship while the cutting action is dominated by the brittle mode. The failure mechanism changes from brittle mode with larger chips under atmospheric conditions, to ductile mode with crushed chips under hydrostatic conditions. As the cutting velocity increases, a grow number of micro-cracks are initiated around the cutter and the volume of the chipped fragmentation is decreasing correspondingly. The crack initiates and propagates parallel to the free surface with a smaller rake angle, but with the rake angle increases, the direction of crack initiation and propagation is changed to towards the intact rock. The existence of joint set have significant influence on crack initiation and propagation, it makes the crack prone to propagate along the joint.

• 한국전산구조공학회논문집
• /
• 제28권3호
• /
• pp.309-316
• /
• 2015

상태 기반 페리다이나믹 모델은 일반적인 재료 구성 모델을 구현할 수 있고 비국부 영역 내에서 연결된 모든 결합의 변형을 통해 각 절점의 재료 응답이 결정되기 때문에 체적 및 전단 변형을 모두 표현할 수 있다. 따라서 상태 기반 모델은 복잡한 동적 취성 파괴 현상(분기균열, 2차 균열, 계단균열, 균열 유착 등)을 해석하는데 유용하다. 본 논문에서는 평면응력 탄성체에 대해 2차원 상태 기반 페리다이나믹 모델을 적용하고 에너지해방율과 페리다이나믹 에너지 포텐셜로부터 손상 모델을 구성하였다. 페리다이나믹 파괴 해석 모델을 통해 취성 유리 재료에 대해 균열 면에 평행한 압축 응력파가 균열 분기 패턴에 미치는 영향에 대해 조사하였다. 실험을 통해 관찰된 동적 균열 진전 및 분기 패턴에 대한 주요 특성들이 페리다이나믹 해석을 통해 확인되었다. 또한 강한 인장 하중 하의 계단균열과 이차균열 등이 상태 기반 페리다이나믹 시뮬레이션을 통해 잘 모사가 되는 것을 확인할 수 있었다.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2003년도 추계학술대회
• /
• pp.1186-1191
• /
• 2003

The 40% of wall criterion, which is generally used for the plugging of steam generator tubes, may be applied only to a single crack. In the previous study, a total of 9 failure models were introduced to estimate the local failure of the ligament between cracks and the optimum coalescence model of multiple collinear cracks was determined among these models. It is, however, known that parallel axial cracks are more frequently detected during an in-service inspection than collinear axial cracks. The objective of this study is to determine the plastic collapse model which can be applied to the steam generator tube containing two parallel axial through-wall cracks. Nine previously proposed local failure models were selected as the candidates. Subsequently interaction effects between two adjacent cracks were evaluated to screen them. Plastic collapse tests for the plate with two parallel through-wall cracks and finite element analyses were performed for the determination of the optimum plastic collapse model. By comparing the test results with the prediction results obtained from the candidate models, a plastic zone contact model was selected as an optimum model.

• Nuclear Engineering and Technology
• /
• 제36권4호
• /
• pp.316-326
• /
• 2004

The $40\%$ of wall criterion, which is generally used for the plugging of steam generator tubes, is applied only to a single crack. In a previous study, a total number of 9 failure models were proposed to estimate the local failure of the ligament between cracks, and the optimum coalescence model of multiple collinear cracks was determined among these models. It is, however known that parallel axial cracks are more frequently detected than collinear axial cracks during an in-service inspection. The objective of this study is to determine the plastic collapse model that can be applied to steam generator tubes containing two parallel axial through-wall cracks. Three previously proposed local failure models were selected as the candidates. Subsequently, the interaction effects between two adjacent cracks were evaluated to screen them. Plastic collapse tests for the plate with two parallel through-wall cracks and finite element analyses were performed to determine the optimum plastic collapse model. By comparing the test results with the prediction results obtained from the candidate models, a COD base model was selected as an optimum model.

• Nuclear Engineering and Technology
• /
• 제36권4호
• /
• pp.327-337
• /
• 2004

It is commonly required that tubes with defects exceeding $40\%$ of wall thickness in depth should be plugged; however, this criterion is too conservative for some locations and for some types of defects. Many studies have been done with the aim of developing an alternative plugging criteria, and these studies have shown that steam generator tubes with a certain range of axial through-wall cracks could remain in service without any safety or reliability problems. However, these studies have been limited, thus far, to consideration of single cracked tubes, necessitating a study on multiple cracks, which are commonly found. A crack coalescence model applicable to steam generator tubes with two collinear axial through-wall cracks was proposed in the previous study. In this paper, the investigation is extended to the parallel axial cracks spaced in a circumferential direction, because parallel axial cracks are more frequently detected during in-service inspections than collinear axial cracks. Interaction effects between two parallel cracks are evaluated by performing elastic and elastic-plastic finite element analyses.

• Computers and Concrete
• /
• 제2권5호
• /
• pp.345-366
• /
• 2005

This work presents an assessment of the computational performance of a vector-parallel implementation of probabilistic model for concrete cracking in 3D. This paper shows the continuing efforts towards code optimization as reported in earlier works Paz, et al. (2002a,b and 2003). The probabilistic crack approach is based on the direct Monte Carlo method. Cracking is accounted by means of 3D interface elements. This approach considers that all nonlinearities are restricted to interface elements modeling cracks. The heterogeneity governs the overall cracking behavior and related size effects on concrete fracture. Computational kernels in the implementation are the inexact Newton iterative driver to solve the non-linear problem and a preconditioned conjugate gradient (PCG) driver to solve linearized equations, using an element by element (EBE) strategy to compute matrix-vector products. In particular the paper analyzes code behavior using OpenMP directives in parallel vector processors (PVP), such as the CRAY SV1 and CRAY T94. The impact of the memory architecture on code performance, and also some strategies devised to circumvent this issue are addressed by numerical experiment.

• 한국재료학회지
• /
• 제3권1호
• /
• pp.84-94
• /
• 1993

GFRP복합재료의 피로거동은 하중형식, 재질 및 섬유의 강화구조, 환경적인 인자들의 영향을 크게 받는것으로 알려져 있다. 본 연구에서는GFRP의 피로거동에 미치는 증류수 흡습의 영향을 알아보기 위해 chopped strand glass mat강화 불포화 polyester수지 복합재료의피로특성을 조사하였다. 피로균열은 건조재와 흡습재 모두 피로 cycle초기에 발생하며 그 후 균열성장이 점차 둔화되는 영역과 가속되는 영역으로 나뉘어졌다. 또한 증류수의 흡습은 섬유와 기지재 사이의 결합력을 저하시키며 그로 인해 균영성장방향에 수직인곳에서의 fiber pull-out 발생과 균열성장방향에 있는 섬유들에서의 debonding이 증가하여 피로강도가 저하하였다.