• Restorative Dentistry and Endodontics
• /
• v.35 no.2
• /
• pp.69-79
• /
• 2010

The purpose of this study was to evaluate the effect of film thickness of various resin cements on bonding efficiency in indirect composite restoration by measurement of microtensile bond strength, polymerization shrinkage, flexural strength and modulus, fractographic FE-SEM analysis. Experimental groups were divided according to film thickness (< $50\;{\mu}m$-control, $50\;{\mu}m$-T50, $100\;{\mu}m$-T100, $150\;{\mu}m$-T150) using composite- based resin cements (Variolink II, Duo-Link) and adhesive-based resin cements (Panavia F, Rely X Unicem). The data was analyzed using ANOVA and Duncan's multiple comparison test (p < 0.05). The results were as follows ; 1. Variolink II showed higher microtensile bond strength than that of adhesive-based resin cements in all film thickness (p < 0.05) but Duo-Link did not show significant difference except control group (p > 0.05). 2. Microtensile bond strength of composite-based resin cements were decreased significantly according to increasing film thickness (p < 0.05) but adhesive-based resin cements did not show significant difference among film thickness (p > 0.05). 3. Panavia F showed significantly lower polymerization shrinkage than other resin cements (p < 0.05). 4. Composite-based resin cements showed significantly higher flexural strength and modulus than adhesive-based resin cements (p < 0.05). 5. FE-SEM examination showed uniform adhesive layer and well developed resin tags in composite-based resin cements but unclear adhesive layer and poorly developed resin tags in adhesive-based resin cements. In debonded surface examination, composite-based resin cements showed mixed failures but adhesive-based resin cements showed adhesive failures.

• The Journal of Korean Academy of Prosthodontics
• /
• v.39 no.2
• /
• pp.184-196
• /
• 2001

The objective of this study was to investigate the influence of resin cements and ceramic etching on shear bond strength of Empress 2 ceramic and observe the change of microstructure of ceramic according to etching time. Sixty-six square ceramic specimens($6{\times}6{\times}1.5mm$) were prepared. 6 specimens were etched with different etching times(0, 10, 20, 30, 40 and 60 seconds) and observed by means of a scanning electron microscope(SEM). Other sixty specimens were divided into 6 groups with 10 specimens in each group. 3 groups were etched with 4% hydrofluoric acid and each groups was bonded with 3 resin cements(Variolink II, Super-Bond C&B, Panavia F). Each specimen was subjected to a shear load in an Instron at a cross-head speed of 0.5mm/min and was observed with SEM after mechanical testing to establish modes of failure. The results were as follows : 1. Within etched groups, Variolink II and Super-Bond C&B exhibited significantly greater bonding strengths than Panavia F(p<0.05) 2. Bond strength of etching groups had three to five times greater than that of no-etching groups. 3. All of no-etching groups showed adhesive failure and etching groups mostly showed mixed failure. And, 20-second etching specimen showed the most distinct lithium disilicate crystal. so it is considered that 20-second etching is optimal time for bonding.

• The Journal of Korean Academy of Prosthodontics
• /
• v.39 no.3
• /
• pp.260-272
• /
• 2001

All-ceramic restorations have had a more limited life expectancy than metal ceramic restorations because of their low strength. Their relatively lower strength and resistance to fracture have restricted the use of all-ceramic crowns to anterior applications where occlusal loads are lower. But there has been increasing interest in all-ceramic restorations because patients are primarily concerned with improved esthetics. Many efforts have been made to in prove the mechanical properties of dental ceramics. This study was designed to elucidate the influence of the luting agent on the strength of the Empress 2 crown (staining technique) cemented on human teeth. Seventy extracted human permanent molar teeth were chosen. Teeth were prepared for Empress 2 crowns with milling machine on a surveyor. A dental bur was placed in the mandrel that was positioned so that the long axis of the bur was perpendicular to the surveyor base. Dimensions of the Empress 2 crown preparation were $6^{\circ}$ taper on each side, $1.5{\pm}0.1mm$ shoulder margin, and 4mm crown height. The luting cements used in this study were as follow: 1. Uncemented 2. Zinc phosphate cements (Confi-Dental) 3. Conventional glass ionomer cement : Fuji 1 (GC) 4. Resin-modified glass ionomer cements : Fuji plus (GC) 5. Adhesive cements : Panavia F (Kuralay), Variolink II (Vivadent), Choice (Bisco). Fracture test using Instron. The crowns were loaded in compressive force to evaluate the effect of these cements on the breaking strength of these all-ceramic crowns. A steel ball with a diameter of 4mm was placed on the occlusal surface and load was applied to the steel ball by a cylindrical bolt with a crosshead speed of 0.5mm per minute until fracture occurred. The fractured surface was examined using Scanning Electron Microscopic Image (SEM) to discover the correlation between fracture strength and bonding capacity. Within the limitation of this in vitro study design, the results were as follows : 1. fomentations significantly increased the fracture resistance of Empress ceramic crowns compared to control. Uncemented (206.9 N): ZPC (812.9 N): Fuji 1 (879.5 N): Fuji Plus (937.7 N): Choice (1105.4 N): Variolink II (1221.1 N): Panavia F (1445.2 N). 2. Resin luting agent, treated by a silane bond enhancing agents, yielded a significant increase in fracture resistance. In some of the Panavia F group, a fracture extended into dentin. 3. According to SEM images of fractured Empress crowns, the stronger the bond at both interfaces(crown and die), the more fracture strength was acquired.

• Restorative Dentistry and Endodontics
• /
• v.30 no.6
• /
• pp.493-504
• /
• 2005

This study was performed to investigate the compatibility between 4 dentin adhesives and 4 resin luting cements. Dentin adhesives used in this study were All-Bond 2 (Bisco Inc., Schaumbrug, IL, USA), Clearfil SE-Bond (Kuraray Medical Inc, Osaka, Japan), Prompt L-Pop (3M Dental Products, St. Paul, MN, USA), One-Up Bond F (Tokuyama corp., Tokyo, Japan) Resin luting cements used in this study were Choice (Bisco Inc., Schaumbrug, IL, USA), Panavia F (Kuraray Medical Inc, Osaka, Japan), RelyX ARC (3M Dental Products, St. Paul, MN, USA) Bistite II DC (Tokuyama corp., Tokyo, Japan). Combination of each dentin adhesive and corresponding resin cement was made to 16 experimental groups. Flat dentin surfaces was created on mid-coronal dentin of extracted mandibular third molars, then dentin surface was polished with 320-grit silicon carbide abrasive papers. Indirect resin composite block (Tescera, Bisco) was fabricated. Its surface for bonding to tooth was polished with silicon carbide abrasive papers Each dentin adhesive was treated on tooth surface and resin composite overlay were luted with each resin cement. Each bonded specimen was poured in epoxy resin and sectioned occluso-gingivally into 1.0mm thick slab, then further sectioned into $1.0{\times}1.0mm^2$ composite-dentin beams. Microtensile bond strength was tested at a crosshead speed of 1.0mm/min. The data were analysed by one-way ANOVA and Duncan's multiple comparison tests The results of this study were as follows, 2-step self-etching dentin adhesive which has additional bonding resin is more comparison than tests. self-etching dentin adhesive.

• Restorative Dentistry and Endodontics
• /
• v.33 no.6
• /
• pp.499-506
• /
• 2008

The purpose of this study was to compare the push-out strength of a fiber post cemented with various resin cements. Newly extracted 36 human mandibular premolars which had single root canal were selected and their crown portions were removed. The root canal was instrumented using $PROTAPER^{TM}$ system and obturated using continuous wave technique. In each root, a 9-mm deep post space was prepared. #2 translucent fiber post (DT Light post, Bisco Inc., Schaumburg, IL, U.S.A.) was cemented using injection technique with Uni-dose needle tip (Bisco) and six different resin cements. The tested resin cements were Duo-Link (Bisco Inc., Schaumburg, IL, U.S.A.), Variolink II (Ivoclar-Vivadent AG, Schann, Liechtenstein), Panavia F (Kuraray Medical Inc., Okayama, Japan), Multilink Automix (Ivoclar-Vivadent AG, Schann, Liechtenstein), RelyX Unicem (3M ESPE Dental Products, St. Paul, MN, U.S.A.), and Maxcem (Kerr Co., CA, U.S.A.). After storage in distilled water for 24 hours, each root was transversally sectioned into approximately 1-mm thick sections. This procedure resulted in 6 serial sections per root. Push-out test wasperformed using a universal testing machine (EZ Test, Shimadzu Co.) with a crosshead speed of 1 mm/min. The data were analyzed with one-way ANOVA and Tukey HSD (p=0.05). The push-out strength of the groups which cemented fiber post with Panavia F and Multilink Automix were lower than those of the other groups. But, there were no statistically significant difference among groups at a probability level of 0.05.

• The Journal of Advanced Prosthodontics
• /
• v.9 no.2
• /
• pp.77-84
• /
• 2017

PURPOSE. The aim of this study was to compare the surface roughness of zirconia when using Zircos E etching system (ZSAT), applying a nitric acid-hydrofluoric acid compound as a pretreatment agent, and also to compare the shear bonding strength according to different resin cements. MATERIALS AND METHODS. ZSAT, air abrasion, and tribochemical silicacoating were applied on prepared 120 zirconia specimens (10 mm in diameter, 7 mm in height) using CAD/CAM. Each 12 specimens with 4 different resin cements (Panavia F 2.0, Rely X Unicem, Superbond C&B, and Hot bond) were applied to test interfacial bond strength. The statistical analysis was performed using SAS 9.1 (SAS Institute Inc., Cary, NC, USA). The results are as follows: after application of the ZSAT on the zirconia specimens, surface roughness value after 2-hour etching was higher than those after 1- and 3-hour etching on SEM images. RESULTS. For Superbond C&B and Rely X Unicem, the specimens treated with ZSAT showed higher shear bond strength values than those treated with air abrasion and tribochemical silicacoating system. Regarding the failure mode of interface over cement and zirconia surface, Rely X Unicem and Hot bond showed cohesive failures and Panavia F 2.0 and Superbond C&B showed mixed failures. CONCLUSION. Zircos E etching system in zirconia restoration could increase its shear bond strength. However, its long term success rate and clinical application should be further evaluated.

• The Journal of Korean Academy of Prosthodontics
• /
• v.42 no.1
• /
• pp.30-40
• /
• 2004

Purpose : The purpose of this study was aimed to compare the shear bond strength on dentin of three dentin bonding agents and two resin cements used in conjunction with self-cured composite resin core material. Material and method : Control group and six experimental groups were divided for this study. Control group was designated as specimens bonded with Tenure$ A&B^{(R)}$. Experimental groups were as follows : PB-BL group : specimens bonded with Prime&Bond $NT^{(R)}$, $BondLink^{(R)}$ SB-BL group : specimens bonded with $^{(R)}$, BondLink$SingleBond^{(R)}$ PB group : specimens bonded with Prime&Bond $NT^{(R)}$ SB group : specimens bonded with $SingleBond^{(R)}$ PF group : specimens bonded with $Panavia-F^{(R)}$ BI group specimens bonded with Bistite $II^{(R)}$ All specimens were stored in $37^{\circ}C$ distilled water for 24 hours, followed by the shear bond strength was tested by universal testing machine. The data was analysed statistically by Mann-Whitney test. Results : 1. For Prime&Bond $NT^{(R)}$ and $SingleBonde^{(R)}$, the shear bond strength was 0.24 MPa and 7.19 MPa each by each, while Tenure $A&B^{(R)}$ group control was measured at 13.93 MPa (p<0.05). Especially for Prime&Bond $NT^{(R)}$ it did not get conjunction with dentin. 2. For Prime&Bond $NT^{(R)}$ and $SingleBond^{(R)}$ using $BondLink^{(R)}$, there was no significant difference as a result of 11.73 MPa and 14.00 MPa each by each (p<0.05). 3. For $Panavia-F^{(R)}$ and Bistite $II^{(R)}$, they showed the highest shear bond strength as measured by 18.24 MPa and 16.09 MPa each (p<0.05).

• Journal of Dental Rehabilitation and Applied Science
• /
• v.18 no.3
• /
• pp.157-170
• /
• 2002

The purpose of this study is to analyze the shear bond strength according to kinds of surface treatment agents and resin cements after acid etching of IPS Empress 2. For this purpose, test groups were classified into silane-treated bonding groups, silica-coated group and Targis link applied group. Then, nine bonding groups in total, each three groups per kind, were prepared by using three kinds of resin cements-Panavia F, Variolink II and Rely-X ARC, and thirty test specimens per group were prepared. To examine any changes in the oral environment, the shear bond strength of each test specimen was measured after dipping test for 24 hours and for five weeks, respectively, in distilled water at $37^{\circ}C$ and performing heat cycle 10,000 times in total, each 2,000 times per week, during a five weeks of dipping, under the condition similar to the oral environment. The bond failure modes were also observed by means of a scanning electron microscope. The results are summarized as follows 1. Statically significant differences between the surface conditioning materials were observed. The shear strength of the silane treatment was the highest of all three types of surface treatments(p<0.001). 2. Shear strengths varied significantly for different types of resin luting agents. But bond strength of Targis link surface treatments were not significantly different(p<0.05). 3. No significant difference of bonding strengths was found between storage time conditions(24 hours and 5 weeks). Only group II, IV, VII, IX were significantly different(p<0.05). 4. After thermocycling, the shear bond strengths of all groups were significantly decreased (p<0.05). Group III, V, VI were no significantly different. 5. On the SEM observation of fractured surfaces, all groups were shown complex failure.

• Imaging Science in Dentistry
• /
• v.48 no.2
• /
• pp.97-101
• /
• 2018

Purpose: This study evaluated the radiopacity of contemporary luting cements using conventional and digital radiography. Materials and Methods: Disc specimens (N=24, n=6 per group, ø$7mm{\times}1mm$) were prepared using 4 resin-based luting cements (Duolink, Multilink N, Panavia F 2.0, and U-cem). The specimens were radiographed using films, a complementary metal oxide semiconductor (CMOS) sensor, and a photostimulable phosphor plate (PSP) with a 10-step aluminum step wedge (1 mm incremental steps) and a 1-mm-thick tooth cut. The settings were 70 kVp, 4 mA, and 30 cm, with an exposure time of 0.2 s for the films and 0.1 s for the CMOS sensor and PSP. The films were scanned using a scanner. The radiopacity of the luting cements and tooth was measured using a densitometer for the film and NIH ImageJ software for the images obtained from the CMOS sensor, PSP, and scanned films. The data were analyzed using the Kruskal-Wallis and Mann-Whitney U tests. Results: Multilink (3.44-4.33) showed the highest radiopacity, followed by U-cem (1.81-2.88), Panavia F 2.0 (1.51-2.69), and Duolink (1.48-2.59). The $R^2$ values of the optical density of the aluminum step wedge were 0.9923 for the films, 0.9989 for the PSP, 0.9986 for the scanned films, and 0.9266 for the CMOS sensor in the linear regression models. Conclusion: The radiopacities of the luting materials were greater than those of aluminum or dentin at the same thickness. PSP is recommended as a detector for radiopacity measurements because of its accuracy and convenience.

• The Journal of Korean Academy of Prosthodontics
• /
• v.41 no.3
• /
• pp.369-378
• /
• 2003

Statement of Problem: Recently, resin cements have become more widely used and have been accepted as prominent luting cements. Current resin cements exhibit less microleakage than conventional luting cements. However, the constant contact with water and exposure to occlusal forces increase microleakage even in resin cements inevitably. Most bonding resins have been modified to contain a hydrophilic resin such as 2-hydroxyethylmethacrylate (HEMA) to overcome some of the problems associated with the hydrophobic nature of bonding resins. By virtue of these modifications, bonding resins absorb a significant amount of water, and there may also be significant stresses at bonding interfaces, which may adversely affect the longevity of restorations. Therefore the reinforcement of water stability of resin cement is indispensable in future study. Purpose: This study was conducted to examine the influence of water retention on microleakage of two resin cements over the period of 6 months. Materials and Methods: 32 extracted human teeth were used to test the microleakage of a single full veneer crown. Two resin cements with different components and adhesive properties - Panavia F (Kuraray Co., Osaka, Japan) and Super-Bond C&B (Sun Medical Co., Kyoto, Japan)- were investigated. The storage medium was the physiological saline solution changed every week for 1 month, 3 months, and 6 months. One group was tested after storage for 1 day. At the end of the each storage period, all specimens were exposed to thermocycling from $5^{\circ}C$ to $55^{\circ}C$ of 500 cycles and chewing simulation of 50,000 cycles, and then stained with 50% silver nitrate solution. The linear penetration of microleakage was measured using a stereoscopic microscope at ${\times}40$ magnification and a digital traveling micrometer with an accuracy of ${\pm}3{\mu}m$. Values were analyzed using two-way ANOVA test, Duncan's multiple range tests (DMRT). Results : Statistically significant difference of microleakage was shown in the 3-month group compared with the1-day or 1-month group in both systems (p<0.05) and there were statistically significant differences in microleakage between the 3-month group and the 6-month group in both systems (p<0.05). The two systems showed different tendency in the course of increased microleakage during 3 months. In Panavia F, microleakage increased slowly throughout the periods. In Super-Bond C&B, there was no significant increase of microleakage for 1 month, but there was statistically significant increase of microleakage for the next 2 months. For the mean microleakage for each period, in the 3-month group, microleakage of Super-Bond C&B was significantly greater than that of Panavia F. On the other hand, in the 6-month group, microleakage of Panavia F was significantly greater than that of Super-Bond C&B (p<0.05). Conclusion: Within the limitation of this study, water retention of two different bonding systems influence microleakage of resin cements. Further studies with the longer observation periods in viro are required in order to investigate water stability and the bonding durability of the resin cement. CLINICAL IMPLICATIONS Microleakage at the Cement-tooth interfaces did not necessarily result in the failure of the crowns. But it is considered to be a major factor influening the longerity of restorations. Further clinical approaches for decreasing the amount of microleakage are required.