• Resources Recycling
• /
• v.27 no.2
• /
• pp.32-37
• /
• 2018

This study was conducted as a preliminary study for the recycling of palladium and palladium oxide. In this study, thermodynamic equations for the formation of palladium oxide (PdO) are established. Palladium chloride is dissolved into hydrochloric acid to generate a palladium chloride solution. Nanosized palladium oxide powder with an average particle size below 30 nm were generated from this raw material solution by means of a spray pyrolysis process. The palladium oxide particles were composed of a single solid crystal. The results of XRD analysis showed that only a PdO phase of the generated powder was formed. And, the specific surface area of the generated palladium powder was approximately $32m^2/g$.

• Bulletin of the Korean Chemical Society
• /
• v.16 no.6
• /
• pp.479-483
• /
• 1995

The synergistic extraction of palladium(Ⅱ) was studied with 1,2-dichloroethane containing thenoyltrifluoroacetone (TTA; HA) and tri-n-octylphosphine oxide (TOPO; S). The main composition of synergistic adduct extracted into 1,2-dichloroethane phase was found to be PdA2S2. The equilibrium constants of the synergistic reaction were calculated. The application of this method to synthetic mixture for the separation of Pd from Pt was developed.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.139.1-139.1
• /
• 2013

Graphene and graphene oxide (GO) have been modified with palladium nanoparticles (Pd NPs) to develop high performance catalysts for the Sonogashira cross coupling reaction. To understand catalytic performance of Pd NPs on graphene (Pd/G) and Pd NPs on GO (Pd/GO), we monitored their morphological and electronic structural changes before/after Sonogashira reaction using FT-IR, XRD, XPS, and XAFS. Here, we demonstrate that both Pd/G and Pd/GO show high catalytic efficiency toward the Sonogashira reaction, but only Pd/GO revealed excellent recyclability. The remarkable catalytic efficiency of both catalysts is attributed to the high degree of the Pd NP dispersions on supports and thus smaller Pd NPs can provide highly reactive low coordinated Pd atoms. However, we attributed the excellent recyclability of Pd/GO to the presence of oxygen functionalities on GO, which can provide nucleation sites for the detached Pd atoms during the Sonogashira reaction and prevent agglomeration of the Pd NPs since the oxygen functional groups are very reactive to mobile Pd adatoms.

• Journal of the Korean institute of surface engineering
• /
• v.25 no.3
• /
• pp.107-116
• /
• 1992

The optimum thickness of Pd-Ni plated layers used as an electrical contact film was investigated by evaluating mechanical, thermal and environmental characteristics. The variations of morphologies and chemical compositions were studied by using SEM, EDS and ESCA. As a result of wear test, the wear resistance behavior of the gold plated layers was not changed with the sliding velocity changes. The palladium-nickel plated layer showed better wear resistance than the gold plated layer at low sliding velocity, but it showed poor wear resistance at high sliding velocity. Under the thermal condition of $400^{\circ}C$ in air, the gold thickness of $2\mu\textrm{m}$ without underplate on phosphorous bronze formed copper oxide on the surface layer by rapid diffusion of copper whereas the gold thickness of $0.8\mu\textrm{m}$ deposited on nickel and palladium-nickel underplate was stable at $400^{\circ}C$. Under the sulfur dioxide environments, the gold thickness of $0.3\mu\textrm{m}$ deposited on the nickel thickness of$ 3\mu\textrm{m}$ and the palladium-nickel thickness of $2\mu\textrm{m}$ underplate was more corrosion-resistant than the gold thickness of $2\mu\textrm{m}$ without underplate on phosphorous bronze. Under the nitric acid vapor environment, corrosion resistance of the gold film was superior to an equivalent thickness of the palladium-nickel film.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2011.05a
• /
• pp.114-114
• /
• 2011

Aluminum oxide surface에 palladium 전처리 공정을 이용하여 무전해 Ni-P 도금을 진행하였다. Ni-P도금액을 산성(pH 4.8~5.3)용액과 알칼리(pH 9~10)용액에 따른 각각의 도금 특성을 평가하였다. 또한 다양한 공정조건(온도, pH, 두께 등...)에서의 도금 특성과 미세구조를 분석하여 $Al_2O_3$막에 적합한 Ni-P 도금액과 공정조건을 개발하였다. 산성 Ni-P 도금액의 경우 pH 5.3, $90^{\circ}C$의 도금 조건에서 phosphorous 12.1 wt.%, 도금속도 274nm/min.의 Ni-P 도금막을 얻을 수 있었다.

• Bulletin of the Korean Chemical Society
• /
• v.35 no.7
• /
• pp.1979-1984
• /
• 2014

We have developed an efficient method to generate highly active Pd and PdO nanoparticles (NPs) dispersed on graphene and graphene oxide (GO) by an impregnation method combined with thermal treatments in $H_2$ and $O_2$ gas flows, respectively. The Pd NPs supported on graphene (Pd/G) and the PdO NPs supported on GO (PdO/GO) demonstrated excellent carbon-carbon cross-coupling reactions under a solvent-free, environmentally-friendly condition. The morphological and chemical structures of PdO/GO and Pd/G were fully characterized using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and transmission electron microscopy (TEM). We found that the remarkable reactivity of the Pd/G and PdO/GO catalysts toward the cross-coupling reaction is attributed to the high degree of dispersion of the Pd and PdO NPs while the oxidative states of Pd and the oxygen functionalities of graphene oxide are not critical for their catalytic performance.

• Korean Journal of Materials Research
• /
• v.24 no.10
• /
• pp.532-537
• /
• 2014

In this study, highly sensitive hydrogen micro gas sensors of the multi-layer and micro-heater type were designed and fabricated using the micro electro mechanical system (MEMS) process and palladium catalytic metal. The dimensions of the fabricated hydrogen gas sensor were about $5mm{\times}4mm$ and the sensing layer of palladium metal was deposited in the middle of the device. The sensing palladium films were modified to be nano-honeycomb and nano-hemisphere structures using an anodic aluminum oxide (AAO) template and nano-sized polystyrene beads, respectively. The sensitivities (Rs), which are the ratio of the relative resistance were significantly improved and reached levels of 0.783% and 1.045 % with 2,000 ppm H2 at $70^{\circ}C$ for nano-honeycomb and nano-hemisphere structured Pd films, respectively, on the other hand, the sensitivity was 0.638% for the plain Pd thin film. The improvement of sensitivities for the nano-honeycomb and nano-hemisphere structured Pd films with respect to the plain Pd-thin film was thought to be due to the nanoporous surface topographies of AAO and nano-sized polystyrene beads.

• Applied Chemistry for Engineering
• /
• v.10 no.4
• /
• pp.557-562
• /
• 1999

The reaction properties of Pd. Pd-Ce and Pd-La catalysts supported on ${\gamma}-Al_2O_3$ were investigated in the oxidation reaction of methane($CH_4$) exhausted from the compressed natural gas vehicle in a U-tube flow reactor with gas hourly space velocity of $72,000h^{-1}$. The catalysts were characterized by X-ray diffraction(XRD), X-ray photoelectron spectroscopy(XPS), BET surface area and hydrogen chemisorption. Pd catalyst prepared by $Pd(NO_3)_2$ as a palladium precursor and calcined at $600^{\circ}C$ showed the highest activity for a methane oxidation. Catalytic activity of calcined $Pd/{\gamma}-Al_2O_3$ in which most of palladium was converted into palladium oxide species was higher than that of reduced $Pd/{\gamma}-Al_2O_3$ in which most of palladium existed in palladium metal by XRD. As increasing the number of reaction cycles in the wide range of redox, the catalytic activity of $Pd/{\gamma}-Al_2O_3$ was decreased and the highly active window became narrower. Lanthanum oxide promoted Pd catalyst, $Pd/La/{\gamma}-Al_2O_3$ showed enhanced thermal stability compared with $Pd/{\gamma}-Al_2O_3$ even after aging at $1000^{\circ}C$, which was ascribed to the role of La as a promoter to suppress the sintering of palladium metal and ${\gamma}-Al_2O_3$ support. Almost all of methane was removed by the reaction with NO at the redox ratio of 1.2 in case of oxygen excluded steam, but that activity was significantly decreased in the steam containing oxygen.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.20 no.4
• /
• pp.458-463
• /
• 2019

Palladium (Pd) is widely used as a catalyst and noxious gas sensing materials. Especially, various researches of Pd based hydrogen gas sensor have been studied due to the noble property, Pd can be adsorbed hydrogen up to 900 times its own volume. In this study, palladium oxide (PdO) nanostructures were grown on Si substrate ($SiO_2(300nm)/Si$) for 3 to 5 hours at $230^{\circ}C{\sim}440^{\circ}C$ using thermal chemical vapor deposition system. Pd powder (source material) was vaporized at $950^{\circ}C$ and high purity Ar gas (carrier gas) was flown with the 200 sccm. The surface morphology of as-grown PdO nanostructures were characterized by field-emission scanning electron microscopy(FE-SEM). The crystallographic properties were confirmed by Raman spectroscopy. As the results, the as-grown nanostructures exhibit PdO phase. The nano-cube structures of PdO were synthesized at specific substrate temperatures and specific growth duration. Especially, PdO nano-cube structrures were uniformly grown at $370^{\circ}C$ for growth duration of 5 hours. The PdO nano-cube structures are attributed to vapor-liquid-solid process. The nano-cube structures of PdO on graphene nanosheet can be applied to fabricate of high sensitivity hydrogen gas sensor.

• Korean Journal of Metals and Materials
• /
• v.48 no.4
• /
• pp.347-352
• /
• 2010

This study reports a novel method off abricating highly sensitive hydrogen gas sensors based on PdO thin films. The PdO thin films with a thickness of 40 nm were deposited on Si substrates under Ar and $O_2$ ambient conditions using a reactive de magnetron sputtering system. Considerable changes in the resistance of the palladium oxide thin films were observed when they were initially exposed to hydrogen gas, as a result of the reduction process. The sensitivity of the PdO thin films was found to be as high as 90%. After the thin films were exposed to hydrogen gas, the nano-sized cracks were discovered to have formed on the surface of the PdO thin films. These types of nano-cracks that formed on the deoxidized PdO thin films are known to play a key role incausing a four-fold reduction of the response time of the absorption process. The results of this study demonstrate that deoxidized PdO thin films can be applied for use in the creation of high-sensitivity hydrogen sensors.