• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.109-112
• /
• 1999

The PZT(10/90)/(90/17) heterolayered thin films were fabricated by the spin-coaling on the Pt/Ti/SiO$_2$/Si substrate using the PZT(10/90) and PZT(70/10) metal alkoxide solutions. The effect of heterolayered thin films on the ferroelectrics and electrical properties have been investigated. The lower PZT layers provided the nucleation site for the formation of a perovskite phase of the upper PZT films. Dielectric constant increased with increasing the number of coatings, and it was about 569.9 at PZT-6 heterolayered films.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.489.2-489.2
• /
• 2014

The planar type flexible piezoelectric energy harvesters (PEH) based on PbZr0.52Ti0.48O3 (PZT) thin films on the flexible substrates are demonstrated to convert mechanical energy to electrical energy. The planar type energy harvesters have been realized, which have an electrode pair on the PZT thin films. The PZT thin films were deposited on double side polished sapphire substrates using conventional RF-magnetron sputtering. The PZT thin films on the sapphire substrates were transferred by PDMS stamp with laser lift-off (LLO) process. KrF excimer laser (wavelength: 248nm) were used for the LLO process. The PDMS stamp was attached to the top of the PZT thin films and the excimer laser induced onto back side of the sapphire substrate to detach the thin films. The detached thin films on the PDMS stamp transferred to adhesive layer coated on the flexible polyimide substrate. Structural properties of the PZT thin films were characterized using X-ray diffraction (XRD) and scanning electron microscopy (SEM). To measure piezoelectric power generation characteristics, Au/Cr inter digital electrode (IDE) was formed on the PZT thin films using the e-beam evaporation. The ferroelectric and piezoelectric properties were measured by a ferroelectric test system (Precision Premier-II) and piezoelectric force microscopy (PFM), respectively. The output signals of the flexible PEHs were evaluated by electrometer (6517A, Keithley). In the result, the transferred PZT thin films showed the ferroelectric and piezoelectric characteristics without electrical degradation and the fabricated flexible PEHs generated an AC-type output power electrical energy during periodically bending and releasing motion. We expect that the flexible PEHs based on laser transferred PZT thin film is able to be applied on self-powered electronic devices in wireless sensor networks technologies. Also, it has a lot of potential for high performance flexible piezoelectric energy harvester.

• Journal of the Korean Ceramic Society
• /
• v.30 no.4
• /
• pp.332-338
• /
• 1993

TiN/Ti is the best buffer layer between PZT thin film and si substrate among the Ti, TiN, ZrN, TiN/Ti, ZrN/Ti. The amorphous PZT films deposited on TiN/Ti buffer layer directly transform into perovskite phase when rapid thermal annealed for 30sec above 55$0^{\circ}C$. As Rapid Thermal Annealing(RTA) temperature increased, the remanent polarization(Pr) and dielectric constant($\varepsilon$r) increased and then showed Pr=21 $\varepsilon$r=593 when rapid thermal annealed 80$0^{\circ}C$ for 30sec. On the contrary the leakage current increased with increasing RTA temperature due to the formation of void made by Pb evaporationand grain cohesion.

• KIEE International Transactions on Electrophysics and Applications
• /
• v.3C no.2
• /
• pp.43-47
• /
• 2003

Lead zirconate titanate (PZT) thin films were fabricated by the pulsed laser ablation deposition (PLAD) method onto Pt/Ti/SiO$_2$/Si substrates. Crystalline phases as well as preferred orientations in PZT films were investigated by X-ray diffraction analysis (XRD). The well-crystallized perovskite phase and the (101) preferred orientation were obtained by two-step annealing at the conditions of $650^{\circ}C$, 1 hour. It was found that the temperature for the pulsed laser ablated PZT films annealed via a two-step annealing process can be reduced 20$0^{\circ}C$ compared to that of the conventional three-step annealing temperature profile for enhancing the transformation of the perovskite phase. The remanent polarization and the coercive field of this film were about 20 $\mu$C/$\textrm{cm}^2$ and 46 kV/cm, while the dielectric constant and loss values measured at 1 KHz were approximately 860 and 0.04, respectively. The interesting phenomena of this film, such as vertical shift in hysteresis curve, are also discussed.

• Electrical & Electronic Materials
• /
• v.7 no.2
• /
• pp.152-156
• /
• 1994

The rapid thermal annealing effects of Sol-Gel derived ferroelectric PZT thin films were investigated. It was found that rapid thermal annealing(RTA) of spin coated thin films on silicon typically >$800^{\circ}C$ for about 1 min. was changed to the perovskite phase. Rapid thermally annealed films recorded maximum remanent polarization of about 5 .mu.C/cm$^{2}$, coercive field of around 30kV/cm. The switching time for polarization reversal was about 220ns. The films of RTA process showed smooth surface, and high breakdown voltages of over 1 MV/cm and resistivity of $1{\times}{10^12}$ .ohm.cm at 1 MV/cm. It was verified that the polarization reversal of the PZT film was varied partially with applying the multiple short pulse.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1994.11a
• /
• pp.10-10
• /
• 1994

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1999.11a
• /
• pp.126-126
• /
• 1999

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1998.05a
• /
• pp.89-89
• /
• 1998

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1992.05a
• /
• pp.41-42
• /
• 1992

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1992.05b
• /
• pp.138-139
• /
• 1992