• Electrical & Electronic Materials
• /
• v.10 no.9
• /
• pp.889-894
• /
• 1997

A miniaturized wind-mill type ultrasonic motor which has diameter in 12.7 mm and thickness in 2.0mm using PMN-PZT piezoelectric ceramics was fabricated. The wind-mill type ultrasonic motors has only three plate and of two wind-mill shape slotted metal endcaps a rotor whose end is hollowed out so that its periphery fits with the shape of the stator and a bearing to guide the rotor. A Finite Element Analysis was carried out to obtain the endcaps behavior under a radial displacement change of piezoelectric disk and to optimize the structure of the number of slots. Increasing the applied voltage the revolution speed of ultrasonic motors was increased. The maximum speed of 700 rpm and the maximum torque of 0.22 nN·m of the wind-mill type ultrasonic motors were obtained.

• Transactions on Electrical and Electronic Materials
• /
• v.2 no.3
• /
• pp.18-23
• /
• 2001

For the piezoelectric transformer application, Pb(Sb$\_$1/2/ Nb$\_$1/2/)O$_3$-Pb(Zr,Ti)O$_3$ ceramics were produced by attrition milling. Microstructural, dielectric and piezoelectric characteristics of the ceramics were investigated as a function of milling time. The particle size and grain size decreased while dielectric constant, density and mechanical quality factor (Q$\_$m/) increased with milling time. Temperature coefficient of resonant frequency (TCf$\_$r/) was shifted to positive side with increasing milling time. The attrition milling process proved to be one of the effective routes to produce transformers for high power application.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.11a
• /
• pp.250-253
• /
• 1997

Generally, Piezoelectric ceramics based lead-zirconate-titanate(PZT) system are well known to use in high power devices. In this pacer. Pb(Mn$\sub$1/3//Sb$\sub$2/3/)O$_3$(PMS) ceramics which have been shown to be adaptable for a high power usage is introduced. The stability of piezoelectric properties in PZ-PT-PMS solid solution system such as piezoelectric constants. electromechanical coupling coefficient and mechanical quality factor is discussed by the addition effect of CeO$_2$ as a additive. The CeO$_2$ ratio ranges from 0 to 2 wt%. The resonant and anti-resonant frequencies. mechanical quality factor, and force factor are also measured as a function of vibration velocity

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.260-264
• /
• 1999

In this paper, the structural, dielectrial and piezoelectrical properties of 0.03Pb(Sb$\sub$1/2/Ti$\sub$0.495/)O$_3$+Xwt% MnO(x= 0, 0.3, 0.4, 0.5, 0.7) system ceramics were investigated as a function of the addition of MnO. As a result, the samples of 0.3wt% MnO content showed the highest mechanical quality factor(Qm) of 1487, and its dielectric constant and electro mechanical coupling factor(Kp) 1357, 54.3%, respectively. Therefore, the dielectrial and piezoelectrical properties of the composition ceramics were indicated as the materials suitable for piezoelectric transformer.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.3
• /
• pp.289-293
• /
• 2004

PNW-PMN-PZT ceramics were fabricated with the variations of Nb$_2$O$_{5}$ addition and their microstructural and piezoelectric characteristics were investigated. When the amount of Nb$_2$O$_{5}$ increased, grain size decreased gradually. At 0.3wt％ Nb$_2$O$_{5}$ which is the same weight percent with Fe$_2$O$_3$, maximum tetragonality(c/a) and density were shown due to the complexed doping effects. Also, this composition that showed Qm of 2,041, kp of 0.55, grain size of 2.5${\mu}{\textrm}{m}$ and $\varepsilon$r of 1704 were proper for high power application. Using this composition, Rosen-type piezoelectric transformer was fabricated as the size of 1 ${\times}$ 16 ${\times}$ 5㎣ and its electrical characteristics were investigated with the variations of load resistance and driving frequency. At the resistance of 200㏀, maximum step-up ratio of 13.68 was shown. After driving PDA CCFL for 25 min using the inverter circuit, at driving frequency of 214.4KHz, input voltage of 31.78 V and input current of 21.1mA were measured at the input part of piezoelectric transformer. And then, output voltage of 293.2 V and output current of 2.2mA were shown at the output part of piezoelectric transformer. At the same time, efficiency of 96.2％ and temperature rise of 3.5$^{\circ}C$ were appeared at the piezoelectric transformer.ormer.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.8
• /
• pp.483-488
• /
• 2016

Ultrasound imaging by using piezoelectric materials, such as lead zirconium titanate (PZT) has been one of the most preferred modes of imaging in the medical field due to its simple, low cost and non-ionizing radiation in comparison to other imaging techniques. Recently, the market demand for portable ultrasound is becoming larger with applications in developing countries, disaster area, military, and emergency purposes. However, most of ultrasound probes used is bulky and high power consumable, so unsuitable for such applications. In this study, the 3 layered ceramic specimen consisted of 128 pitches of $420{\mu}m$ in width and $450{\mu}m$ in thickness were prepared by using the Ti-rich PZT compositions co-fired at $1,050^{\circ}C$. Their electrical and ultrasound pulse-echo properties were investigated and compared to the single layer specimen. The 3 layered ultrasound probe showed 1.584 V of Vp-p, which is 3.2 times higher than single layered one, implying that it would allow effectively such a portable ultrasound probe system. The result were discussed in terms of higher capacitance, lower impedance and higher dielectric coefficient of the 3 layered ultrasound probe.

• Journal of the Korean Ceramic Society
• /
• v.37 no.4
• /
• pp.395-401
• /
• 2000

In this study, we chose the basic composition which indicated the best electrical properties by change of x content(0, 0.05, 0.1, 0.15, 0.2, 0.25 mol respectively) in xPb(Mn1/3Sb2/3)O3-(1-x)Pb(Zr0.52Ti0.48)O3 ceramics. And we substituted Cd2+ for Pb2+ site, then observed the sintering behavior, microstructure and electrical propertties according to the various sintering temperature. The basic composition was the 0.05PMS-0.95PZt, and it showed single perovskite phase and excellent properties. In case of Cd2+ substitution, we were able to sinter at 90$0^{\circ}C$ which was lower than conventional sintering temperature(1200~130$0^{\circ}C$). Especially, when the 2mol% substituted PMS-PZT specimens were sintered at 90$0^{\circ}C$ for 2h, we obtained the p=7.6g/㎤, kp=56%, Qm=520 and made sure of a position of Cd2+ substitution by observing lattice parameter, phase transition temperature. From this results, we could infer that because Cd2+ substituted fro A-site, low temperature sintering of Cd2+ substituted PMS-PZT without any loss of electrical properties shows its applicability for the piezoelectric ceramic transformer.

• Proceedings of the KIEE Conference
• /
• 1999.07d
• /
• pp.1726-1728
• /
• 1999

Dielectric and piezoelectric properties of xPb$(Al_{1/2}Ta_{1/2})O_3$-(1-x)Pb$(Zro_{0.52}Ti_{0.48})O_3$ system were investigated. The highest density of $7.80g/cm^3$ for PAT-PZT ceramics of 5mol% PAT was obtained. The relative permittivity of PAT-PZT ceramics of 5mol% PAT was 1.642 at room temperature. The maximum value of electromechanical coupling factor $k_p$ of 55% and $k_t$ of 33% were obtained at the composition of 5mol% PAT. The grain sizes were reduced by increasing the amount of PAT, however mechanical quality factor$(Q_m)$ had a minimum value of 44 at the composition of 5mol% PAT.

• The Journal of the Acoustical Society of Korea
• /
• v.6 no.4
• /
• pp.55-63
• /
• 1987

Modified $PbTiO_3$ piezoelectric ceramics added with 0.2, 0.25, 0.3 mol of $CaCO_3$ and 0.04 mol of $(Co_{\frac{1}{2}}W_{\frac{1}{2}})$ and 0.05 mol of $MnO_2$ and NiO have been fabricated. These ceramics can be poled sufficiently within 10 minutes at $100^{\circ}C$ under about d.c. field of 40 kv/cm. Detailed measurement was performed on dielectric constants, cutie temperatures, elastic and piezoelectric properties and coupling factors for the fabricated ceramics. The most value of the piezoelectric coupling factors was coupling factor of thickness mode kt and its value for 0.25 mol of Ca was about $45\%$. Dielectric constants of $\varepsilon_{33}^T$ and $\varepsilon_{11}^T$ for 0.25 mol of Ca were 242 and 260, and coupling factor ratio (kt/Kp) and Qm were 6 and 357 respectively.

• Transactions on Electrical and Electronic Materials
• /
• v.10 no.4
• /
• pp.121-124
• /
• 2009

In this study, in order to develop compositions of ceramics suitable for piezoelectric actuator and ultrasonic vibrator applications using low temperature sintering, multilayer, PMN-PNN-PZT ceramics were fabricated using $Li_2CO_3$ and $Na_2CO_3$ as sintering aids. Their structural, piezoelectric and dielectric characteristics were investigated according to the Zr/Ti ratio. As the Zr/Ti ratio increased, the electromechanical coupling factor $k_p$, and piezoelectric constant $d_{33}$ and the mechanical quality factor $Q_m$ all increased with Zr/Ti ratio and then decreased after the ratio exceeded 50/50. At the ratio of Zr/Ti =49/51 and sintering temperature of $900^{\circ}C$; the density, electromechanical coupling factor $k_p$, dielectric constant ${\varepsilon}_r$ piezoelectric $d_{33}$ constant and mechanical quality factor $Q_m$ all showed the optimum values of 7.900 $g/cm^3$, 0.576, 856, 312 pC/N, 1,326, respectively. These property values are very suitable for multilayer ceramics actuator applications.