• Membrane Journal
• /
• v.26 no.2
• /
• pp.116-125
• /
• 2016

This study described a synthesis of MF having a arsenic removal characteristics and the fundamental research was performed about the simultaneous removal system of both As(III) and As(V) ions with the composite nanofiber membrane (PMF) based on PVdF and MF materials for the water-treatment application. From the TEM analysis, the shape and structure of MF materials was investigated. The mechanical strength, pore-size, contact angle and water-flux analysis for the PMF was performed to investigate the possibility of utilizing as a water treatment membrane. From these results, the PMF11 showed the highest value of mechanical strength ($232.7kgf/cm^2$) and the pore-diameter of composite membrane was reduced by introducing the MF materials. In particular, their pore diameter decreased with an increase of iron oxide composition ratio. The water flux value of PMF was improved about 10 to 60% compared with that of neat PVdF nanofiber membranes. From the arsenic removal characterization of prepared MF materials and PMF, it was shown the simultaneous removal characteristics of both As(III) and (V) ions, and the MF01, in particular, showed the highest adsorption-removal rate of 93% As(III) and 68% As(V), respectively. From these results, prepared MF materials and PMF have shown a great potential to be utilized for the fundamental study to improve the functionality of water treatment membrane.

• 한국전기화학회:학술대회논문집
• /
• 2001.10a
• /
• pp.43-43
• /
• 2001

• Membrane Journal
• /
• v.18 no.1
• /
• pp.84-93
• /
• 2008

Poly(vinylidene fluoride) has received much attention in the last several years for the lithium secondary batteries. In this study, to enhance the porosity, PVdF was prepared by phase inversion method using as an additive, PEG (poly(ethylene glycol)), with N,N-dimethylformamid as a solvent. The pores are generated during the solvent and non-solvent exchange process in the coagulation bath filled with non-solvent (distilled water). The surface and cross-section of the membranes were observed with a scanning electron microscopy (SEM). The mechanical property of the membrane was determined by using an universal testing machine (UTM) and thermal property was verified by heat shrinkage. Uniformed sponge structure of PVdF-PEG membrane for the lithium secondary batteries was prepared with 10 wt% of PEG concentration in the PVdF-PEG solution. Porosity, elongation and tensile strengh of the membrane were 87%, 75.45%, and 275. 27 MPa respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.409-411
• /
• 2005

A series of inorganic-organic hybrid membranes were prepared with a systematic variation of titanium dioxidenanoparticles content. Their water uptake, methanol permeability and proton conductivity as a function of inorganic oxide content were investigated. The results obtained show that the inorganic oxide network decreases the proton conductivity and water swelling. It is also found that increase in inorganic oxide content leads to decrease of methanol permeability. In terms of the morphology, membranes are homogeneous and exhibit a good adhesion between inorganic domains and the polymer matrix. The properties of the composite membranes are compared with the standard nation membrane.

• Membrane Journal
• /
• v.25 no.4
• /
• pp.358-366
• /
• 2015

Flat membrane with $0.4{\mu}m$ pore size was prepared with PVdF (polyvinylidene fluoride) nanofiber, which has the advantages such as excellent strength, chemical resistance, nontoxic, non-combustibility. After that, spiral wound module was manufactured with it including a woven paper. Effect of pH was studied by comparing permeate fluxes and rejection rates of the spiral wound module using simulation solution including kaolin and humic acid. The recovery rate and filtration resistance were calculated after water back-washing at the end of filtration experiment. In addition, after the water filtrated by the spiral wound module was passed through a column filled with GAC (granular activated carbon), adsorption effect of GAC was investigated by measuring the turbidity and $UV_{254}$ absorbance.

• Membrane Journal
• /
• v.25 no.5
• /
• pp.431-439
• /
• 2015

The study was evaluated and compared to commercial heterogeneous membrane in order to make cation exchange membrane set up the optimal preparing condition. The research findings show that ion exchange resin was added more than 40 wt% in order to show chemical properties of HPVDF higher than commercial heterogeneous membrane. But ion exchange resin was added less than 40 wt% in order to show mechanical properties of HPVDF higher than commercial heterogeneous membrane. According to conditions above, Electrical resistance was $1.83{\Omega}{\cdot}cm^{-1}$, water uptake was 79%, ion exchange capacity was 1.60 meq/g, and burst strength was 0.97 MPa. Also The TDS remove efficiency was measured by approximately 40%.

• Membrane Journal
• /
• v.27 no.1
• /
• pp.68-76
• /
• 2017

Flat membrane with $0.4{\mu}m$ pore size was prepared with PVdF (polyvinylidene fluoride) nanofiber, which has the advantages such as excellent strength, chemical resistance, non-toxicity, and incombustibility. The spiral wound module was manufactured with the flat membrane and a woven paper. Hybrid water treatment process was composed of the PVdF nanofibers spiral wound microfiltration and granular activated carbon (GAC) adsorption column. Effect of GAC packing mass was investigated by comparing the case of recycling or discharging the treated water using the synthetic solution of kaolin and humic acid. After each filtration experiment, water back-washing was performed, and recovery rate and filtration resistances were calculated. Also, effect of GAC adsorption was compared by measuring turbidity and $UV_{254}$ absorbance. As a result, there was no effect of GAC packing mass on turbidity treatment rate; however, the treatment rate of $UV_{254}$ absorbance was 0.7~3.6% for recycling the treated water, and increased to 3.2-5.7% for discharging the treated water. In the case of recycling the treated water, reversible filtration resistance ($R_r$) and irreversible filtration resistance ($R_{ir}$) trended to decrease as increasing GAC packing mass; however, total fitration resistance ($R_t$) was almost constant, and recovery rate of water back-washing trended to increase a little.

• Membrane Journal
• /
• v.31 no.6
• /
• pp.417-425
• /
• 2021

As the demand for high-capacity batteries increases, there has been growing researches on the lithium metal anode with a capacity (3,860 mAh/g) of higher than that of conventional one and a low electrochemical potential (-3.040 V). In this study, using the anatase phased TiO₂ nanoparticles synthesized by hydrothermal synthesis, a PVdF-HFP/TiO₂ organic/inorganic composite material was designed and used as an interfacial protective layer for a Li metal anode. As-formed organic/inorganic-lithium composite thin film was confirmed through the crystalline structure and morphological analyses. In addition, the electrochemical test (cycle stability and voltage profile) confirmed that the protective layer of PVdF-HFP/TiO₂ composite (10 wt% TiO₂ and 1.1 ㎛ film thickness) contributed to the enhanced electrochemical performance of the lithium metal anode (Colombic efficiency retention: 90% for 77 cycles). Based on comparative test with the untreated lithium electrode, it was confirmed that our protective layer plays an important role to stabilize/improve the EC performance of the lithium metal negative electrode.

• 한국전기화학회:학술대회논문집
• /
• 2005.07a
• /
• pp.233-240
• /
• 2005

A series of inorganic-organic hybrid membranes were prepared with a systematic variation of titanium dioxidenanoparticles content. Their water uptake, methanol permeability and proton conductivity as a function of inoranic oxide content were investigated. The results obtained show that the inorganic oxide network decreases the proton conductivity and water swelling. It is also found that increase In inorganic oxide content leads to decrease of methanol permeability. In terms of the morphology, membranes are homogeneous and exhibit a good adhesion between inorganic domains and the polymer matrix. The properties of the composite membranes are compared with the standard nafion membrane.

• Proceedings of the KIEE Conference
• /
• 2005.11a
• /
• pp.194-196
• /
• 2005

A series of inorganic-organic hybrid membranes were prepared with a systematic variation of titanium dioxidenanoparticles content. Their liquid uptake, methanol permeability and proton conductivity as a function of inoranic oxide content were investigated. The results obtained show that the inorganic oxide network decreases the proton conductivity and liquid uptake. It is also found that increase in inorganic oxide content leads to decrease of methanol permeability. In terms of the morphology, membranes are homogeneous and exhibit a good adhesion between inorganic domains and the polymer matrix. The properties of the composite membranes are compared with the standard nafion membrane.