• Journal of the Korean Ceramic Society
• /
• v.45 no.10
• /
• pp.579-583
• /
• 2008

A porous $Al_2O_3$, scaffold coated with tricalcium phosphate(TCP) was fabricated by replica method using polyurethane(PU) foam as a fugitive material. Successive coatings of $Al_2O_3$ and hydroxyapatite(HAp) were applied via dip coating onto polyurethane foam, which has a slender and well interconnected network. A porous structure was obtained after sequentially burning out the foam and then sintering at $1500^{\circ}C$. The HAp phase was changed to TCP phase at high temperature. The scaffold showed excellent interconnected porosity with pore sizes ranging from $300{\sim}700{\mu}m$ in diameter. The inherent well interconnected structural feature of PU foam remained intact in the fabricated porous scaffold, where the PU foam material was entirely replaced by $Al_2O_3$ and TCP through a consecutive layering process. Thickness of the $Al_2O_3$ base and the TCP coating was about $7{\sim}10{\mu}m$ each. The TCP coating was homogeneously dispersed on the surface of the $Al_2O_3$ scaffold.

• Journal of the Korean Applied Science and Technology
• /
• v.24 no.2
• /
• pp.182-189
• /
• 2007

Used polyurethane was chemically degraded by treatments with flame retardants such as tris(3-chloropropyl) phosphate (TCPP), triethyl phosphate (TEP), and trimethyl phosphate (TMP). The structure of degraded products (DEP) was analyzed by FT-IR and P-NMR and it turned out to be phosphorus containing oligourethanes. Rigid polyurethane foam was produced by using the degraded products (DEP) as flame retardants. The flammability of recycled rigid polyurethane was investigated. The recycled polyurethane shows a reduced flammability over virgin polyurethane. In order to evaluate flame retardant properties of the recycled polyurethane foams with various amounts of DEP, the combustion parameters of the foam was measured by a cone calorimeter. Scanning electron micrograph of recycled PU shows the same uniform cell morphology as virgin PU.

• Polymer(Korea)
• /
• v.25 no.5
• /
• pp.679-690
• /
• 2001

High resilience PU foams were prepared with polyether type cell opener. The influences of cell opener concentration on the kinetics, rheology, structural stability morphology and open cell content of the obtained foam were investigated and the role of cell opener during cell opening was determined. And mechanical properties as a function of cell opener concentration were studied. It was observed that urea formation reaction was delayed due to high hydrophilicity of cell opener The decrease of viscosity and the increase of tan $\delta$ were confirmed with increasing cell opener concentration so that the resulted foam had low structural stability and high open cell content. The deterioration of matrix and uniform dispersion of hydrogen-bonded urea in matrix with cell opener concentration was revealed by SEM analysis. As a result, elastic properties of the foam matrix were decreased due to high hydrophilicity of cell opener during the preparation of high resilience polyurethane foam and foam with high open cell content resulted. Hardness, tensile strength, tear strength, elongation of foam were decreased with increasing cell opener concentration.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.05a
• /
• pp.44.2-44.2
• /
• 2009

BCP powder was synthesized using microwave hydrothermal process with mixed calcium hydroxide and phosphoric acid. After using replica method, porous BCP scaffold was fabricated. PU (Poly Urethane) was used as the fugitive skeleton to fabricate the porous scaffold. BCP powder was mixed in PVB (Polyvinyl butyral) and ethanol solution and then applied to the PU foam by dip coating. After several times of coating and the subsequent oven drying the coated PU foam was burnt out at $750^{\circ}C$ at air to remove the PU. The resulting networked porous composites were sintered at $1250^{\circ}C$, $1300^{\circ}C$ and $1350^{\circ}C$ in microwave furnace for 30 minutes. Material properties of the porous bodies like compressive strength and porosity were investigated. Detailed microstructure of the BCP porous body was characterized by SEM and XRD and TEM techniques. In our experiments, the relationship between mechanical property and viscosity of powder, sintering temperature was investigated.

• Journal of Korean Society of Occupational and Environmental Hygiene
• /
• v.24 no.3
• /
• pp.281-292
• /
• 2014

Objectives: The aim of this case study is to verify the chemical exposure reductions for various chemicals by substituting the ingredients of raw materials in a polyurethane(PU) foaming industry. The PU foaming process was making various passenger car seats from chemicals such as toluene diisocinate(TDI), methylene bisphenyl isocyanate(MDI) and polyols. Methods: Basic process data and workers' health effects could be gathered by interviewing managers and reviewing previous exposure monitoring data. Amine, aldehyde and isocyanate chemicals were analyzed following the NIOSH-NMAM. Area sampling methods rather than personal sampling were introduced for this field investigation. Results: Two amines, triethylene diamine(TEDA) and N,N,N',N'-Tetramethyl-1,6- hexanediamine(TMHDA) were identified in raw polyol, cured PU foam and air. The average concentrations of TEDA and TMHDA showd less than 1 ppm by area sampling; however, that caused halovision among workers in PU-PAD process. Aldehydes and isocyanates were detected in the air while the concentrations were relatively low compare to occupational exposure limits. Successful raw material substitution from nonreactive amine to reactive amine could reduces air-borne amine and aldehyde levels by about 70%. Halovision had been disappeared successfully in the process. Conclusions: Several amines caused halovision among workers in PU-PAD process, especially during summer season in spite of relatively low levels. Combination of reactive amines into urethane foam could reduced vapor generation into air, which resulted in the elimination of eye troubles in the process.

• Polymer(Korea)
• /
• v.25 no.4
• /
• pp.528-535
• /
• 2001

Polyurethane specimens were mainly composed of polyol, MDI, silicone surfactant, and water. The effects of ethylene glycol on the cell size, forming magnification, cream time, gel time, take free time, final free rising height, and reactive temperature were investigated. The cyclopentane was used for PU foam as a physical blowing agent. The components were hand-mixed at about 5000 rpm within 4 seconds at room temperature. The mixtures with various ethylene glycol contents were foamed in the wood mold. When the index of isocyanate was fixed, as the amount of ethylene glycol increased, cell size and thermal conductivity were decreased by about 5.1% and 14%, respectively.

• Fire Science and Engineering
• /
• v.20 no.4 s.64
• /
• pp.110-115
• /
• 2006

Polyurethane(PU) was mixtured by the treatment with flame retardants such as Tri(chloroisopropyl) phosphate(TCPP), Triethyl phosphate(TEP) and Trimethyl phosphate(TMP) at about $90^{\circ}C$. Rigid polyurethane foam was produced using the mixured products as flame retardants. The mechanical property and flammability of rigid polyurethane was investigated. The mixtured polyurethane shows reduced flammability over virgin polyurethane. Mechanical strength of mixtured polyurethane also shows as high as that of virgin polyurethane. In order to evaluate flame retardant properties of the mixtured polyurethane foams, heat release rate(HRR) of the foam was measured by cone calorimeter. Scanning electron micrograph of mixtured PU shows uniform cell morphology as virgin PU.

• Journal of the Korean Wood Science and Technology
• /
• v.26 no.4
• /
• pp.43-49
• /
• 1998

The availability of large quantities of waste woods provides an impetus for investigating woody biomass potential uses. Polyurethane (PU) foams are prepared with reacting isocyanates and polyols, and are used. in various industry fields. Thus, lignocellulosic waste raw-materials are proposed as replacement for synthetic polyol to PU foam formulation. In this study PU foams were manufactured from liquefied woods, methanediisocyanate(MDI), catalyst, foaming stabilizer, and viscosity aids. The polyol content, isocyanate.hydroxyl group (NCO/OH) ratio, and water content were varied to evaluate their effects on the foaming and water absorption of the PU foams. Less than 400 Molecular weight. of polyethylene glycol(PEG) and 1 to 3 solvent to woody raw-material ratio were desirable for liquefying woody materials. Liquefying rate was increased with more than 3 % addition of inorganic and organic catalysts and raising reaction temperature more than $150^{\circ}C$. Addition of starch enhanced liquefying of woody materials. Fourty percents of starch resulted in about 90% liquefying rates. Foaming rates were increased with increasing moisture contents of liquefied wood. Moisture contents of 0.6% resulted in 5 time-foaming rates, and seven percents of moisture contents more than 30 time-foaming rates. But, an increase in water content may result in a decrease in cross-links between wood polyol and isocyanate, because the NCO/OH ratio is constant. Increasing moisture contents have significantly decreased density of PU foams. The optimum water content should be about 2.5% or less in this adopted condition.

• Resources Recycling
• /
• v.26 no.6
• /
• pp.97-101
• /
• 2017

Metal foams have a cellular structure consisting of a solid metal containing a large volume fraction of pores. In particular, open pores which are penetrable pores are necessary for industrial applications such as in high temperature filters and as support for catalysts. In this study, Fe foam with greater than 90% porosity and 2-mm pore size was successfully fabricated using a slurry coating process and the pore properties were characterized. The Fe and $Fe_2O_3$ powder mixing ratios were controlled to produce Fe foam samples with different pore sizes and porosity. First, the slurry was prepared through the uniform mixing of powders, distilled water, and polyvinyl alcohol(PVA). The amount of slurry coated with the PU foam increased with increasing $Fe_2O_3$ mixing powder ratio, but the shrinkage and porosity of the Fe foams decreased, respectively, with increasing $Fe_2O_3$ mixing powder ratio.

• Tunnel and Underground Space
• /
• v.16 no.3 s.62
• /
• pp.241-250
• /
• 2006

Ice ring formation, one of the core techniques in LNG storage in a lined rock cavern, is investigated through hydro-thermal coupled analysis. An ice ring acts as a secondary barrier in case of leakage of cryogenic liquid and as a primary barrier for groundwater intrusion into an LNG cavern. Therefore, the thickness and location of the ice ring are crucial factors for the safe operation of an LNG storage cavern, especially for maintaining the integrity of a primary barrier composed of concrete, PU foam, and steel membrane. Through numerical analyses, the position and thickness of the ice ring are estimated, and the temperature and groundwater level are compared with measured values. The temperature md groundwater level by numerical analyses show good agreement with the field measurements when temperature-dependent properties and phase change are taken into account. The schemes used in this paper can be applied for estimation of ice ring formation in designing a full-scale LNG cavern.