• Electrical & Electronic Materials
• /
• v.6 no.6
• /
• pp.573-581
• /
• 1993

0.10Pb(Sb$_{1}$2/Sn$_{1}$2/)O$_{3}$-0.25PbTiO$_{3}$-0.65PbZrO$_{3}$ 세라믹을 소결온도 및 시간을 각각 1200-1250[.deg.C]에서 2, 4, 6시간으로 변화시켜 제작하였으며 시편의 소결조건 및 MnO$_{2}$(0~0.30mol%)첨가량에 따른 잡음특성을 관찰하였다. 초전계수 및 전압감도는 1250[.deg.C]에서 2시간 소결시킨 시편에서 각각 3.49x$10^{-8}$[C/$cm^{2}$K], 147[V/W]의 최대값을 나타내었다. 초전형 적외선 검출기의 잡음특성에 있어 증폭기의 전류잡음 .DELTA.V$_{i}$가 총 잡음전압에 대해 지배적인 경향을 나타내었으며 MnO$_{2}$가 0.24[mol%] 첨가된 1250[.deg.C]에서 2시간 소결시킨 시편에서 가장 양호한 pop-corn잡음특성을 나타내었다.다.

• Proceedings of the KIEE Conference
• /
• 1991.07a
• /
• pp.194-197
• /
• 1991

In this study, $(Pb_{0.99}La_{0.01})[(Sb_{1/2}Sn_{1/2})_{0.10}Ti_{0.25}Zr_{0.65}]O_3$, added $MnO_2$ (0-0.30[mol%]) ceramics were fabricated by the mixed oxide method. The sintering temperature and time were $1250[^{\circ}C]$, 2[hr], respectively. In the $(Pb_{0.99}La_{0.01})[(Sb_{1/2}Sn_{1/2})_{0.10}Ti_{0.25}Zr_{0.65}]O_3$ added $MnO_2$ (0.24[mol%]) specimens, relative dielectric constant and dielectric loss were minimum values 3.52, 0.003, respectively, and Curie temperature were highest values $256[^{\circ}C]$. Pyroelectric coefficient and voltage responsivity of the $(Pb_{0.99}La_{0.01})[(Sb_{1/2}Sn_{1/2})_{0.10}Ti_{0.25}Zr_{0.65}]O_3$, and added $MnO_2$ (0.24[mol%]) specimen were good values, $6.73{\times}10^{-8}[C/cm^2K],\;125[v/W]$, respectively. Figure of merit of pyroelectric current, voltage and detectivity of the specimen, $(Pb_{0.99}La_{0.01})[(Sb_{1/2}Sn_{1/2})_{0.10}Ti_{0.25}Zr_{0.65}]O_3$ added $MnO_2$ (0.24[mol%]) were good values $2.714{\times}10^{-8}[Ccm/J],\;7.706{\times}10^{-11}[Ccm/J],\;2.640{\times}10^{-8}[Ccm/J]$, respectively. Voltage responsivity of the $(Pb_{0.99}La_{0.01})[(Sb_{1/2}Sn_{1/2})_{0.10}Ti_{0.25}Zr_{0.65}]O_3$ added $MnO_2$ (0.24[mol%]) specimens were decreased with increasing the chopper frequency.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.41 no.5
• /
• pp.517-524
• /
• 1992

In this study, 0.10Pb(SbS11/2TSnS11/2T)OS13T-(0.90-x)PbZrOS13T (0.25 x 0.40) ceramics were fabricated by the atmospheric method. The sintering temperature and time were 1250[$^{\circ}C$] and 2[2hr], respectively. The structureal, dielectric and piezoelectric properties with composition of PbTiOS13T were studied. As the results of XRD ans SEM, the crystal structure of a specimen was rhombohedral, lattice constant and average grain size were decreased with increasing the contents of PbTiOS13T. Relative dielectric constant and Curie temperature were increased with increasing the contents of PbTiOS13T, 0.10PSS-0.40PT-0.50PZ specimen had the highest values of 904 and 265[$^{\circ}C$], respectively. In increasing of PbTiOS13T contents form 25[mol%] to 40[mol%], piezoelectric charge constant and electromechanical coupling factors were increased form 114[pC/N] to 142[pC/N], 17[%] to 24[%] and mechanical quality factor were decreased with increasing the contents of PbTiOS13T. In the 0.10PSS-0.40PT-0.50PZ specimens, those values were 14.2[kV/cm] and 9.43[x10S0-6TC/cmS02T], resectively.

• Transactions on Electrical and Electronic Materials
• /
• v.6 no.3
• /
• pp.119-123
• /
• 2005

$0.10Pb(Sb_{1/2}Sn_{1/2})O_3-0.25PbTiO_3-0.65PbZrO_3$ specimens doped with $ MnO_2\;(0.18\;mol\%)$ and $Y_2O_3\;(0\~0.4\;wt\%)$ were fabricated by the mixed-oxide method. All specimens showed the typical XRD patterns of a perovskite polycrystalline structure and the lattice constant decreased with increasing amount of $Y_2O_3$. The relative dielectric constant and the dielectric loss of the specimens doped with $0.2\;wt\%\;Y_2O_3$ were 704 and 0.0201, respectively. The remanent polarization, the coercive field and the pyroelectric coefficient of the specimen doped with $0.2\;wt\%\;Y_2O_3$ were $10.88\times10^{-2}Cm^{-2},\;11.12\times10^2kVm^{-1}$ and $5.03\times10^{-4}Cm^{-2}K^{-1}$ at $25^{\circ}C$, respectively. The figures of merit, $F_V$ for the voltage responsivity and $F_D$ for the specific detectivity, of the specimen doped with $0.2\;wt\%\;Y_2O_3$ were the good values of $3.04\times10^{-2}\;m^2C^{-1}\;and\;1.50\times10^{-5}\;Pa^{-1/2}$, respectively.