• Korean Chemical Engineering Research
• /
• v.50 no.4
• /
• pp.639-645
• /
• 2012

Waterborne polyurethane dispersion (PUD) was synthesized by capping the NCO groups of polyurethane prepolymers, prepared from isophorone diisocyanate, polycarbonate diol and dimethylol propionic acid, with aminopropyl triethoxysilane (APS). Subsequently, silylated acrylic polyurethane dispersion was synthesized by reacting the PUD with the mixture of acrylate monomers, 2-hydroxyethyl methacrylate and methyl methacrylate. The average particle size of silylated acrylic polyurethane dispersion, measured by the dynamic light scattering method, was increased from 39.0 nm to 399.8 nm by increasing the addition amounts of APS. Also, the pencil hardness of coating films of silylated acrylic polyurethane dispersion was enhanced from B grade to F grade with increasing APS content.

• Textile Coloration and Finishing
• /
• v.27 no.2
• /
• pp.126-131
• /
• 2015

Silica-polyurethane hybrid breathable films were prepared and their breathabilities were assessed. Appropriately aggregated silica was prepared through sol-gel reaction of water glass and its particle size ranged 360~500nm. The polyurethane dispersion was prepared by the reaction of isophorone diisocyanate(IPDI) as diisocyanate and polytetramethylene glycol(PTMG) and dimethylol propionic acid(DMPA) as polyol, particle size ranging 30~120nm. The reaction between isocyanate and hydroxyl group to form urethane bonding was checked by the intensity of the stretch peak of isocyanate at $2270cm^{-1}$ in the FT-IR. The silica was incorporated into polyurethane dispersion and casted into film. It was shown that the incorporated silica(1~5wt.%) increased water vapour permeability of the films by 30~100%, and decreased the hydrostatic pressure by 10~40%. From the results, it could be concluded that the appropriate hybridization of silica can increase the breathability of polyurethane dispersion film, while minimizing the loss of hydrostatic pressure.

• Corrosion Science and Technology
• /
• v.14 no.5
• /
• pp.207-212
• /
• 2015

The purpose of this research was to synthesize fluorine modified waterborne polyurethane dispersion (F-WPU) by soap-free (internal emulsifier) emulsion polymerization techniques, to prepare coating solution based on fluorine modified waterborne polyurethane dispersion (F-WPU) and to compare the chemical and thermo-mechanical properties on the electrogalvanized steel sheet. Environmentally friendly F-WPU was prepared with a fluorinated polyol containing 60 wt% of fluorine. There are various ways of combining a wide variety of fluorinated polyols and diisocyanate to exhibit novel properties of waterborne polyurethane dispersion. Components of coating solution were largely divided into 4 kinds i.e., F-WPU, acrylic emulsion, silane coupling agent, and colloidal silicate. F-WPU coating solution on the electro-galvanized steel sheet showed excellent properties of corrosion resistance, alkali resistance and heat resistance, as compared to other coating solutions using a general waterborne resin. The F-WPU coating solution's reliable effects are possibly due to the fluorine atoms incorporated even in a small amount of F-WPU.

• Korean Chemical Engineering Research
• /
• v.50 no.3
• /
• pp.403-409
• /
• 2012

Polyurethane prepolymers were prepared from poly (carbonate diol), isophrone diisocyanate, and dimethylol propionic acid. Then, aniline terminated waterborne polyurethane dispersion (ATWPUD) was synthesized by capping aniline on the NCO group of the prepolymer. Subsequently, ATWPUD was mixed with multi-walled carbon nanotube (MWCNT) to yield coating solutions, and the mixture was coated on the polycarbonate substrate. The surface resistance ($10^{7.6}{\sim}10^{7.7}{\Omega}/cm^2$) of coating films from ATWPUD showed better conducting properties than that ($10^{10.9}{\Omega}/cm^2$) from pure waterborne polyurethane dispersion (WPUD) when MWCNT was mixed. Also, the surface resistance of coating films was increased, but the pencil hardness and adhesion were decreased with increasing the amount of MWCNT added in the ATWPUD.

• Textile Coloration and Finishing
• /
• v.22 no.4
• /
• pp.362-372
• /
• 2010

This paper surveys the physical properties of the multiwall carbon nanotube (MWNT) and polyurethane composite film for improvement of mechanical properties and electrical characteristics. The modification of MWNT was carried out by acid treatment with nitric and sulphuric acid mixed solution, and then followed by thermal treatment for enhancing MWNT dispersion with polyurethane. This modified MWNT was mixed with polyurethane by changing the loading content of MWNT and dispersion time under the dimethylformamide solution in the ultrasonic wave apparatus. Various physical characteristics of the modified PU/MWNT films were measured and analyzed in terms of the loading content and dispersion time. The maximum absorbance of the PU/MWNT films were observed with the 2wt% loading at dispersion times of 2 and 24 hour, respectively. The minimum electrical volume resistivity of PU/MWNT film was shown at the loading content of 0.5wt% or more irrespective of dispersion treating time. However the optimum condition was assumed to 2wt% loading at dispersion time of 2 hours by assessing the surface profile of the film using video microscope. The breaking stress and strain of the PU/MWNT film decreased with increasing loading content, but no change of physical properties was shown with increasing in dispersion time.

• Korean Chemical Engineering Research
• /
• v.50 no.4
• /
• pp.614-620
• /
• 2012

Polyurethane prepolymers were prepared from poly (carbonate diol), isophrone diisocyanate and dimethylol propionic acid. Then, aniline terminated waterborne polyurethane dispersion (ATPUD) was synthesized by capping the NCO group of the prepolymer with aniline monomer. Subsequently, ATPUD and waterborne polyurethane dispersion (PUD), respectively, were blended with conducting polymer, poly (3,4-ethylenedioxythiophene)/polystyrene sulfonate [PEDOT/PSS], to yield antistatic coating solutions, and the mixture was coated on the polycarbonate substrates. At adequate addition amounts of PEDOT/PSS less than or equal to 2.5 g, the surface resistances ($1.0{\times}10^{11}{\sim}2.5{\times}10^8{\Omega}/cm^2$) of coating films from ATPUD showed better electronic conductivities than those ($5.0{\times}10^{11}{\sim}6.3{\times}10^9{\Omega}/cm^2$) from PUD. However, at excess amount of PEDOT/PSS of 3.0 g, the surface resistance from ATPUD showed similar electronic conductivity with that from PUD.

• Textile Coloration and Finishing
• /
• v.22 no.1
• /
• pp.43-50
• /
• 2010

The thermal treatment for carbon nanotube was applied to remove the water, metal catalyst and other impurities in carbon nanotube. The surface of carbon nanotube was changed into open structure with acid treatment by mixed solution of $HNO_3$ and $H_2SO_4$. The dispersion property of the functionalized and modified carbon nanotube was assessed with naked eyes by dispersing it in DMF. Carbon nanotube mixd polyurethane film was made to estimate the dispersion property by reflectance of the film with UV-Vis spectrometer. Also the internal structure of carbon nanotube was observed with SEM and TEM and thermal pyrolysis property of the carbon nanotube was measured by TGA and DSC. The surface modification of carbon nanotube by thermal and acid treatments improved the dispersion property of carbon nanotube/polyurethane mixed materials.

• Korean Chemical Engineering Research
• /
• v.52 no.4
• /
• pp.451-458
• /
• 2014

Waterborne polyurethane dispersion (WPUD) was prepared from polycarbonate diol (PCD), isophorone diisocyanate (IPDI) and dimethylol propionic acid (DMPA) as starting materials. Then, waterborne acrylic polyurethane dispersion (AUD) was synthesized by reacting the WPUD with different types of acrylate monomers, such as methyl methacrylate (MMA), 2-hydroxyethyl methacrylate (HEMA) and butyl acrylate (BA). Subsequently, the AUD was mixed with multi-walled carbon nanotube (MWCNT) to yield a conductive coating solution, and the mixture was coated on the polycarbonate substrate. The pencil hardness, abrasion resistance and chemical resistance of the coating films from AUD were improved than those from WPUD, while the electrical conductivity of the coating films from AUD was decreased than that of WPUD. Also, the effect of acrylate types on the properties of coating films was investigated. The AUD obtained from HEMA showed the strongest pencil hardness, while the AUD obtained from MMA exhibited the strongest abrasion resistance, chemical resistance and electrical conductivity among several types of acrylate monomers.

• Korean Chemical Engineering Research
• /
• v.51 no.1
• /
• pp.73-79
• /
• 2013

Waterborne polyurethane dispersion (WPUD) was synthesized from polycarbonate diol (PCD), isophorone diisocyanate (IPDI) and dimethylol propionic acid (DMPA) as starting materials. Then, waterborne acrylic polyurethane dispersion (AUD) was synthesized by reacting the WPUD with an acrylate monomer, methyl methacrylate (MMA). Subsequently, the AUD was mixed with multi-walled carbon nanotube (MWCNT) to yield a conductive coating solution, and the mixture was coated on the polycarbonate substrate. With increasing the amount of MMA in the AUD, the pencil hardness, abrasion resistance and chemical resistance of the coating films were improved, but the electrical conductivity of the coating films was decreased. On the other hand, the pencil hardness, abrasion resistance and chemical resistance of coating films were decreased, but the electrical conductivity was enhanced with increasing the amount of MWCNT in the conductive coating solutions.

• Journal of the Korean Applied Science and Technology
• /
• v.18 no.3
• /
• pp.241-247
• /
• 2001

Aqueous urethane dispersion resin begins to assume commercial importance due to increasing environmental awareness of VOC in coating industry. Moreover there have been strong industrial needs for the development of reactive-type polyurethane flame retardant coatings. In this study, chlorinated polyester polyols were synthesized by two step polycondensation reaction using mono chloroacetic acid, adipic acid, trimethylol propane, and 1,4-butanediol. In the next step polyurethane dispersion was prepared using these chlorinated polyester polyols and isophorone diisocyanate with dimethylol propionic acid(DMPA) and trimethylamine. The structure of chlorinated polyol was characterized by GPC, FT-IR and NMR. Particle size and its distribution were examined in terms of various dispersion parameters including molecular weight and composition of polyol, amount of DMPA, and NCO/OH ratio, etc. The effect of chlorinated polyols on flammability was also evaluated.