Copolyamic acid PMDA/6FDA-PDA(PAA) and homopolyamic acids PMDA-PDA(PAA) and 6FDA-PDA(PAA) were synthesized from 1,2,4,5-benzenetetracarboxylic dianhydride(PMDA) and 2,2'-bis(3,4-dicarboxyphenyl) hexafluoropropane dianhydride(6FDA) as the dianhydride and 1,4-phenylenediamine (PDA) as the diamine. Residual stresses were detected in-situ during thermal imidization of the co- and homopolyimide precursors as a function of processing temperature over the range of $25{\sim}400^{\circ}C$ using thin film stress analyzer(TFSA), and morphological structures were investigated by WAXD. In comparison, the resultant residual stress of polyimide films composed of different compositions decreased with the increasing content of PMDA unit in the chain and was about 5 Mpa in compression mode for PMDA-PDA. In this study, the synthesis of random PMDA/6FDA-PDA copolyimide could be completed and compensate for the difficulty of process due to high $T_g$ of PMDA-PDA and relatively higher stress of 6FDA-PDA. It showed that we can make a low level stress copolyimied having excellent mechanical properties by incorporating appropriate rod-like rigid structure PMDA-PDA unit into 6FDA-PDA polyimide backbone which generally shows higher stress due to rotational hinges such as bulky di(trifluoromethyl). Specially, PMDA/6FDA-PDA(0.9:0.1:1.0) satisfied excellent mechanical property and low level stress as an inter layer showing low dielectric constant.

• Applied Chemistry for Engineering
• /
• v.9 no.2
• /
• pp.306-310
• /
• 1998

The soluble polyimides(PMDA/diamine/dianhydride) were prepared and investigated. After coating the prepared PMDA/diamine/dianhydride solution into the commercial tubular alumina ceramic membranes, gas permeation characteristics was investigated. $T_g{\prime}s$ of the polyimides were in the range of $337{\sim}358^{\circ}C$ and thermal stability was good. The polymer was soluble in NMP, DMAc, DMSO, THF, and m-cresol. The adhesion between the alumina membrane and the soluble polyimide was excellent. The soluble polyimide/alumina membranes containing 6FDA showed the highest permeability among others. The permeability of nitrogen of PMDA/1,3PDA/6FDA-alumina membrane was about $7.6{\times}10^{-7}(mol/m^2{\cdot}Pa{\cdot}s)$ in the gas permeation experiments. The ideal separation factor of $O_2/N_2$ and $H_2/N_2$ in PMDA/1,3PDA/6FDA-alumina membrane were 6.19, and 70.0, respectively.