• Journal of the Microelectronics and Packaging Society
• /
• v.13 no.4
• /
• pp.51-56
• /
• 2006

Polymer light emitting diodes (PLEDs) with ITO/EDOT:PSS/PVK/PFO-poss/LiF/Al structures were prepared by the spin coating method on ITO(indium tin oxide)/glass substrates. PFO-poss[Poly(9,9-dioctylfluorenyl-2,7-diyl) end capped with poss] was used as light emitting polymer. PVK[poly(N-vinyl carbazole)] and PEDOT:PSS [poly(3,4-ethylenedioxythiophene):poly(styrene sulfolnate)] polymers were used as the hole injection and transport materials. The effect of PFO-poss concentration and the heating temperatures on the electrical and optical properties of the devices were investigated. At the same concentration of PFO-poss solution, the current density and luminance of PLED device tend to increase as the annealing temperature increase from $100^{\circ}C$ to $200^{\circ}C$. The maximum luminance was found to be about 958 cd/m2 at 13V for the PLED device with 1.0 wt% PFO-poss at the annealing temperature of $200^{\circ}C$. In addition, the PLED device showed bluish white emission through the strong greenish peak with 523 nm in wavelength. As the concentration of PFO-poss increase from 0.5 wt% to 1.0 wt% and temperature of PLEDs increase from $100^{\circ}C$ to $200^{\circ}C$, the emission color tend to be shifted from blue with (x, y) = (0.17,0.14) to bluish white with (x, y) : (0.29,0.41) in CIE color coordinate.

• Proceedings of the Korean Society Of Semiconductor Equipment Technology
• /
• 2006.10a
• /
• pp.154-157
• /
• 2006

ITO(indium tin oxide)/glass 기판 위에 PEDOT:PSS[poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate)]와 PVK[poly(N-vinyl carbazole)] 고분자 물질을 정공 주입 및 수송층으로, 발광층으로 PFO-poss[Poly(9,9-dioctylfluorenyl-2,7-diyl) end capped with POSS]를 사용하여 스핀코팅법과 열 증착법으로 ITO/PEDOT:PSS/PVK/PFO-poss/LiF/Al 구조의 고분자 발광 다이오드를 제작하였다. PFO-poss 유기발광 층의 열처리 조건 (온도, 시간)이 PLED 소자의 전기적, 광학적 특성에 미치는 영향을 조사하였다. 1 wt%의 농도를 갖는 PFO-poss 유기물 발광 층을 200C 온도로 3시간 열처리 할 경우 11 V 인가전압에서 $1497\;cd/m^2$의 최대 휘도를 나타내었다. 동일온도에서 열처리 시간을 1시간에서 3시간으로 증가시킬 경우 휘도의 증가와 함께 발광 개시온도가 감소하는 경향을 보여주었다. 또한 열처리 온도와 시간을 증가시킬 경우 제2발광피크인 excimer 피크가 크게 나타났으며 청색에서 황색 발광 쪽으로 천이되는 경향을 나타내었다.

• Korean Journal of Materials Research
• /
• v.19 no.6
• /
• pp.313-318
• /
• 2009

Polymer Light Emitting Diodes (PLEDs) with an ITO/PEDOT:PSS/PVK/PFO-poss/LiF/Al structure were prepared on plasma-treated ITO/glass substrates using spin-coating and thermal evaporation methods. The annealing effects of the PFO-poss film when it acts as the emission layer were investigated by using electrical and optical property measurements. The annealing conditions of the PFO-poss emission film were 100 and $200^{\circ}C$ for 1, 2 and 3 hours, respectively. The luminance increased and the turn-on voltage decreased when the annealing temperature and treatment time increased. After examining the Luminance-Voltage (L-V) properties of the PLED, the maximum luminance was found to be 1497 cd/$m^2$ at 11 V for the device when it was annealed at $200^{\circ}C$ for 3 hours. The peak intensity of the PLED emission spectra at approximately 525 nm in wavelength increased when the annealing temperature and time of the PFO-poss film increased. These results suggest that the light emission color shifted from blue to green.

• Journal of the Korean institute of surface engineering
• /
• v.39 no.3
• /
• pp.93-97
• /
• 2006

Polymer light emitting diodes (PLEDs) are expected to be commercialized as next generation displays by advantages of the fast response time, low driving voltage and easy manufacturing process for large sized flexible display. Generally, the electrical and optical properties of PLEDs are affected by the surface conditions of transparent electrode. The PLED devices with ITO/PEDOT:PSS/PVK/PFO-poss/LiF/Al structures were prepared by using the spin coating method. For this, PEDOT:PSS(poly(3,4-ethylenedioxythiophene):poly(styrene sulfolnate)) Al 4083 and PVK(N-vinylcabozole) were used as hole injection and transport layers. The PFO-poss(poly(9,9-dioctylfluorene)) was used as the emitting layer. The dependence of $O_2$ plasma treatment of ITO electrode on the electrical and optical properties of PLEDs were investigated. The sheet resistances increased slightly with an improved surface roughness of ITO electrode as the RF power increased during $O_2$ plasma treatment. The PLED devices prepared on the ITO/Glass substrates, which were plasma-treated at 40 watt in RF power for 30 seconds under 40 mtorr $O_2$ pressure, showed the maximum external emission efficiency of 0.86 lm/W and the maximum luminance of $250\;cd/m^2$, respectively. The CIE color coordinates are ranged $X\;=\;0.13{\sim}0.18$ and $Y\;=\;0.10{\sim}0.16$, showing blue color. emission.

• Proceedings of the KAIS Fall Conference
• /
• 2006.11a
• /
• pp.133-134
• /
• 2006

본 논문에서는 ITO/Glass 기판에 스핀 코팅법(Spin Coating)과 열 증착법(Thermal Evaporation)을 이용하여 ITO/PEDOT:PSS/PVK/PFO-poss/Li/Al 구조를 갖는 청색 고분자 유기전계발광소자를 제작하였다. 청색 고분자 유기발광다이오드 제작시 ITO 전극을 $O_2$ gas를 이용한 Plasma Treatment와 Heat Treatment를 실시하여 기판처리가 제작된 소자의 전기, 광학적 특성에 미치는 영향에 대하여 조사하였다. Plasma와 Heat Treatment를 동시에 처리한 소자에서 가장 우수한 전기, 광학적 특성을 나타냈으며, 기판처리를 하지 않은 경우는 전기, 광학적 특성은 크게 감소하였다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2007.11a
• /
• pp.89-90
• /
• 2007

본 연구에서는 ITO/PEDOT:PSS/PFO-poss/LiF/Al 구조를 갖는 고분자 유기발광다이오드(PLED)를 제작하여 ITO 투명 전도막의 전처리 효과가 유기발광 다이오드의 특성에 미치는 영향에 대하여 조사하였다. 최적의 전처리 조건을 찾기 위하여 다양한 플라즈마 처리 조건에 다른 ITO 투명전도막의 표면형상의 변화와 전기적 특성을 관찰하였다. 또한 ITO 투명전도막에 플라즈마 처리와 열처리를 실시하여 PLED 소자를 제작하고 전기 광학적 특성을 조사하여 ITO 투명 전도막의 전처리가 소자의 특성에 미치는 영향을 조사하였다.