This study investigates the micro-cutting of cemented carbides using PCD(polycrystalline diamond) and PCBN(polycrystalline cubic boron nitride) cutting tools are performed with SEM direct observation method. The purpose of this study is to make clear the cutting mechanism of cemented carbides and the fracture of WC particles at the plastic deformation zone in orthogonal micro-cutting. And also to achieve systematic understanding, the effect of machining parameter on chip formation and machined surface was investigated, including cutting speed. depth of cut and various tool rake angle.

• Journal of Welding and Joining
• /
• v.32 no.2
• /
• pp.9-13
• /
• 2014

Friction stir welding (FSW) was successfully performed about 900MPa grade Twinning Induced Plastisity (TWIP) steel. A PCBN tool with convex-type shoulder was applied. Optimal process conditions were deduced. Microstructure and mechanical properties such as hardness, tensile strength and impact absorbed energy were observed and evaluated, respectively. An optical microscope (OM) and a field emission scanning electron microscope (FE-SEM) was selected for observing the grain structure.

• Journal of Advanced Marine Engineering and Technology
• /
• v.33 no.2
• /
• pp.322-329
• /
• 2009

Machinability of LAM(Laser Assisted Machining) has been studied for ceramics such as $Al_2O_3$, $Si_3_N4$ and $ZrO_2$ by $CO_2$ laser. It was possible to remove ceramics by PCBN tool because material became softening and deterioration by local laser beam irradiation. The advantage of LAM is the ability to produce larger material removal rates and tool life. But, for cutting of $Al_2O_3$ and $ZrO_2$, stage of laser power control was needed owing to thermal shock with high temperature of workpiece by laser power. And when $Si_3N_4$ was machined by LAM, $N_2$ gas spouted from surface of one cause of high temperature. Characteristics of LAM were analyzed using pyrometer, dynamometer, SEM and EDS to measure temperature of workpiece surface, cutting force, variation of machining surface and structure of lattice respectively. As the result of this study, it was found that machinability of LAM for ceramics in $CO_2$ laser and mechanism of LAM was different according to the kind of ceramics because of properties of materials.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2012.05a
• /
• pp.103.1-103.1
• /
• 2012

본 연구는 차량경량화를 위하여 높은 인장강도와 우수한 인성을 가지는 590MPa급 이상조직강(Dual phase steel)을 이용하여 1991년 TWI(The Welding Institute)에서 개발된 마찰교반접합을 적용하여 접합을 실시하였다. 접합의 공정조건으로 툴의 회전속도는 250~350 RPM, 접합속도로는 50~350 mm/min로 겹치기접합을 실시하였다. 접합에서 사용된 툴은 Megastir에서 제작한 고융점마찰교반접합용 툴인 PCBN(Q-60)을 이용하였고 연구에 사용된 DP590은 포스코(POSCO)에서 제작된 1.4t(mm) 두께인 AHSS(advanced high strength steels)을 사용하였다. 모재인 DP590과 접합체의 미세조직은 광학현미경과 주사전자현미경을 이용하여 관찰하였으며 기계적 특성은 경도시험과 인장시험을 실시하여 조사하였다. 경도의 분포는 모재에서 약 220~230Hv이며 TMAZ부분에서 상승하기 시작하여 접합부에서 약 320Hv까지 상승하는 경향을 보였으며 인장시험 결과 접합속도 100~200 mm/min에서는 모든 시편이 모재에서 파단되어지는 것을 확인할 수 있었다. 위와 같은 결과 300~350 RPM, 100~200 mm/min의 공정조건에서는 접합이 성공적으로 이루어졌으며 차량경량화에 적용이 가능하다고 판단되어진다.

• Korean Journal of Materials Research
• /
• v.30 no.12
• /
• pp.672-677
• /
• 2020

Expensive PCBN or ceramic cutting tools are used for the processing of difficult-to-cut materials such as Ti and Ni alloy materials. These tools have a problem of breaking easily due to their high hardness but low fracture toughness. To solve this problem, cutting tools that form various coating layers are used in low-cost WC-Co hard material tools, and researches on various tool materials are being conducted. In this study, WC-5, 10, and 15 wt%Ni hard materials for difficult-to-cut cutting materials are densified using horizontal ball milled WC-Ni powders and pulsed current activated sintering method (PCAS method). Each PCASed WC-Ni hard materials are almost completely dense, with a relative density of up to 99.7 ~ 99.9 %, after the simultaneous application of pressure of 60 MPa and electric current for 2 min; process involves almost no change in the grain size. The average grain sizes of WC and Ni for WC-5, 10, and 15 wt%Ni hard materials are about 1.09 ~ 1.29 and 0.31 ~ 0.51 µm, respectively. Vickers hardness and fracture toughness of WC-5, 10, and 15 wt%Ni hard materials are about 1,923 ~ 1,788 kg/mm2 and 13.2 ~ 14.3 MPa.m1/2, respectively. Microstructure and phase analyses of PCASed WC-Ni hard materials are performed.

• Korean Journal of Materials Research
• /
• v.31 no.7
• /
• pp.392-396
• /
• 2021

Expensive PCBN or ceramic cutting tools are used for processing of difficult-to-cut materials such as Ti and Ni alloy materials. These tools have the problem of breaking easily due to their high hardness but low fracture toughness. To solve these problems, cutting tools that form various coating layers are used in low-cost WC-Co hard material tools, and research on various tool materials is being conducted. In this study, binderless-WC, WC-6 wt%Co, WC-6 wt%Co-1 wt% Mo₂C, and WC-6 wt%Co-2.5 wt% Mo₂C hard materials are densified using horizontal ball milled WC-Co, WC-Co-Mo₂C powders, and spark plasma sintering process (SPS process). Each SPSed Binderless-WC, WC-6 wt%Co-1 wt% Mo₂C, and WC-6 wt%Co-2.5 wt% Mo₂C hard materials are almost completely dense, with relative density of up to 99.5 % after the simultaneous application of pressure of 60 MPa and almost no significant change in grain size. The average grain sizes of WC for Binderless-WC, WC-6 wt%Co-1 wt% Mo₂C, and WC-6 wt%Co-2.5 wt% Mo₂C hard materials are about 0.37, 0.6, 0.54, and 0.43 ㎛, respectively. Mechanical properties, microstructure, and phase analysis of SPSed Binderless-WC, WC-6 wt%Co-1 wt% Mo₂C, and WC-6 wt%Co-2.5 wt% Mo₂C hard materials are investigated.