• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.349-350
• /
• 2012

Porous silicon (PS) was prepared by electrochemical anodization. Ultra-thin zinc oxide (ZnO) capping layers were deposited on the PS by plasma-assisted molecular beam epitaxy (PA-MBE). The effects of the ZnO capping layers on the properties of the as-prepared PS were investigated using scanning electron microscopy (SEM) and photoluminescence (PL). The as-prepared PS has circular pores over the entire surface. Its structure is similar to a sponge where the quantum confinement effect (QCE) plays a fundamental role. It was found that the dominant red emission of the porous silicon was tuned to white light emission by simple deposition of the ultra-thin ZnO capping layers. Specifically, the intensity of white light emission was observed to be enhanced by increasing the growth time from 1 to 3 min.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.78-78
• /
• 2011

수열합성법을 이용하여 Si(111) 기판에 ZnO 박막을 성장하였다. ZnO 박막의 성장을 위한 씨앗층은 plasma-assisted molecular beam epitaxy (PA-MBE)를 이용하였다. 씨앗층의 표면 거칠기(root-mean-square roughness)는 2.5 nm이고, 씨앗층 위에 성장된 ZnO 박막은 다양한 크기의 입자들로 이루어져 있었으며 두께는 약 $1.8{\mu}m$로 매우 일정하였다. 배향성을 알아보기 위하여 texture coefficient (TC)를 계산해 보았다. TC(100)과 TC(200)은 a-축 배향성을, TC(002)는 c-축 배향성을 나타내는데, c-축으로 더 우세한 배향성(99.5%)을 보였다. TC 비율(TCa-axis/TCc-axis)은 열처리 온도를 $700^{\circ}C$까지 올렸을 때, 점차적으로 증가하였고, 그 이상의 열처리 온도(< $900^{\circ}C$)에서는 급격히 감소하였다. 잔류응력과 Zn와 O의 bond length도 유사한 경향을 보였다. $700^{\circ}C$까지 열처리 온도가 증가함에 따라, 잔류응력은 증가하였고 bond length는 감소하였다. Near-band-edge emission (NBE)의 피크 강도는 열처리 온도가 $700^{\circ}C$까지 증가함에 따라 점차적으로 증가하였다. 열처리 온도가 $800^{\circ}C$ 이상 증가함에 따라 deep-level emission (DLE)가 적색편이(red-shift)하였다. $700^{\circ}C$로 열처리를 한 ZnO 박막이 가장 우세한 (002)방향의 배향성을 보였을 뿐만 아니라 가장 큰 발광효율 증가를 보였다.