• 한국자동차공학회논문집
• /
• 제7권9호
• /
• pp.112-118
• /
• 1999

Shrinkage behavior was investigated to obtain more accurate dimensions of injected molding parts for free and restricted shrinkage conditions. various parameters for metal inserted injection process, such as thickness of resin, holding pressure and time, mo이 temperature and restriction condition of mold, were considered for the analysis of shrinkage phenomena. For numerical analysis, MOLDFLOW software was used to find the deterministic parameters of filling time, temperature, pressure and holding time. Also , experimental shrinkage effects were measured through actual injection molding process and the resin thickness was under controlled as 3 mm , 5 mm, and 7mm for the shapes of plastic gear made of Polymide(PA) and Polyxymethlene(POM). The main parameters of these injection processes were found to be holding pressure, holding time and mold temperature in the case of metal inserted molding.

• 공업화학
• /
• 제10권8호
• /
• pp.1136-1140
• /
• 1999

폴리아마이드6(PA6)와 무수말레산이 그라프트된 폴리프로필렌(PP-g-MA)의 용융혼합된 블렌드계를 제조하고, 이 블렌드계의 인장, 굴곡, 충격, 동적기계적열 특성 및 상구조의 변화를 조사하였다. 인장강도와 인장탄성율은 두 조성물의 혼합에 따른 상승효과가 나타났고, 굴곡특성의 경우는 두 조성물의 산술평균값을 유지함을 알 수 있었다. 그리고 충격강도의 경우는 PA6/PP-g-MA 50/50 wt % 조성에서 최대값을 보였다. Tan ${\delta}$결과로부터, 두 조성물간의 반응에 의해 혼화성이 증가되었음을 확인하였다. 또한 상구조와 충격강도의 결과로부터, 본 블렌드계는 PA6 매트릭스에 PP-g-MA가 $2{\mu}m$정도 크기로 고르게 분산되어진 경우에 우수한 내충격성을 갖음을 알 수 있었다.

• 폴리머
• /
• 제32권2호
• /
• pp.125-130
• /
• 2008

A commercial cyclic diphosphonate ester (TPMP) and melamine (MA) was combined and added to polyamide 6 (PA6) to prepare the fire retardant PA6. An increase of the oxygen index to 28.6 as well as an improvement of the UL-94 classification to V-0 rating was observed. Cone measurements explained the rate of heat release (RHR) decreased and TGA showed the early decomposition and high solid residue due to co-addition of TPMP and MA, suggesting the occurrence of synergistic effect of TPMP and MA on fire resistance of PA6. The morphology of the char developed during combust ion showed the appearance of thick, intumescent cells on the surface of retardant PA6, which protects the underlying material from the action of the heat flux or flame and limits the diffusion of combustible volatile products towards the flame and oxygen.

• 폴리머
• /
• 제36권6호
• /
• pp.712-720
• /
• 2012

광학현미경분석, 주사전자현미경분석 및 적외선분광분석을 이용하여, 열화시간 경과에 따른 유리섬유가 보강된 폴리아미드 66 복합소재의 열 열화 특성을 조사하였다. 열화시간이 증가함에 따라, 인장강도는 열화 초기 약간의 증가 후 점진적으로 감소하는 경향을 보였다. 이러한 결과는 열 열화가 진행됨에 따라 결정화도의 증가, 가교밀도의 증가, 사슬 전단 및 사슬 운동성의 감소 등에 기인한 것으로 판단된다. 적외선분광분석을 통하여, 폴리아미드 66 복합소재 표면상에 열화에 기인한 케톤 피크와 규소 피크의 증가를 관찰하엿다. 또한 세 가지 승온속에서 측정된 열중량분석 결과를 이용하여 폴리아미드 66 복합소재으 열 분해 반응동역학을 분석하였다. 통계학적 기법, UL 746B, Ozawa 및 Kissinger 등 여러 방법을 통해 계산된, 폴리아미드 66 복합소재의 활성화 에너지와 수명 예측간의 상관관계를 조사하였다. 열중량분석으로부터 계산된 활성화 에너지는 가속시험으로 구한 값보다 상대적으로 큰 값을 나타내며, 이는 폴리아미드 66 소재으 수명을 과대 평가하는 결과를 초래하였다. 본 연구에서는 다양한 사용 온도에서의 활성화 에너지를 외삽하여 계산 가능한 지수 패턴의 표준곡선을 개발하였다.