• Journal of Powder Materials
• /
• v.1 no.2
• /
• pp.198-207
• /
• 1994

In order to find an optimal friction-welding condition for Ni-base ODS alloy (MA 754) produced by mechanical alloying, joint experiments were performed with various conditions of friction pressures (50~500 MPa), friction times (1~5 sec) and upset pressures (50~600 MPa). The optimal friction pressure and upset pressure must be above 400 MPa and 500 MPa, respectively, which are determined by tensile strengths and fracture features of as-welded joints. A maximum stress설h of 975 MPa could be obtained under these pressure conditions at friction time of 2 sec. Microstructural features of bonded interface by optical microscope and SEM revealed that the interface regions of all specimens are consisted with three distinct regions and defects such as voids, cracks and wavy interfaces exist in the joints produced under not-optimized conditions. EDS results showed that these defects include oxides composed with elements of Al, Y and Ti. The hardness on the bonded interface was higher than in the base metal region. Specimens fractured in bonded interface region had lower strength values compared to those fractured in base metal region. Surfaces of the former showed a typical intergranular fracture.

• Journal of Welding and Joining
• /
• v.23 no.6
• /
• pp.77-86
• /
• 2005

Low temperature bonding of the silicon and glass using the Spin-on Glass (SOG) has been conducted experimentally to figure out the effects of the SOG solution composition and process variables on bond strength using the Design of Experiment method. In order to achieve the high quality bond interface without rack, sufficient reaction time of the optimal SOG solution composition is needed along with proper pressure and annealing temperature. The shear strength under the optimal SOG solution composition and process condition was higher than that of conventional anodic bonding and similar to that of wafer direct bonding.

• Journal of Welding and Joining
• /
• v.15 no.4
• /
• pp.109-115
• /
• 1997

Laser cladding is a technique for modification of metal surface. In this laser cladding experiment a metal powder feeding system was developed for more efficient laser cladding. This system can reduce processing time and be used simpler than the conventional method. The feeding of metal powder has given a rise to the process for sequential buildup of bulk rapidly solidified materials in the form of fine powder stream to the laser cladding process. The parameters of laser cladding have been investigated using this experimental equipment. Bronze on aluminum alloy and copper on aluminum alloy were experimented by using defocused beam, powder feeding system, and gas shielding. Good cladding was achieved in the range of beam travel speed of 2.25m/min. In the case of copper/aluminum and bronze/aluminum substrate, the absorption of laser beam was too high to produce low diluted clad. In the case of copper/1050 aluminum, the optimal laser cladding condition was of laser power of 2.8kW, powder feed rate of 0.31g/s and beam travel speed of 2.25m/min. In the case of bronze/aluminum the optimal condition is of laser power of 2.5kW, powder feed rate of 0.31g/s, and beam travel speed of 2.36m/min.

• Proceedings of the KSME Conference
• /
• 2004.04a
• /
• pp.400-405
• /
• 2004

In this study, the optimal welding condition of the input power was selected experimentally through the ERW simulator, which is equal to welding status of ERW part in pipe. This condition is the input power 250kW in the heat treatment of the $900^{\circ}C$ normalizing derived from the nondestructive technique and impact energy. In order to evaluate the variation of the fatigue life in the pipe, fatigue surface crack growth test of base and optimal welded metal were performed statistically. As stress intensity factor range (${\Delta}K_s$) increases, the fatigue crack propagation rate (da/aN) of the base metal is faster than that of the welded joint. The variation of the fatigue life in the ERW pipe was estimated statistically using Monte-Carlo simulation with the standard deviation of material constants (C and m) of the paris law in the specimen.

• Journal of Ocean Engineering and Technology
• /
• v.13 no.3 s.33
• /
• pp.77-82
• /
• 1999

The compleete joining method for dissimilar hot die punch materials and its real-time evaluation method are not available at present. Brazing method has been used for joining them, but it is known that the welded joint by the brazing has the lower bonding efficiency and reliability than the diffusion welding. The friction wleding with a diffusion mechanism in bonding was applied in this study. So, this work was carried out to determine the optimal friction welding conditions and to analyze mechanical properties of friction welded joints of hot die punch materials (STD61 for the blade part of hot die punch) to alloy steel (SCM440 for the shank park of hot die punch) such as plunger. In addition, acoustic emission test was carried out during friction welding to evaluate the weld quality.

• Journal of Welding and Joining
• /
• v.30 no.6
• /
• pp.68-73
• /
• 2012

Nowadays, car manufacturers tried to improve automotive fuel efficiency, and applied many high strength steels such as AHSS or UHSS to car bodies. Therefore, the number of steel combinations for the resistance spot welding are dramatically increased and the need for weldability evaluation of these combinations are also required. In this study, we suggest the lobe curve using FEM simulations for DP780 steel with 1.0t, 1.4t. The lobe curves which could expressed weldablity and optimal welding condition were obtained according to 6 steel combinations. There were two combinations for same steel sheet which were DP780 1.0t, DP780 1.4t. Dissimilar steel sheet combination with different thickness was 1.0t and 1.4t of DP780. Different steel combinations were DP780 1.0t and SPRC440 1.0t, and DP780 1.0t and DP590 1.0t. Finally dissimilar combinations was and DP780 1.0t and DP590 1.4t. The trend of low boundary and high boundary variation of lobe curve were analyzed with a viewpoint of the contact resistance and the heat input.

• Journal of Welding and Joining
• /
• v.34 no.6
• /
• pp.35-41
• /
• 2016

The experimental study has been performed through residual stress using the Ti6Al4V, investigate the effect of laser shock peening on laser welding process residual stress of Ti6Al4V welds in a reduce safety weld zone. This research evaluated the effects of shock waves from laser shock peening with a pulsed Nd:YAG laser on Ti6Al4V welding specimens, through the analysis of the residual stress of the specimens. The residual stress could be formed by the depth of 1 mm if the proposed method of reducing the residual stress is performed in the optimal condition. The welded structures and products during the production process increase the mechanical property of repeated stress, which could be expected to extend the fatigue life of the structure.

• Journal of Welding and Joining
• /
• v.27 no.3
• /
• pp.38-43
• /
• 2009

The optimization of the welding parameters was studied to maximize the weldability and minimize the amount of spatter in the MAG welding of automotive steel sheets under different shielding gas composition ratio. JS-EFSC, JS-SPHC steel plates and Ar mixture gases were used as a substrate and shielding gas for welding respectively. The five welding parameters were selected through preliminary experiments and their effects on the weldability were analyzed. Experiments were performed using the Taguchi experimental method. As results, appropriate range for welding could be achieved. Amount of spatter in 80%Ar+20%$CO_2$ shielding gas was 20% of that of $CO_2$welding. Therefore, in terms of high productivity and welding cost, Ar mixture gas(80%Ar+20%$CO_2$) was recommended as a shielding gas for application of MAG process, indicating the low spatter and good weld quality.

• Journal of the Korean Society of Safety
• /
• v.16 no.4
• /
• pp.58-64
• /
• 2001

In this study, it is developed that the system for effective prediction of residual stresses by the back-propagation algorithm using the neural network. To achieve This goal, the series experiment were carried out and measured the residual stresses using the sectional method. Using the experimental results, the optional control algorithms using a neural network should be developed in order to reduce the effect of the external disturbances during GMA welding processes. Then the results obtained from this study were compared between the measured and calculated results, weld guality might be controlled by the neural network based on backpropagation algorithm. This system can no only help to understand the interaction between the process parameters and residual stress, but also improve the quantity control for welded structures.

• Journal of Power System Engineering
• /
• v.18 no.3
• /
• pp.106-111
• /
• 2014

Welding is very popular method for joining two or more metals. However, welding causes residual stress and distortion and these give a bad influence to the structure strength. In this paper, TIG welding technique was performed to investigate the joint characteristics of AISI321 steel. For its evaluation, the orthogonal array method and variance analysis were applied with three factors of electric current, travel speed and argon gas and also three levels of each factor to tensile tests for optimum design. From the results, the increaser weld speed the narrower bead width and the lower weld penetration. The increaser electric current the brighter argon gas and the wider bead width. Also weld speed influenced most on the tensile strength and presumption range of tensile strength at optimal condition from reliability 95% was estimated to $635.02{\pm}14.64$. In addition the increaser weld speed and electric current the fracture occurred around bead vicinity.