• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.46 no.3
• /
• pp.73-80
• /
• 2014

In this study, in order to investigate the influence of insolubilizer on the double coating structure, we carried out basic research related to the double coating formulation with four insolubilizers having various chemical types such as amino aldehyde, glyoxal and two metallic salts. It was found that although the four insolubilizers showed similar results on optical and surface properties of the coated papers, they gave different results in the printabilities of the coated papers since coating structure was significantly influenced by different reacting mechanism of the insolubilizers. Three of the insolubilizers (glyoxal, two metallic salts) showed better results than amino aldehyde type one when they were applied to top coating formulation. Metallic salts type insolubilizers showed good results in the print gloss when it was applied to top coating formulation. It was believed that amino aldehyde type insolubilizer applied top coating formulation showed good both of dry-pick and wet-pick strength.

• Journal of the Korean Society for Heat Treatment
• /
• v.13 no.2
• /
• pp.71-84
• /
• 2000

A study on adhesion and wear resistance of VC(vanadium carbide) coating on die steels, STD11 and STD61, has been carried out. The VC coating on the die steels was made by immersing them in molten borax bath, a kind of TRD(thermo-reactive deposition and diffusion). Adhesion strength and wear resistance were investigated using scratch test, indentation test and plate-disc test(Ogoshi type) respectively. The influence of sliding distance on the amount of wear has been determined and dominant wear mechanisms has been characterized using optical microscopy, scanning electron microscopy and EDS spectroscopy. The critical adhesion strength($L_c$) between VC coating layer and substrate(STD11) was increased to 60N($L_c$) in the scratch test. In the case of STD61, the strength increased to 24N. The wear resistance of VC coated die steels was excellent because the diffusion layer formed just below the coating layer. The dominant wear mechanism was identified as adhesive wear for VC coating die steels which were worn by combination of cracking and plucking of VC fragments and disc.

• Corrosion Science and Technology
• /
• v.17 no.1
• /
• pp.1-5
• /
• 2018

As structural materials, magnesium (Mg) alloys have been widely used in the fields of aviation, automobiles, optical instruments, and electronic products. There are few studies on the effect of coating conditions on the compositional variation during the formation process of the conversion coatings. Rare-earth based conversion coating on AZ91 magnesium alloy was prepared in ceric sulfate and hydrogen peroxide contained solution. The element composition and valence as well as their distribution in the coating were analyzed with energy dispersive X-ray spectroscopy (EDS), Electron probe micro-analyzer (EPMA), X-ray photoelectron spectroscopy (XPS). The effect of treating process on the element composition were also studied. It was found that the conversion coating surface consists of Mg, Al, O, Ce, and the weight content of Ce in the coating was affected by the treating solution concentration and immersion time; the Ce element was distributed in the coating non-uniformly and existed in the form of $Ce^{+3}$ and $Ce^{+4}$, while the O element existed in the form of $OH^-$, $O^{2-}$, $H_2O$. Based on microscopic analysis results, the electrochemical deposition mechanism on the micro-anode and micro-cathode in the process of the coating growth was suggested.

• Proceedings of the Optical Society of Korea Conference
• /
• 2004.07a
• /
• pp.132-133
• /
• 2004

• Proceedings of the Optical Society of Korea Conference
• /
• 2007.02a
• /
• pp.313-314
• /
• 2007

• Proceedings of the Optical Society of Korea Conference
• /
• 2002.11a
• /
• pp.212-213
• /
• 2002

• Journal of Korean Ophthalmic Optics Society
• /
• v.4 no.1
• /
• pp.51-56
• /
• 1999

$TiO_2$ thin films were spin coated on commercial Nickel-Silver with 2%Ti-naphthanate toluene solution by sol-gel process. The thin films were heat-treated at $500^{\circ}C$ for 2min and then decorative-protective coating was obtained. The conditions for gold colored coating, and the morphology, microstructure and color of the coating surface were have been characterized by Optical microscope, Photospectrometer and XRD. The heating temperature of colored-$TiO_2$ coating was $500^{\circ}C$ and was preferable. The average thickness of 1 time coating was $0.24{\mu}m$ and the total thickness increased linearly as a function of the coating time. The color of amorphous colored-$TiO_2$ coating was changed from gold to dark redish gold with coating time. 'L' as lightness and 'b' were decreased to red, but 'a' was decreased to blue after increase with coating time.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.336-336
• /
• 2013

Zinc oxide (ZnO) based transparent oxide semiconductors have been studied due to their high transmittance and electrical conductivity. Pure ZnO have unstable optical and electrical properties at high temperatures but doped ZnO thin films can have stable optical and electrical properties. In this paper, transparent oxide semiconductors of Y-doped ZnO thin films prepared by sol-gel method. The ionic radius of $Y^{3+}$ (0.90 A) is close to that of $Zn^{2+}$ (0.74 A), which makes Y suitable dopant for ZnO thin films. The Sn-doped ZnO thin films were deposited onto quartz substrates with different atomic percentages of dopant which were Y/Zn = 0, 1, 2, 3, 4, and 5 at.%. These thin films were pre-heated at $150^{\circ}C$ for 10 min and then annealed at $500^{\circ}C$ or 1 h. The structural and optical properties of the Y-doped ZnO thin films were investigated using field-emission scanning electronmicroscopy (FE-SEM), X-ray diffraction (XRD), UV-visible spectroscopy, and photoluminescence (PL).

• 한국전산유체공학회:학술대회논문집
• /
• 2011.05a
• /
• pp.92-95
• /
• 2011

In manufacturing optical fibers, the process starts with the glass fiber drawing from the heated and softened silica preform in the furnace, and the freshly drawn glass fiber is still at high temperature when it leaves the glass fiber drawing furnace. It is necessary to cool down the glass fiber to the ambient temperature before it then enters the fiber coating applicator, since the hot glass fiber is known to cause several technical difficulties in achieving high quality fiber coating. As the fiber drawing speed keeps increasing, a current manufacturing of optical fibers requires a dedicated cooling unit with helium gas injection. A series of three-dimensional flow and heat transfer computations are carried out to investigate the effectiveness of fiber cooling in the fiber cooling unit. The glass fiber cooling unit is simplified into the long cylindrical enclosure at which the hot glass fiber passes through at high speed, and the helium is being supplied through several injection slots of rectangular shape along the cooling unit. This study presents and discusses the effects of helium injection rates on the glass fiber cooling rates.

• Journal of the Optical Society of Korea
• /
• v.13 no.3
• /
• pp.310-315
• /
• 2009

We report the fabrication of double clad fiber (DCF) and DCF coupler, suitable for fiber based imaging systems requiring the dual-channel transmission. Unlike the conventional DCF which uses silica for both cladding layers, the proposed DCF uses a low-index polymer for its outer-cladding layer coated over the conventional silica inner-cladding layer. The DCF is drawn with a conventional SMF preform but a low-index polymer coating is used for both jacket and outercladding of the fiber. To achieve the cladding mode coupling, a DCF coupler is fabricated by simply twisting two pieces of the proposed DCF after removing the polymer-coating at contacting regions. A cladding mode coupling ratio of 30% was achieved with a contact length of 16 cm. The proposed DCF and DCF coupler were employed in a composite optical coherence tomography (OCT) and fluorescence spectroscopy (FS) system, and both OCT images and FS signal from a plant tissue are measured simultaneously.