This paper studies the experimental method that uses the homogeneous precipitation method to prepare mica flakes coated with anatase-type titania pearlescent pigment with urea as precipitant. The optimum technology parameters, the chemical composition, the microstructure, and the color property of resulting pigments are discussed. The coating principle of mica coated titania with various coating thickness is analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy(TEM) and tested by spectrophotometer analysis. The colored nanocrystalline pigments with different morphology and coating thickness 45-170 nm were prepared by homogeneous precipitation treatment of $TiOSO_4$(titanum oxysulfate) aqueous solutions. Characterizations on the pigments show that the pearlescent effects of the pigments depend mainly on mica size, thickness of the metal oxide deposit, its chemical composition, and crystal structure.

• Advances in nano research
• /
• v.12 no.4
• /
• pp.415-426
• /
• 2022

Nickel substituted cobalt-zinc ferrite nanoparticles with composition Co_0.5Zn_0.5Ni_xFe_2-xO₄ (x = 0.25, 0.5, 0.75, 1.0) were synthesized using a wet chemical method named citrate precursor method. Various characterizations of the prepared nanoferrites were done using X-ray powder diffractometry (XRD), Scanning electron microscopy (SEM), UV visible spectroscopy and Fourier transform spectroscopy technique (FT-IR). XRD confirmed the formation of cubic spinel structure of the samples with single phase having one characteristic peak at (311). The value of optical band gap (E_g) was found to decrease with Ni substitution and have values in the range 2.30eV to 1.69eV. A Fenton-type system was created by photocatalytic activity using source of visible light for removal of methylene blue dye. Observations revealed increase in the degradation of methylene blue dye with increasing nickel content in the samples. The degradation percentage was increased from 77.32% for x = 0.25 to 90.16% for x = 1.0 in one hour under the irradiation of visible light. Also, the degradation process was found to have pseudo first order kinetics model. Hence, it can be observed that synthesized nickel doped cobalt-zinc ferrites have good capability for water purification and its degradation efficiency enhanced with increase in nickel concentration.

• Applied Microscopy
• /
• v.50
• /
• pp.17.1-17.9
• /
• 2020

Recent advances in fabrication have enabled radial-junction architectures for cost-effective and high-performance optoelectronic devices. Unlike a planar PN junction, a radial-junction geometry maximizes the optical interaction in the three-dimensional (3D) structures, while effectively extracting the generated carriers via the conformal PN junction. In this paper, we report characterizations of radial PN junctions that consist of p-type Si micropillars created by deep reactive-ion etching (DRIE) and an n-type layer formed by phosphorus gas diffusion. We use electron-beam induced current (EBIC) microscopy to access the 3D junction profile from the sidewall of the pillars. Our EBIC images reveal uniform PN junctions conformally constructed on the 3D pillar array. Based on Monte-Carlo simulations and EBIC modeling, we estimate local carrier separation/collection efficiency that reflects the quality of the PN junction. We find the EBIC efficiency of the pillar array increases with the incident electron beam energy, consistent with the EBIC behaviors observed in a high-quality planar PN junction. The magnitude of the EBIC efficiency of our pillar array is about 70% at 10 kV, slightly lower than that of the planar device (≈ 81%). We suggest that this reduction could be attributed to the unpassivated pillar surface and the unintended recombination centers in the pillar cores introduced during the DRIE processes. Our results support that the depth-dependent EBIC approach is ideally suitable for evaluating PN junctions formed on micro/nanostructured semiconductors with various geometry.

• Applied Chemistry for Engineering
• /
• v.21 no.3
• /
• pp.317-322
• /
• 2010

In this study, poly(methyl methacrylate) (PMMA) was treated with changing mixing ratios of $F_2$ and $O_2$ using oxyfluorination method for hydrophilic modification of PMMA film. For the characterizations of oxyfluorinated PMMA surface, contact angle, surface free energy, X-ray photoelectron spectroscopy (XPS) and optical transmittance (UV-vis) were carried out. After the oxyfluorination, PMMA surface became more hydrophilic showing the decrease of water contact angle from $69^{\circ}$ to $44^{\circ}$. So, surface free energy of oxyfluorinated PMMA film was increased from 46 to $58\;mN\;m^{-1}$. These results are attributed to hydrophilic functional groups such as hydroxyl group formed oxyfluorination method on the PMMA surface. From XPS results, it was confirmed that O/C concentration ratio on the surface of PMMA was increased, the amount of C-OH bonding which shows hydrophilicity was also largely increased from 6.7 to 24.8% with increasing fluorine partial-pressure via the oxyfluorination, The oxyfluorination conditions, room temperature, 1 bar with one mixture ratio of $F_2$ to $O_2$ had little influence on optical transmittance properties of PMMA film but enhanced its surface hydrophilicity. This result suggests that oxyfluorination method could be useful to change hydrophobic PMMA surface to hydrophilic.

• Transactions on Electrical and Electronic Materials
• /
• v.16 no.2
• /
• pp.90-94
• /
• 2015

In this study, the characterizations of oxide contact hole etching are investigated with C₄F₈/O₂/Ar and CH₂F₂/C₄F₈/O₂/ Ar plasma. As the percent composition of C₄F₈ in a C₄F₈/O₂/Ar mixture increases, the amount of polymer deposited on the etched surface also increases because the C_xF_y polymer layer retards the reaction of oxygen atoms with PR. Adding CH₂F₂ into the C₄F₈/O₂/Ar plasma increases the etch rate of the oxide and the selectivity of oxide to PR. The profile of contact holes was close to 90°, and no visible residue was seen in the SEM image at a C₄F₈/(C₄F₈+O₂) ratio of 58%. The changes of chemical composition in the chamber were analyzed using optical emission spectroscopy, and the chemical reaction on the etched surface was investigated using X-ray photoelectron spectroscopy.

• Bulletin of the Korean Chemical Society
• /
• v.33 no.5
• /
• pp.1741-1747
• /
• 2012

Water-dispersible ZnS:Mn nanocrystals were synthesized by capping the surface of the nanocrystals with conventional aminoacids ligands: serine and threonine. The aminoacids capped ZnS:Mn nanocrystal powders were characterized by XRD, HR-TEM, EDXS, ICP-AES and FT-IR spectroscopy. The optical properties were also measured by UV/Vis and solution photoluminescence (PL) spectroscopies in aqueous solvents. The solution PL spectra showed broad emission peaks around 600 nm with PL efficiencies of 9.7% (ZnS:Mn-Ser) and 15.4% (ZnS:Mn-Thr) respectively. The measured particle sizes for the aminoacid capped ZnS:Mn nanocrystals by HR-TEM images were about 3.0-4.0 nm, which were also supported by Debye-Scherrer calculations. In addition, cytotoxic effects of four aminoacids capped ZnS:Mn nanocrsystals over the growth of wild type E. coli were investigated. Although toxicity in the form of growth inhibition was observed with all the aminoacids capped ZnS:Mn nanocrystals at higher dose (1 mg/mL), ZnS:Mn-Met and ZnS:Mn-Thr appeared non-toxic at doses less than 100 ${\mu}g$/mL. Low biological toxicities were seen at doses less than 10 ${\mu}g$/ mL for all nanocrystals.

• Journal of Sensor Science and Technology
• /
• v.15 no.3
• /
• pp.186-191
• /
• 2006

In general, Cerenkov light is produced by a charged particle that passes through a medium with a velocity greater than that of visible light. Although the wavelength of Cerenkov light is very broad, the peak is in the almost visible range from 400 to 480 nm. Therefore, it always causes a problem to detect a real light signal that is generated in the scintillator on the fiber-optic sensor tip for dose measurements of high-energy electron beam. The objectives of this study are to measure, characterize and remove Cerenkov light generated in a fiber-optic radiation sensor tip to detect a real light signal from the scintillator. In this study, the intensity of Cerenkov light is measured and characterized as a function of incident angle of electron beam from a LINAC, and as a function of the energy of electron beam. As a measuring device, a photodiode-amplifier system is used, and a subtraction method using a background optical fiber is investigated to remove Cerenkov light.

• Korean Journal of Materials Research
• /
• v.23 no.9
• /
• pp.477-482
• /
• 2013

We investigated the detection properties of nitrogen monoxide (NO) gas using transparent p-type $CuAlO_2$ thin film gas sensors. The $CuAlO_2$ film was fabricated on an indium tin oxide (ITO)/glass substrate by pulsed laser deposition (PLD), and then the transparent p-type $CuAlO_2$ active layer was formed by annealing. Structural and optical characterizations revealed that the transparent p-type $CuAlO_2$ layer with a thickness of around 200 nm had a non-crystalline structure, showing a quite flat surface and a high transparency above 65 % in the range of visible light. From the NO gas sensing measurements, it was found that the transparent p-type $CuAlO_2$ thin film gas sensors exhibited the maximum sensitivity to NO gas in dry air at an operating temperature of $180^{\circ}C$. We also found that these $CuAlO_2$ thin film gas sensors showed reversible and reliable electrical resistance-response to NO gas in the operating temperature range. These results indicate that the transparent p-type semiconductor $CuAlO_2$ thin films are very promising for application as sensing materials for gas sensors, in particular, various types of transparent p-n junction gas sensors. Also, these transparent p-type semiconductor $CuAlO_2$ thin films could be combined with an n-type oxide semiconductor to fabricate p-n heterojunction oxide semiconductor gas sensors.

• Journal of Conservation Science
• /
• v.22
• /
• pp.61-76
• /
• 2008

We examined characterizations of Paraloid B72 films when it dissolved in four different solvents-acetone, MEK, toluene and xylene. The surface before and after coating were observed by optical microscope and AFM. Thickness and contact angle of films was measured and surface energy was calculated for grasping properties of films. We also tested adhesive strength of films by scratch tester and durability of films by performing yellowing test. The result was that xylene has better coating property than other solvents. Because 10% Paraloid B72 in xylene film is even, non-mottled, thin, stabilized in yellowish and has proper hydrophobic, we confirmed xylene is good solvent for bronze artifact conservation. However, other tests will need for finding appropriate concentration of Paraloid B72.

• Journal of the Institute of Electronics Engineers of Korea SP
• /
• v.41 no.6
• /
• pp.33-41
• /
• 2004

This paper proposes a color matching 3D look-up table simplifying the complex color matching procedure between a monitor and a mobile display device. In other to perform color matching, it is necessary to process color of image in the device independent color space like CIEXYZ or CIELAB. To obtain the data of the device independent color space from that of the device dependent RGB color space, we must perform display characterizations. LCD characterization error using S-curve model is larger than tolerance error since LCD is more nonlinear than CRT. This paper improves the S-curve model to have smaller characterization error than tolerance error using the electro-optical transfer functions of X, Y, and Z value. We obtained images having higher color fidelity on mobile display devices through color matching experiments between monitor and mobile display devices. As a result of this experiments, we concluded that the color matching look-up table with 64(4${\times}$4${\times}$4) is the smallest size allowing characterization error to be acceptable.