• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2003년도 춘계학술발표강연 및 논문개요집
• /
• pp.99-99
• /
• 2003

The growth of GaN on Si is of great interest due to the several advantages : low cost, large size and high-quality wafer availability as well as its matured technology. The crystal quality of GaN is known to be much influenced by the surface pretreatment of Si substrate[1]. In this work, the properties of GaN overlayer grown on ion beam modified Si(111) have been investigated. Si(111) surface was treated RIB with 1KeV-N$_2$$\^$+/(at 1.9 ${\times}$ 10$\^$-5/) to dose ranging from 5${\times}$10$\^$15/ to 1${\times}$10$\^$17/ prior to film growth. GaN epilayers were grown at 1100$^{\circ}C$ for 1 hour after growing AlN buffer layers for 5∼30 minutes at 1100$^{\circ}C$ in Metal Organic Chemical Vapor Deposition (MOCVD). The properties of GaN epilayers were evaluated by X-Ray Diffraction(XRD), Raman spectroscopy, Photoluminescence(PL) and Hall measurement. The results showed that the ion modified treatment markedly affected to the structural, optical and electrical characteristic of GaN layers.

• 한국정보통신학회논문지
• /
• 제14권3호
• /
• pp.691-698
• /
• 2010

본 연구에서는 RF magnetron sputtering 법으로 AZO 세라믹 타켓 ($Al_2O_3$ : 3 wt%)을 이용하여 Eagle 2000 유리 기판위에 기판온도 ($100{\sim}500^{\circ}C$)와 공정압력 (10 ~ 40 mTorr)에 따른 AZO 박막을 제작하여, 결정화 특성과 전기적 및 광학적 특성을 조사하였다. 모든 AZO 박막은 육방정계구조를 가지는 다결정 이었고, (002)우선 배향성이 관찰되었다. 기판온도 $300^{\circ}C$, 10 mTorr에서 제작한 AZO 막에서 가장 우수한 (002) 배향성을 나타냈으며, 이때의 반가폭 값은 $0.42^{\circ}$였다. 전기적 특성은 기판온도 $300^{\circ}C$, 10 mTorr에서 가장 낮은 비저항 $2.64{\times}10^{-3}\;{\Omega}cm$과 우수한 캐리어 농도 및 이동도를 $5.29{\times}10^{20}\;cm^{-3}$, $6.23\;cm^2/Vs$를 나타내었다. 모든 AZO 박막은 가시광 영역에서 80%의 투과율을 나타내었으며, 기판온도 증가와 공정압력 감소에 따른 Al 도핑효과의 증가로 밴드 갭이 넓어지는 Burstein-Moss 효과가 관찰 되었다.

• 한국진공학회지
• /
• 제16권2호
• /
• pp.134-140
• /
• 2007

[ $V_{2}O_{5}$ ] 박막의 성장특성을 분석하기 위해 RF 스퍼터링 시스템으로 C-Si 기판에 10 %와 0 %의 산소 분압비로 시료를 제작하였다. 구조적 특성의 분석을 위해 SBM과 XRD 측정을 실시하였고, 위상변조방식의 분광타원계를 이용하여 $0.75{\sim}4.0\;eV$ 범위에 걸쳐 타원상수를 측정하였다. 측정된 타원상수 분석을 위해 상용화된 분석용 프로그램인 DeltaPsi2를 이용하여, Double Amorphous 분산관계식으로 최적 맞춤 하였다. SEM과 XRD 측정결과 시료의 표면 및 결정 상태는 비정질임을 확인하였고, 타원상수의 분석에 의해 $V_{2}O_{5}$층의 두께, void비율, 표면 거칠기를 알 수 있었다. 또한 SEM 측정치와 비교한 결과 두 시료의 두께와 표면 거칠기의 결과가 잘 일치함을 확인 하였다.

• 한국세라믹학회지
• /
• 제34권2호
• /
• pp.209-215
• /
• 1997

Reactive Single Ion Beam Sputtering 방법을 이용하여 AIN박막을 증착하고 물성을 분석하였다. 반응성 가스로 질소 가스 또는 암모니아 가스를 이용하였다. 증착된 AIN박막의 구조적, 화학적, 광학적 물성을 분석하기 위해 XRD, GAXRD, TEM, SEM, XPS, UV/VIS spectrophotometer, FT-IR등을 이용하였다. XRD, GAXRD분석결과에 의하면 증착된 모든 AIN박막은 비정질이었으나 TEM분석결과에서는 비정질 속에 육방정의 AIN미세결정들이 분포해 있었다. 그리고 FT-IR과 XPS분석을 통하여 Al-N결합을 확인하였으며, 화학양론적인 조성이 됨에 따라 UV-VIS spectrophotometery 분석에서 투광성이 증가하며 광학적 밴드갭은 6.2eV까지 증가함을 확인하였다. 또한 단면과 표면 형상관찰에서는, 반응성 가스로 질소 가스나 암모니아 가스에 관계없이, 결정입계가 전혀 관찰되지 않는 아주 평활한 현상이었으며 굴절율은 1.6~1.7의 값을 갖는다.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2010년도 추계학술대회 초록집
• /
• pp.42.2-42.2
• /
• 2010

Transparent conducting oxides (TCOs) are of significant importance for their applications in various devices, such as light-emitting diodes, thin-film solar cells, organic light-emitting diodes, liquid crystal displays, and so on. In order for TCOs to contribute to the performance improvement of these devices, TCOs should have high transmittance and good electrical properties simultaneously. Sn-doped $In_2O_3$ (ITO) is the most commonly used TCO. However, indium is toxic and scarce in nature. Thus, ZnO has attracted a lot of attention because of the possibility for replacing ITO. In particular, group III impurity-doped ZnO showed the optoelectronic properties comparable to those of ITO electrodes. Al-doped ZnO exhibited the best performance among various doped ZnO films because of the high substitutional doping efficiency. However, in order for the Al-doped ZnO to replace ITO in electronic devices, their electrical and optical properties should further significantly be improved. In this connection, different ways such as a variation of deposition conditions, different deposition techniques, and post-deposition annealing processes have been investigated so far. Among the deposition methods, RF magnetron sputtering has been extensively used because of the easiness in controlling deposition parameters and its fast deposition rate. In addition, when combined with post-deposition annealing in a reducing ambient, the optoelectronic properties of Al-doped ZnO films were found to be further improved. In this presentation, we deposited Al-doped ZnO (ZnO:$Al_2O_3$ = 98:2 wt%) thin films on the glass and sapphire substrates using RF magnetron sputtering as a function of substrate temperature. In addition, the ZnO samples were annealed in different conditions, e.g., rapid thermal annealing (RTA) at $900^{\circ}C$ in $N_2$ ambient for 1 min, tube-furnace annealing at $500^{\circ}C$ in $N_2:H_2$=9:1 gas flow for 1 hour, or RTA combined with tube-furnace annealing. It is found that the mobilities and carrier concentrations of the samples are dependent on growth temperature followed by one of three subsequent post-deposition annealing conditions.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2009년도 제37회 하계학술대회 초록집
• /
• pp.185-185
• /
• 2009

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2009년도 제37회 하계학술대회 초록집
• /
• pp.190-190
• /
• 2009

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2007년도 제38회 하계학술대회
• /
• pp.1349-1350
• /
• 2007

Epitaxial thin films of aluminum-doped zinc oxide (AZO) have been deposited on commercial corning glass using an Nd:YAG pulsed laser deposition technology. The structural, electrical and optical properties of these films were investigated as a function of oxygen pressure. The experimental results show that the electrical resistivity of films deposited at 5 mTorr with substrate temperature of $300^{\circ}C$ were $4.633{\times}10^{-4}$. The average transmission of AZO thin films in the visible range were over 90%.

• 한국결정성장학회지
• /
• 제22권2호
• /
• pp.73-77
• /
• 2012

스컬용융법으로 큐빅지르코니아(YSZ) 단결정들($ZrO_2$: $Y_2O_3$= 80 : 20, 70 : 30, 60 : 40, 50 : 50 wt%, $Co_3O_4$: 0.8wt%, $CeO_2$: 0.4wt%)을 성장시켜 $N_2$ 분위기 $1000^{\circ}C$에서 5시간 동안 열처리 하였다. 오랜지색, 황갈색 또는 갈색의 단결정들은 각각 갈적색, 황색 또는 녹색으로 변화되었다. 열처리 전 후의 YSZ 단결정들은 직경 6.5, 두께 2 mm의 웨이퍼로 연마 하였다. 각 시편의 광학적 또는 구조적 특성은 UV-VIS 분광광도계와 XRD(X-ray diffraction)로 분석하였으며, $Ce^{3+}(^2F_{5/2,7/2}(4f){\rightarrow}^2T_g(5d^1))$, $Co^{2+}(^4A_2(^4F){\rightarrow}^4T_1(^4F)$ 또는 $^4T_1(^4P))$ 및 $Co^{3+}$에 의한 흡수, 이온화에너지 및 격자상수 변화를 확인하였다.

• 한국진공학회지
• /
• 제15권2호
• /
• pp.194-200
• /
• 2006

분자선증착기 (Molecular beam epitaxy. MBE)를 이용하여 InP (001) 기판에 자발형성 (Self-assembled) InAs/InAlAs, InAs/InAlGaAs 양자점 (quantum dots, QDs)을 형성하고 구조 및 광학적 특성을 원자력간현미경(Atomic force microscopy, AFM), 투과전자현미경 (Transmission electron microscopy, TEM), 상온 포토루미네슨스 (Photoluminescence, PL) 실험을 통하여 분석하였다. AFM 측정을 통해 표면 형태를 분석한 결과 InAs 양자구조는 기저물질의 표면상태에 따라 양자대쉬, 비대칭적인 형태를 갖는 양자점, 대칭적인 형태를 갖는 양자점과 같이 다양하게 성장되었다. InAlGaAs 물질을 장벽층으로 하는 InAs 양자점의 평균크기는 폭이 대략 23 nm, 높이가 약 2 nm 이었다. 성장조건을 다양하게 변화시켜 광통신시스템에 중요한 파장중의 하나인 $1.55{\mu}m$ 발광파장을 갖는 InAs 양자점을 형성하였다.