• Journal of the Korean institute of surface engineering
• /
• v.41 no.4
• /
• pp.156-162
• /
• 2008

Small FRP(fiber-reinforced polymer) fishing ships have numerous problems with the point of the environmental and recycling perspectives. In light of these aspects, aluminum can be used as a material for ship building. It is environmental friendly, easy to recycle, and provides a high added value to fishing boats. In this paper, we report on mechanical and electrochemical characteristics of welding parts for friction stir welded 5456-H116 Al alloy. In friction stir welded at various traveling speeds under the rotation speed of 500 RPM, the best characteristics presented in traveling speed of 15mm/min. The anodic polarizations of base metal and welding metal were observed tendency which current density from the open circuit potential suddenly increase. The cathodic polarization presented concentrated polarization caused by the dissolved oxygen reduction reaction and activation polarization caused by hydrogen generation. From result of Tafel analysis, the corrosion potential of 5456 alloy(Base metal) was lower than that of friction stir welded part, as were its corrosion current densities.

• Restorative Dentistry and Endodontics
• /
• v.14 no.1
• /
• pp.199-204
• /
• 1989

The purpose of this study was to observe the anodic polarization curve from 4 kinds of low copper amalgam (Fine cut alloy, Spheralloy, Aristalloy and Amalcap) and 4 kinds of high copper amalgam (Dispersalloy, Sybraloy Orosphere and Tytin) obtained by using the potentiostat. The specimen made as the direction of manufacturer was stored at room temperature for about 7 days. The standard surface preparation was routinely carried out. The 0.9% saline solution was used as electrolyte in pH 6.8-7.0 at $37^{\circ}C$. The open circuit potential was determined after 30 minutes' immersion of specimen. The scan rate was 1mV/sec and the surface area of amalgam exposed to the solution was 0.785$cm^2$ for each specimen. All potentials reported are with respect to Ag/AgCl eelctrode. The following results were obtained. 1. The corrosion potential of high copper amalgams was higher than one of low copper amalgams, and the current density of high copper amalgam was lower than one of low copper amalgams. 2. The low copper amalgams had the similar pattern of polarization curve, but the high copper amalgams had the different pattern one another. 3. The polarization curve of Orosphere amalgam which is the admixed type was similar to one of low copper amalgam.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.39 no.4
• /
• pp.291-297
• /
• 2003

Al-brass is usually used as the tube material of vessel's heat exchanger for seawater cooling system because it has high thermal conductivity and good mechanical properties and high corrosion resistance due to cuprous oxide (Cu20) layer against seawater. However, Al-brass tubes of heat exchanger for vessel at the actual environment is reported that local corrosion such as stress corrosion cracking occurred by synergism effect between mechanical factor and corrosion environment In this paper, the effect of corrosion environment on the stress corrosion cracking of Al-brass in various NH4OH of 3.5% NaCl solution, under flow by constant displacement tester. Based on the test results, the behavior of polarization, stress corrosion crack propagation and dezincification phenomenon of Al-brass are investigated. The main results are as follows：(1) Increasing range of potential from open circuit potential to repassivation gets lower, as the contain rate of NH4OH gets higher. (2) As contain rate of NH4OH gets higher, SCC of Al-brass is become activation but the protection film(Cu20) of Al-brass is created in 3.5% NaCl solution. (3) According as content of NH4OH increases in 3.5% NaCl solution, the dezincifiction area is spread. It is concluded that dezincification occurred by localized preferential anodic dissolution at stress focusing region.

• Corrosion Science and Technology
• /
• v.16 no.4
• /
• pp.183-186
• /
• 2017

Galvanic corrosion tests of Zn/steel couples were conducted in 1 M NaCl and $1M\;MgCl_2$ solutions to investigate the impact of magnesium ion on corrosion behavior of the couples. Two types of Zn/steel couples were used for measurements of open circuit potential (OCP) and galvanic current. From the results of OCP transient of Zn/steel couples, the corrosion potential in $1M\;MgCl_2$ was a more positive value than that in 1 M NaCl during the sacrificial dissolution of Zn. However, earlier increase of OCP of the couples in $1M\;MgCl_2$ solution indicates that the sacrificial dissolution rate of Zn in $1M\;MgCl_2$ was enhanced more than that in 1 M NaCl, agreeing with the results on transients of galvanic current. This result is due to that cathodic reaction on the steel surface of the Zn/steel couple was enhanced in $1M\;MgCl_2$ by the occurrence of hydrogen evolution reaction.

• Corrosion Science and Technology
• /
• v.20 no.2
• /
• pp.45-51
• /
• 2021

In this work, we describe the effect of pulse anodizing duty ratio on the corrosion resistance of anodic films in magnesium AZ31B. The process involves the application of square pulse potential for a constant period with a duty ratio varying from 40, 60 and 80%. In several samples, a sealing treatment for 30 minutes was conducted after anodization in order to seal the pores available in the anodic layer. After anodizing, the surface morphology of the anodic layer was examined using a scanning electron microscope (SEM Hitachi SU3500). The corrosion characteristics of the sample were evaluated through an open circuit potential (OCP) and potentiodynamic polarization test using potentiogalvanostat. SEM observation shows that the increase of anodization duty ratio (α) results in a more uniform anodic layer, with fewer pores and cracks. The increase of duty ratio (α) decreases the OCP value from approximately -1.475 to about -1.6 Volt, and significantly improves the corrosion resistance of the anodic coating by 68%. The combination of anodization and sealing treatment produces an anodic coating with a very low corrosion rate of 4.4 mpy.

• Metals and materials international
• /
• v.24 no.6
• /
• pp.1232-1240
• /
• 2018

Corrosion properties of dissimilar friction stir welded 6061 aluminum and HT590 steel were investigated to understand effects of galvanic corrosion. As cathode when coupled, HT590 was cathodically protected. However, the passivation of AA6061 made the aluminum alloy cathode temporarily, which leaded to corrosion of HT590. From the EIS analysis showing Warburg diffusion plot in Nyquist plots, it can be inferred that the stable passivation layer was formed on AA6061. However, the weld as well as HT590 did not show Warburg diffusion plot in Nyquist plots, suggesting that there was no barrier for corrosion or even if it exists, the barrier had no function for preventing and/or retarding charge transport through the passivation layer. The open circuit potential measurements showed that the potential of the weld was similar to that of HT590, which lied in the pitting region for AA6061, making the aluminum alloy part of the weld keep corrosion state. That resulted in the cracked oxide film on AA6061 of the weld, which could not play a role of corrosion barrier.

• Bulletin of the Korean Chemical Society
• /
• v.28 no.10
• /
• pp.1729-1734
• /
• 2007

The electrochemical behaviors of estrone in the presence of various surfactants were examined with great details. It is found that a cationic surfactant, cetyltrimethylammonium bromide (CTAB), obviously facilitates the electro-oxidation of estrone at carbon paste electrode (CPE) from the significant peak current enhancement and the negative shift of peak potential. Additionally, chronocoulometry and electrochemical impedance spectroscopy (EIS) were also used for further investigation of the electrode process of estrone, indicating that low concentration of CTAB exhibits excellent enhancement effects on the electrochemical oxidation of estrone, greatly enhances the diffusion coefficient and the electron transfer rate. Based on this, an electrochemical method was proposed for the determination of estrone. The oxidation peak current is proportional to the concentration of estrone in the ranges over 9.0 × 10?8 - 8.0 × 10?6 mol/L, and a low detection limit of 4.0 × 10?8 mol/L was obtained for 180s accumulation at open circuit (S/N = 3). Finally, this proposed method was demonstrated using estrone tablets with good satisfaction.

• Proceedings of the KIEE Conference
• /
• 2003.10b
• /
• pp.101-103
• /
• 2003

This paper deals with field distributions in high speed motor with two different types of diametrically magnetized PM rotor, one is that rotor is consisted of PM and shaft, the other is that rotor has only PM. In case of high speed motor with rotor consisted of PM and shaft, this paper predicts field distributions in high speed motor according to the quality of shaft. The magnetic field solutions are derived analytically in terms of vector potential and 2-D polar coordinate system. The results are shown in good conformity with those obtained from the commonly used finite element method.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2013.05a
• /
• pp.137-137
• /
• 2013

본 연구에서는 반도체 검사 장비인 프로브 카드의 핵심 부품인 프로브 니들의 팁 부분의 내마모성을 향상시키기 위하여 무전해 Ni-B-W 합금 도금 실험을 실시하였다. 무전해 Ni-B-W 합금 도금 실험에서 여러 가지 제어인자 중 도금욕의 pH와 온도 그리고 환원제의 농도 등을 변수로 하였다. 도금욕 pH와 온도에 따른 전착속도 및 물성 변화를 관찰하였으며, 환원제 농도 변화에 의한 open circuit potential의 변화를 측정하였다.

• Bulletin of the Korean Chemical Society
• /
• v.35 no.11
• /
• pp.3227-3231
• /
• 2014

Bamboo-like Te nanotubes were synthesized via the galvanic displacement reaction of NiFe nanowires with Ni-rich and Fe-rich segments. The thick and thin components of the synthesized Te nanotubes were converted from the Ni-rich and Fe-rich segments in the NiFe nanowires respectively. The dimensions of the Te nanotubes were controlled by employing sacrificial NiFe nanowires with tailored dimensions as the template for the galvanic displacement reaction. The segment lengths of the Te nanotubes were found to be dependent on those of the sacrificial NiFe nanowires. The galvanic displacement reaction was characterized by analyzing the open circuit potential and the corrosion resistance.