• Polymer(Korea)
• /
• v.37 no.6
• /
• pp.770-776
• /
• 2013

The ENR 50 having the lowest gas permeability was blended with Nylon 6 which exhibits superior gas permeability, excellent wear resistance by using a twin-screw extruder. The blended materials showed the increased gas barrier property and physical properties, but did not yield a great synergistic effect due to low dispersion of Nylon 6 to ENR 50. To improve dispersion of Nylon 6 in the rubber matrix, maleic anhydride (MAH) was grafted to ENR 50. The grafting reaction between MAH and ENR 50 was evidenced using IR spectroscopy. The grafted and blended materials, ENR 50- g-MAH/Nylon 6 compounds, resulted in an enhanced gas barrier property and physical properties compared with compounds without MAH. The compound at 5 phr of MAH showed the highest crosslinking density and the best performances.

• Nuclear Engineering and Technology
• /
• v.8 no.3
• /
• pp.159-168
• /
• 1976

Acrylic acid has been grafted onto nylon fabric with ceric salts and ${\gamma}$-rays from Co-60 as initiators. The distribution of molecular weight of the grafted polyacrylic acid has been determined and it was found that the ratio of weight-average and number-average molecular weight was higher in room temp. than in low temp. (-184$^{\circ}C$). The weight-average molecular weight of the polyacrylic acid was calculated from viscosity measurements in sodium hydroxide solution. The factors affecting graft polymerization of acrylic acid onto nylon were examined. A possible mechanism that the oxidation of nylon probably takes place at the methylene group attached to nitrogen to give a free-radical was discussed.

• International Journal of Industrial Entomology and Biomaterials
• /
• v.16 no.2
• /
• pp.61-66
• /
• 2008

In this paper, the regenerated silk fibroin (SF)/nylon 6 blend filaments were fabricated using wet spinning technique and the effect of coagulant on the post drawing and morphology of blend filaments was investigated. In the result of wet spinnability, methanol, acetone, DMF, and THF showed relatively good coagulation strength and fiber formation for the regenerated SF. On the contrary, they did not exhibit strong enough to produce a uniform nylon 6 filament due to the lack of coagulation strength. In the examination of post drawing performance, methanol showed the highest maximum draw ratio of the blend filament over all blend ratios. The maximum draw ratio of SF/nylon 6 blend filaments decreased with the reduction of SF content regardless of type of coagulant. SEM observation showed the consistent result with that of post-drawing performance. As SF content decreased, the uniform and regular structure was changed to irregular one. In particular, the severe macro-phase separation between SF and nylon 6 could be detected in the 50/50 SF/nylon 6 blend filaments coagulated in methanol and THF.

• Journal of the Korean Society for Precision Engineering
• /
• v.22 no.2
• /
• pp.139-147
• /
• 2005

The lubricant impregnated MC nylon has good frictional properties, but its mechanical strength is inferior to steel for the mechanical elements. For the tribological application Nylon as gears, sliding bearings, cam and etc, the steel shafts are fitted in pre-heated nylon cylinder by a process of interference expansion fit and bonded by induction heating method. The joint shear strength of the two materials was measured by a universal test machine. From the study, the adhesive shear strength between these two materials was affected by the factors of the interference between nylon and steel, the size of nylon cylinder, knurl of steel shaft and inducting heating conditions. The most effective jointing conditions were analyzed and decided for the practical application in the industry.

• Textile Coloration and Finishing
• /
• v.6 no.3
• /
• pp.67-73
• /
• 1994

The adsorption behaviors of acid dye and disperse dye on silk and nylon fabrics were examined, in one bath dyeing system on silk/nylon blend fabric with disperse dyes and acid dyes. In the dyeing of nylon fabric with C. I. Disperse Red 19 (Red 19) and C. I. Disperse Red 60 (Red 60), dye uptake of Red 19 was higher than that of Red 60. When silk/nylon blend fabric was dyed with Red 19 and Red 0, the dye uptake on nylon was influenced by the ffinity of the dye to the silk fabric. In the dyeing of silk/nylon with C. I. Acid Blue 80 and C. I. Acid Yellow 121, solid shade could not be obtained with the conventional method but could be obtained with the dyeing resist agent for nylon. There was not any relationship between K/S value and Munsell value, but Munsell value tended to change with the K/S value.

• Journal of the Korean Society of Industry Convergence
• /
• v.12 no.1
• /
• pp.5-10
• /
• 2009

The Nylon/clay nanocomposite were prepared with Cloisite25A and Cloisite30B. And mechanical properties and thermal properties of Nylon/clay nanocomposites on the amount of MMT have been investigated. From the results of XRD and TEM, we found that mono layered silicates were dispersed in polymer matrix and those resultants were exfoliated nanocomposites. When Cloisite30B was used as an intercalant in the Nylon/Clay nanocomposites, the mechanical and thermal properties of Nylon were higher than those with Cloisite25A.

• Proceedings of the Korean Fiber Society Conference
• /
• 2001.10a
• /
• pp.265-269
• /
• 2001

nylon 6의 단점인 저온에서의 연성 및 내충격성 저하를 개선하는 동시에 nylon 6의 내후성도 개선시키는 방법의 하나로 유리전이온도가 매우 낮고, 내가수분해성, 내후성 및 연성(ductile property)이 뛰어난 불소함유 고분자계의 한 종류인 PVDF(polyvinylidene fluoride)를 nylon 6에 용융블렌드 하는 방법이 제안되었다. [1-5] (중략)

• Journal of the Korean Chemical Society
• /
• v.23 no.5
• /
• pp.329-337
• /
• 1979

The water-vapour transmission ratios (WVTR) of the various commercial polymer films have been investigated at the constant pressure and relative humidity (RH). Water proofnesses, the reciprocals of WVTR for the various samples, were determined using a cup device and maintaining the sample films at a constant temperature ($40{\pm}1^{\circ}C$) and a constant R. H ($90{\pm}2%$) for 24 hours. The following order of the relative proofness was observed; oriented polypropyrene (O.PP) > high density polyethylene (HDPE, Inflation) > high density polyethylene (HDPE. T-die) > casted polypropylene (C. PP) > nonoriented polyester (N. PET) > low density polyethylene (LDPE) > oriented polyester (O. PET) > rigid polyvinyl chloride (Rigid PVC) > semirigid polyvinyl chloride (Semirigid PVC) > nonrigid polyvinyl chloride (Nonrigid PVC) > oriented nylon (O. Nylon) > nonoriented nylon (N. Nylon). And water proofness order was also observed to decrease with the temperature rising; HDPE (T-die) > C. PP > O. PET > LDPE > O. Nylon. The activation energies of LDPE, HDPE (T-die), C. PP, O. PET and O.Nylon films were 12.0, 11.1, 11.4, 11.7, 14.1 kcal/mole, respectively. The WVTR's of the films were increased with the polarity of polymer and the addition of plasticizer in PVC, decreased with the increase of the film thickness and mechanical orientation. The WVTR's of the laminated films O. PP/LDPE, N.Nylon/LDPE, C.PP/LDPE were also more dependent on the film thickness than the WVTR's of the single films.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.29 no.2
• /
• pp.117-123
• /
• 1993

In order to analysis the tensile properties of the high-tech fibers for fishing gear materials. tensile strength was tested on raw materials, single yarns and netting twines(plied yarns)made of nylon, kevlar 29 and techmilon respectively. The results obtained are as follows: 1. The tensile stress and tenacity of unknotted single yarns in dry and wet conditions were 3 to 3.5 times greater in the high-tech fibers than in nylon. But the elongation of the high-tech fibers was about 15% of that in nylon. 2. The tensile strength of knotted single yarns in dry and wet conditions was arranged in order of as follows : techmilon. kelver 29, and nylon. The ratio of knot strength to tensile strength, knot efficiency, was the highest in nylon. 3. The tensile strength of unknotted netting twines in dry and wet conditions was 2.3 to 2.5 times greater in the high-tech fibers than in nylon. 4. The tensile strength of knotted netting twines in dry and wet conditions was arranged in order of as follows : techmilon, kevlar 29, nylon. The knot efficiency was the highest in nylon.

• Journal of the Korean Association of Oral and Maxillofacial Surgeons
• /
• v.26 no.2
• /
• pp.146-153
• /
• 2000

The purpose of present study is comparing the effect of Teflon Membrane and Nylon Membrane on bone regeneration in rabbit tibia. The 6 defects of $8{\times}8{\times}5mm$ size were drilled with dental handpiece in rabbit tibia, which on left side as an order of Control group(no coverage), Group 1(Nylon $5{\mu}m$ size), Group 3(Nylon $10{\mu}m$ size), and on right side Control group, Group 2($5{\mu}m$ Teflon), Group 4($10{\mu}m$ Teflon). Animals were killed at 7, 10, 14, 42 days to make specimens and observed the difference of healing potentials with light microscopy. The results were as follows ; 1. New bone formation has taken place at 14 days in Guided Bone Regeneration (GBR) group comparing to the Control group of massive inflammatory status. 2. Larger pore membrane allows more favorable healing potentials. Bone formation started earlier in larger membrane pore groups than smaller groups, until 14 days. 3. Bone forming potentials of Teflon membrane group was higher than Nylon membrane groups, Control group has the lowest bone forming potentials. 4. New bone formation was almost ended in 42 days, and there was no difference of bone formation between Nylon and Teflon membrane group of different size. There was no difference of bone formation at final stage(42 days) between Nylon membrane and Teflon membrane of same pore size. So nylon membrane may be clinically usable in guided bone regeneration case with further studies.