• Proceedings of the KACD Conference
• /
• 2001.11a
• /
• pp.588.1-588
• /
• 2001

The purpose of this study was to compare the root canal shaping ability of four nickel-titanium rotary instruments. Forty eight simulated curved root canals were instrumented in plastic with the Crown-down technique using the $ProTaper^{TM}$ , the ProFile, the $GT^{TM}$, and the Quantec. Canals were instrumented until apical canal were up to size 30 by one operator. Each instrument was used only once and instrumentation time was measured.(omitted)

• Proceedings of the KACD Conference
• /
• 2003.11a
• /
• pp.552-552
• /
• 2003

The purpose of this study was to quantify the amount of remaining gutta-percha/sealer on the walls of root canals when three types of nickel-titanium rotary instruments and a hand instrument were used to remove these materials. Forty extracted mandibular premolars were prepared by step-back method and obturated with gutta-percha and sealer. Gutta-percha removal for group 1 was done using hand file with chloroform, group 2 using Profile and group 4 using K3. The following factors were evaluated : Time taken to reach working length, total time for gutta-percha removal and number of fractured instruments.(중략)

• Journal of Korean Dental Science
• /
• v.15 no.2
• /
• pp.112-120
• /
• 2022

In this article, the contemporary root canal treatment procedure using nickel-titanium (NiTi) instruments was reviewed to understand the correlations between the properties of files and safety of the clinical usage. Literatures were reviewed according to the process of clinical procedure of the root canal preparation, mainly for shaping during orifice flaring, glide-path preparation, and main canal instrumentation. Considering the reasons for NiTi file fracture, clinically implacable issues and ideas were discussed to reduce the fracture risk and increase clinical efficiency of the NiTi file systems. Various kinds of NiTi file systems have their own characteristics and properties given from their geometries and heat treatments and so on. Proper selection and careful usage of the NiTi file systems may reduce the risk of file fracture and increase the efficiency of NiTi file systems. Understanding of the clinical implications from the mechanical properties and characteristics of the engine driven NiTi instruments may decrease the risk of NiTi file fractures and increase the success rate in root canal treatment.

• The Journal of the Korean dental association
• /
• v.34 no.5 s.324
• /
• pp.363-372
• /
• 1996

• The korean journal of orthodontics
• /
• v.37 no.2 s.121
• /
• pp.137-149
• /
• 2007

Objective: The purpose of this study was to compare changes in frictional resistance between the bracket and wire under dry and wet conditions according to a change in moment. Methods: A stainless steel bracket of $0.022"{\times}0.028"$ slot, and $0.019"{\times}0.025"$ stainless steel, beta-titanium, and nickel-titanium wires were used. A 10 mm length lever was attached to the test (sliding) brackets to generate a moment. The experimental model was designed to allow tipping until contacts were established between the wire and the mesiodistal edges of the bracket slot. The moment was generated by suspending a 100 g or 200 g weight on the end of the lever. The moments applied were $1000g{\cdot}mm\;(100g{\times}10mm)\;and\;2000g{\cdot}mm\;(200g{\times}10mm)$. The test brackets were ligated with elastomeric ligature for a constant ligation force and the fixed brackets were ligated with stainless steel ligature. Brackets were moved along the wire by means of an universal testing machine, and maximum frictional resistances were recorded. Results: Stainless steel wire showed least frictional resistance and there was no significant difference between beta-titanium and nickel-titanium except at $2000g{\cdot}mm$ moment in wet conditions. Frictional resistance of all wires increased as the moment increased from $1000g{\cdot}mm\;to\;2000g{\cdot}mm$. Under wet conditions, the frictional resistance of stainless steel wires increased in both $1000g{\cdot}mm\;and\;2000g{\cdot}mm$ moment conditions, but frictional resistance of nickel-titanium and beta-titanium increased only in $2000g{\cdot}mm$ conditions. Conclusion: These results indicated that various conditions influence on frictional resistance. Therefore, laboratory studies of frictional resistance should simulate clinical situation.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07b
• /
• pp.900-903
• /
• 2003

Using $DV-X{\alpha}$ method, it is calculated that nickel reduces the energy band gap of manganese oxide in 3 additives of titanium, nickel and tin. Therefore, it is estimated that the electrical conductivity of manganese-nickel oxide has the lowest value in 3 kinds of manganese oxide. The manganese oxide and manganese-nickel oxide which were produced by anodic deposition under $30mA/cm^2$ at room temperature in manganese sulfate and manganese-nickel sulfate solution were thermal-analyzed by DTA and TGA. The weight change of manganese oxide continuously decreased below $508^{\circ}C$ and kept constant at $518{\sim}600^{\circ}C$. However, the manganeses-nickel oxide transformed at the temperature range of $510{\sim}537^{\circ}C$. It is observed that the nickel addition to manganese oxide increases transformation temperature and its range.

• Restorative Dentistry and Endodontics
• /
• v.38 no.1
• /
• pp.31-35
• /
• 2013

Objectives: This study compared the cyclic fatigue resistance of nickel-titanium (NiTi) files obtained in a conventional test using a simulated canal with a newly developed method that allows the application of constant fatigue load conditions. Materials and Methods: ProFile and K3 files of #25/.06, #30/.06, and #40/.04 were selected. Two types of testing devices were built to test their fatigue performance. The first (conventional) device prescribed curvature inside a simulated canal (C-test), the second new device exerted a constant load (L-test) whilst allowing any resulting curvature. Ten new instruments of each size and brand were tested with each device. The files were rotated until fracture and the number of cycles to failure (NCF) was determined. The NCF were subjected to one-way ANOVA and Duncan's post-hoc test for each method. Spearman's rank correlation coefficient was computed to examine any association between methods. Results: Spearman's rank correlation coefficient (${\rho}$ = -0.905) showed a significant negative correlation between methods. Groups with significant difference after the L-test divided into 4 clusters, whilst the C-test gave just 2 clusters. From the L-test, considering the negative correlation of NCF, K3 gave a significantly lower fatigue resistance than ProFile as in the C-test. K3 #30/.06 showed a lower fatigue resistance than K3 #25/.06, which was not found by the C-test. Variation in fatigue test methodology resulted in different cyclic fatigue resistance rankings for various NiTi files. Conclusions: The new methodology standardized the load during fatigue testing, allowing determination fatigue behavior under constant load conditions.

• Restorative Dentistry and Endodontics
• /
• v.42 no.4
• /
• pp.332-341
• /
• 2017

Objectives: To determine the incidence of crack formation and propagation in apical root dentin after retreatment procedures performed using ProTaper Universal Retreatment (PTR), Mtwo-R, ProTaper Next (PTN), and Twisted File Adaptive (TFA) systems. Materials and Methods: The study consisted of 120 extracted mandibular premolars. One millimeter from the apex of each tooth was ground perpendicular to the long axis of the tooth, and the apical surface was polished. Twenty teeth served as the negative control group. One hundred teeth were prepared, obturated, and then divided into 5 retreatment groups. The retreatment procedures were performed using the following files: PTR, Mtwo-R, PTN, TFA, and hand files. After filling material removal, apical enlargement was done using apical size 0.50 mm ProTaper Universal (PTU), Mtwo, PTN, TFA, and hand files. Digital images of the apical root surfaces were recorded before preparation, after preparation, after obturation, after filling removal, and after apical enlargement using a stereomicroscope. The images were then inspected for the presence of new apical cracks and crack propagation. Data were analyzed with ${\chi}^2$ tests using SPSS 21.0 software. Results: New cracks and crack propagation occurred in all the experimental groups during the retreatment process. Nickel-titanium rotary file systems caused significantly more apical crack formation and propagation than the hand files. The PTU system caused significantly more apical cracks than the other groups after the apical enlargement stage. Conclusions: This study showed that retreatment procedures and apical enlargement after the use of retreatment files can cause crack formation and propagation in apical dentin.

• Restorative Dentistry and Endodontics
• /
• v.42 no.4
• /
• pp.301-308
• /
• 2017

Objectives: It was aimed to compare the cyclic fatigue resistances of ProTaper Universal (PTU), ProTaper Next (PTN), and ProTaper Gold (PTG) and the effects of sterilization by autoclave on the cyclic fatigue life of nickel-titanium (NiTi) instruments. Materials and Methods: Eighty PTU, 80 PTN, and 80 PTG were included to the present study. Files were tested in a simulated canal. Each brand of the NiTi files were divided into 4 subgroups: group 1, as received condition; group 2, pre-sterilized instruments exposed to 10 times sterilization by autoclave; group 3, instruments tested were sterilized after being exposed to 25%, 50%, and 75% of the mean cycles to failure, then cycled fatigue test was performed; group 4, instruments exposed to the same experiment with group 3 without sterilization. The number of cycles to failure (NCF) was calculated. The data was statistically analyzed by using one-way analysis of variance and post hoc Tukey tests. Results: PTG showed significantly higher NCF than PTU and PTN in group 1 (p < 0.05). Sterilization significantly increased the NCF of PTN and PTG (p < 0.05) in group 2. PTN in group 3 had significantly higher cyclic fatigue resistance than PTN group 4 (p < 0.05). Also, significantly higher NCF was observed for PTG in group 2 than in groups 3 and 4 (p < 0.05). Conclusions: PTG instrument made of new gold alloy was more resistant to fatigue failure than PTN and PTU. Autoclaving increased the cyclic fatigue resistances of PTN and PTG.

• The korean journal of orthodontics
• /
• v.50 no.6
• /
• pp.373-382
• /
• 2020

Objective: To compare computer-aided design and computer-aided manufacturing (CAD/CAM) customized nitinol retainers with standard stainless-steel fixed retainers over a 12-month study period. Methods: This randomized controlled trial (RCT) was conducted on 62 patients randomly allocated to a control group that received stainless-steel retainers or a test group that received customized CAD/CAM nickel-titanium retainers. Four time points were defined: retainer placement (T0) and 1-month (T1), 6-month (T2), and 12-month (T3) follow-up appointments. At each time point, Little's irregularity index (LII) (primary endpoint) and dental stability measurements such as intercanine width were recorded in addition to assessment of periodontal parameters. Radiological measurements such as the incisor mandibular plane angle (IMPA) were recorded at T0 and T3. Failure events (wire integrity or debonding) were assessed at each time point. Results: From T0 to T3, LII and other dental measurements showed no significant differences between the two groups. The data for periodontal parameters remained stable over the study period, except for the gingival index, which was slightly, but significantly, higher in the test group at T3 (p = 0.039). The IMPA angle showed no intergroup difference. The two groups showed no significant difference in debonding events. Conclusions: This RCT conducted over a 12-month period demonstrated no significant difference between customized CAD/CAM nickel-titanium lingual retainers and standard stainless-steel lingual retainers in terms of dental anterior stability and retainer survival. Both retainers eventually appeared to be equally effective in maintaining periodontal health.