• Korean Journal of Materials Research
• /
• v.15 no.6
• /
• pp.375-381
• /
• 2005

High temperature oxidation behavior of thermal barrier coating (TBC) system (IN738 substrate + NiCoCrAlY or NiAl bond coat with or without Pt + yttria stabilized zirconia) prepared by air plasma spray (APS) process has been studied in order to understand the effect of Pt addition to bond coat on the stability of TBC system. Specimens were oxidized in thermal cycling and isothermal oxidation test at $1100^{\circ}C$. The Pt addition in TBC system with NiCoCrAlY bond coat showed a longer life time compared to that without addition of Pt. Pt addition to TBC system is believed to help the formation of more stable thermally grown oxide, $Al_2O_3$, at the TBC/bond coat interface, leading to a longer lifetime of TBC system.

• Journal of the Korean Chemical Society
• /
• v.41 no.10
• /
• pp.561-565
• /
• 1997

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2001.11a
• /
• pp.55-55
• /
• 2001

• Journal of Korea Soil Environment Society
• /
• v.4 no.2
• /
• pp.113-125
• /
• 1999

Heavy metal elements were analysed to assess degrees of heavy metal contents for the plants, M. sinensis, A. vulgaris and G. oldhamiana, from the Baekdong serpentine area within the western part of Chungnam. The area was divided into two sites ; serpentine area (SP, consisting of serpentinite, SP) and non-serpentine area (NSP, containing amphibole schist, AS and gneiss, GN). Their host rocks(R) and top soils(S) were also collected from the each site. As the results of the study, the plants contain high concentration of Ni Cr, Co in the SP and Fe, Zn in the AS and GN. Plants from the AS of the NSP contain mainly high content in the most of elements. Averages of Ni, Co and Cr for the plants decreased in the order of SP, AS and GN. In the total element contents, M. sinensis and A. vulgaris decreased in the order of Fe > Ni or Cr > Zn > Co > As > Sc within the SP and in the order of Fe > Zn > Cr > Ni, within the GN. Comparing among the parts of plants, root parts were higher in the most of elements than the above grounds. In the relative element ratios of plants collected from the SP and GN (SP/GN) M. sinensis was lower than A. vulgaris in the most of elements, suggesting that the M. sinenis shows low absorption within the infertile serpentine soil and high absorption within the fertile gneiss soil. In the element contents of the top soils and their host rocks, the SP shows higher Ni, Co and Cr contents than the others. Their total contents decreased from SP to AS and GN, suggesting that the soils reflect the composition of their host rocks. Total element contents of the SP decreased in the order of Fe> Cr or Ni> Co> Zn> As> Sc and, for the GN, in the order of Fe> Zn> Cr> Ni> Co or Sc, respectively. In the relative element ratios, R/S of the SP decreased in the order of Cr> As> Fe> Sc> Co> Ni> Zn and for the GN, in the order of Sc> Fe> Ni> Zn> Cr> Co. Comparing with plants within the each site, their top soils were higher than the plants in the most of elements. and their increase and decrease trends for each element are similar. Differences of element contents between the top soils and plants decreased in the order of SP, AS and GN. Plants of the GN were moi-e similar to their soils than those of the others, suggesting that each plant species show different absorptions within the different soils. Comparing with the plants of GN, higher Ni, Co, Cr contents within those of the SP and their survival within the infertile serpentine soil suggest that the M. sinensis, A vulgaris and G. oldhamiana may be the tolerance species in the serpentine soil. Comparisons with the upper crust show that M. sinensis, and A. vulgaris within the SP show high Hi and Cr contents. suggestive of hyperaccumulation. Upper results with the previous studies for the contaminated soils developed as parent materials with the serpentinites suggest additional studies for ecological behaviors for the plant and degrees of accumulations for the elements need to know phytoextraction of the heavy metal elements within the soils.

• Journal of Korea Foundry Society
• /
• v.27 no.3
• /
• pp.120-125
• /
• 2007

The microstructure, mechanical properties and melting range of Ni-Cr-Mo based alloys were investigated to develop Be-free Ni-Cr-Mo base dental alloys for Porcelain-Fused-to-Metal Firing(PFM). All as-cast alloys showed dendritic structure. Rockwell hardness of 20Cr7Mo was increased with addition of Si and Ti. On the contrary, it was decreased with addition of Co. The duplex alloying elemental addition such as 3Co + xTi, 2Si + xCo and 2Si + xTi to 20Cr7Mo resulted in much increase of hardness. Rockwell hardness and compressive strength for 20Cr3CoSiTi or 17Cr6CoSiTi alloy that add Si-Ti had similar values compared to the commercial alloys. Melting range for 20Cr3CoSiTi and 17Cr6CoSiTi alloy that add Si-Ti showed similar or lower than commercial alloys. In conclusion, 20Cr3CoSiTi and 17Cr6CoSiTi alloys can be applied for commercial use.

• Korean Journal of Soil Science and Fertilizer
• /
• v.33 no.6
• /
• pp.446-452
• /
• 2000

This study was carried out to investigate the effect of mine activity on paddy fields, agricultural water, and plants in the ruined Oksung Cu-Zn mine area. Soil samples collected from paddy fields adjacent to the Cu-Zn mine sites were sequentially extracted and determined the contents of heavy metals such as Cd, Zn, Cu, Pb, Cr and Ni. Distribution of exchangeable heavy metals in soils was 30.2% of Cd, 11.3% of Zn, 2.2% of Cu, 4.6% of Cr, 0.6% of Pb and 3.9% of Ni. Water soluble heavy metals were only detected with Zn. The contents of heavy metals in water collected from the mine were 0.01 of Cd, 27.35 of Zn, 4.86 of Cu, 1.04 of Pb, 0.03 of Cr and $0.08mg\;L^{-1}$ of Ni. while the contents in waler collected out of the mine were 16.67 of Zn, 0.59 of Cu, 0.49 of Pb, 0.05 of Cr and $0.06mg\;L^{-1}$ of Ni. On the other hand, agricultural water near mine area were 1.26 of Zn, 0.05 of Cu, 0.05 of Pb and $0.02mg\;L^{-1}$ of Ni. Both Cd and Cr were not detected in the agricultural water.

• Journal of Welding and Joining
• /
• v.15 no.5
• /
• pp.46-55
• /
• 1997

This study has evaluated the liquation cracking behavior in the heat affected zone of several Ni base superalloys (Incoloy 825, Inconel 718 and Inconel 600). 304 and 310S austenitic stainless steels were also included for comparison. In addition, the mechanism of liquation cracking in the HAZ was postulated based on the extensive microstructural examinations with SEM, EDAX and TEM. The liquation cracking resistance of Ni base alloys was found to be far inferior to that of austenitic stainless steels. The liquation cracking of Incoloy 825 and Inconel 718 was believed to be closely related with the Laves-austenite(Ti rich in 825 and Nb rich in 718) and MC-austenitic eutectic phases formed along the grain boundaries by constitutional liquation and incipient melting under rapid welding thermal contraction. Further, liquation cracking resistance of the HAZ was dependent not only upon the type and amount of low melting phases but also on the grain size.

• Korean Journal of Materials Research
• /
• v.12 no.3
• /
• pp.220-224
• /
• 2002

The oxide scales formed on $Ni_3Al$-7.8%Cr-1.3%Zr-0.8%Mo-0.025%B after oxidation at 900, 1000 and 110$0^{\circ}C$ in air were studied using XRD, SEM, EPMA and TEM. The oxide scales consisted primarily of $NiO,\; NiAl_2O_4,\;{\alpha}-Al_2O_3,\; monoclinic-ZrO_2,\; and \;tetragonal-ZrO_2$. The outer layer of the oxide scale was rich in Ni-oxides, whereas the internal oxide stringers were rich in Al-oxides and $ZrO_2$. Within the above oxide scales, Cr and Mo tended to exist as dissolved ions.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.3
• /
• pp.163-175
• /
• 1996

Flame-sprayed Ni-based coatings are investigated in order to improve the thermal fatigue properties of gray cast iron in the presence of water spraying. The results of thermal cycling tests from room temperature to $1100^{\circ}C$ indicate that thermal fatigue endurance is increased in the order of Ni-20%Cr, NiCr-6%Al, and Ni-5%Al. The thermal fatigue failure is caused by the formation of iron oxides between the coating and the substrate and then the thermal fatigue cracks have propagated either along the brittle iron oxide layer resulting in the spatting of the coatings in case of Ni-5%Al and NiCr-6%Al coatings or to the substrate resulting in the whole specimen fracture in case of Ni-20%Cr coating. It seems that the most governing factor for thermal fatigue resistance is the thermal expansion coefficient difference between the coating and the substrate. Microstructural variations before and after the tests are also discussed.

• Journal of dental hygiene science
• /
• v.9 no.4
• /
• pp.405-412
• /
• 2009

The purpose of this study investigated the effect of Au coating on adhesion between porcelain matrix and metal substructure interface. Titanium, Ni-Cr alloy and Co-Cr alloy are well known as proper metal for the dental restorations. The success of a porcelain fused to metal (PFM) restoration depends upon the quality of the porcelain-metal bond. However, adhesion between dental alloys and porcelain is related to diffusion of oxygen during ceramic firing. The excessive oxidized layers make hard adhesion between dental alloy and ceramic. Ni-Cr and Co-Cr specimens were divided into test and a control group and Titanium specimens were divided into three test groups and a control group. Each group had 20 specimens. The adhesion characteristics of porcelain and metal with Au coating layer and without Au coating layer were observed with scanning electron microscopy(SEM). The adhesion was evaluated by a biaxial flexure test and volume fraction of adherent porcelain was determined by SEM/EDS analysis. Result of this study suggest that Au coating layer is effective barrier to diffuse oxide layer completely protect non-precious alloys from oxidation during the porcelain firing. The SEM photomicrographs of cross-section specimens showed a smooth interface between Au coating layer and metals and porcelain which suggested proper chemical bonding, and no gap, porosity were observed. The mode of failure was mainly adhesive for Ti tested specimens, but mixed failures with adhesive and cohesive were observed in Ni-Cr and Co-Cr specimens. The adhesion between non-precious metals and porcelain would not be improved by Au coating agent. However, It is suggested that the continuous study is required further investigation and development.