• Transactions of the Korean hydrogen and new energy society
• /
• v.21 no.5
• /
• pp.412-418
• /
• 2010

Steam reforming of n-hexadecane, a major component of diesel over Ni-based hydrotalcite-like catalyst was carried out at $900^{\circ}C$ at atmospheric pressure with space velocity of $10,000h^{-1}$ and feed molar ratio of steam/carbon=3.0. Ni-based hydrotalcite catalyst was prepared by a solid phase crystallization (spc) method and characterized by $N_2$-physisorption, CO chemisorption, TPR., XRD, and TEM techniques. It was found that spc Ni/MgAl catalyst showed higher catalytic stability and inhibition of carbon formation than Ni/$\gamma-Al_2O_3$ catalyst under the tested conditions. The results suggest that the modified spc-Ni/MgAl catalyst after optimization may be applied for the SR reaction of diesel.

• Korean Journal of Materials Research
• /
• v.9 no.6
• /
• pp.615-621
• /
• 1999

The new process in order to fabricate of Ni catalyst with high activity by the mechanochemical(MC) method which was combined the mechanical alloying(MA) and the chemical treatment process. The microstructure and characterization of mechanically alloyed Ni-5-wt% Al powder and Ni catalyst gained by alkali leaching were investigated byt he various analysis such as XRD, SEM-EDS, HRTEM and laser particle analyzer. The steady state powder with 1~2$\mu\textrm{m}$ mean particle size was obtained after 30hr milling with the PCA of 2 wt% stearic acid under the condition of grinding stainless steel ball to powder ratio of 60:1 and rotating speed fo 300rpm. According to result of HRTEM diffraction pattern, MA powder of the steady state was nanocrystalline $Al_3$$Ni_2$ intermetallic compound. Ni catalyst was obtained after KOH leaching of the steady state powder was about 20nm nanocrystalline which contained about 8 wt % Al.

• Journal of the Korean Society for Heat Treatment
• /
• v.7 no.2
• /
• pp.129-138
• /
• 1994

The purpose of this study is to clarify the influence of the reaction temperature and $AlCl_3$ content on the aluminide coating formation on Ni-based superalloy IN713C in CVD process and to compare its throwing power with that of Pack Cementation process. Aluminide coating was formed by CVD in hot-wall stainless tube reactor from an $AlCl_3-H_2$ mixture in the temperature range $850{\sim}1050^{\circ}C$. At reaction temperature $850^{\circ}C$, the coating thickness and the content of aluminium at the surface were increased as $AlCl_3$ heating temperature was raised. At reaction temperature $1050^{\circ}C$, they were not influenced by the variation of $AlCl_3$ heating temperature. When $AlCl_3$ heating temperature was fixed $125^{\circ}C$, the phases of the coatings were varied from $Ni_2Al_3$ to Al-rich NiAl and to Ni-rich NiAl with the reaction temperature. Therefore, in this study the reaction temperature has been found to be a major factor in determining the phase formed in CVD process. The throwing power of CVD was superior to that of Pack Cementation.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1997.04a
• /
• pp.465-469
• /
• 1997

In this paper, shape memory compsites are made by powder metallurgy. And then, an self-strengthening effect of the composites by shape memory effect above inverse transformation temperature A/sab f/ of TiNi alloy discussed. Moreover, TiNiCo/Al composite is made by using TiNiCo alloy as fiber. And it is discused aboutaffection of Co in the shape memory composite. The results of the intelligent properties of TiNi/Ai-radical shape memory composite, using SMA, by powder metallurgy are the tensile strength of TiNiCo wire is much higher than that of TiNi wire. and the strength of TiNiCo/Al composite is generally higher than that TiNi/Al composite.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.18 no.7
• /
• pp.1713-1721
• /
• 1994

Intermetallic-matrix composites(IMCs) have the potential of combing matrix properties of oxidation resistance and high temperature stability with reinforcement properties of high specific strength and modulus. One of the major limiting factors for successful applications of these composite at high temperatures is the formation of interfacial reactions between matrix and ceramic reinforcement during composite process and during service. The purpose of the present investigation is to develop a better understanding of the nature of creep fracture mechanisms in a $Ni_{3}Al$ composite reinforced with both $TiB_{2}$ and SiC particulates. Emphasis is placed in the roles of the products of the reactions in determining the creep lifetime of the composite. In the present study, creep rupture specimens were tested under constant ranging from 180 to 350 MPa in vacuum at $760^{\cric}C$. The experimental data reveal that the stress exponent for power law creep for the composite is 3.5, a value close to that for unreinforced $Ni_{3}Al$. The microstructural observations reveal that most of the cavities lie on the grain boundaries of the $Ni_{3}Al$ matrix as opposed to the large $TiB_{2}/Ni_{3}Al$ interfaces, suggesting that cavities nucleate at fine carbides that lie in the $Ni_{3}Al$ grain boundaries as a result of the decomposition of the $SiC_{p}$. This observation accounts for the longer rupture times for the monolicthic $Ni_{3}Al$ as compared to those for the $Ni_{3}Al/SiC_{p}/TiB_{2} IMC$. Finally, it is suggested that creep deformation in matrix appears to dominate the rupture process for monolithic $Ni_{3}Al$, whereas growth and coalescence of cavities appears to dominate the rupture process for the composite.

• Korean Journal of Materials Research
• /
• v.27 no.7
• /
• pp.392-397
• /
• 2017

Fluorine-doped tin oxide (FTO) coated NiCrAl alloy foam is fabricated using ultrasonic spray pyrolysis deposition (USPD). To confirm the influence of the FTO layer on the NiCrAl alloy foam, we investigated the structural, chemical, and morphological properties and chemical resistance by using USPD to adjust the FTO coating time (12, 18, and 24 min). As a result, when an FTO layer was coated for 24 min on NiCrAl alloy foam, it was found to have an enhanced chemical resistance compared to those of the other samples. This improvement in the chemical resistance of using USPD NiAlCr alloy foam can be the result of the existence of an FTO layer, which can act as a protection layer between the NiAlCr alloy foam and the electrolyte and also the result of the increased thickness of the FTO layer, which enhances the diffusion length of the metal ion.

• Journal of Powder Materials
• /
• v.6 no.1
• /
• pp.62-68
• /
• 1999

The effects of the carbon content ranging from 17.5 to 21.0 wt.% in TiC-30vol.% $Ni_3Al$ cenmet and the $Mo_2C$ content raging from 0 to 30 wt.% in TiC-20 vol.% $Ni_3Al$ cermet were investigated in the relation to the microstures and harbness. The speciment were sintered at 140$0^{\circ}C$, 143$0^{\circ}C$ and 145$0^{\circ}C$ for 60minutes. The results were summarized as follows; 1) The shrinkages and relative densitites of the specimens were incrased up to 20.0 wt.% C and then decreased. 2) The grains of TiC were almost the same size with the different content of carbon. Free carbons were appeared on the microstrures when carbon was added over 20.5 wt.% while TiC and $Ni_3Al$l were formed when carbon was added below 20.0 wt.%; 3) The lattice parameters of the $Ni_3Al$ and TiC phases were increased up to 20.5 wt.% C, and then saturated. 4) The hardess was increased up to 20.0 wt.% C, and then decreased. 5) The $Mo_2C$ made the TiC grains fine and the surrounding structure around TiC gains. 6) The micropores were decreased with increasing the binder and the sintering temperature. 7) The lattice parameter of the $Ni_3Al$l ana TiC were almost the samp up to 10 wt.% $Mo_2C$ and then decreased. 8) The hatdness was increased up to 5wt.% $Mo_2C$ and then decreased owing to the micrpores. 9) The more the binder phase, the higher the relative density and the proper $Mo_2C$ amount of $TiC-Ni_3Al$ cermets were obtained.

• Korean Journal of Materials Research
• /
• v.29 no.5
• /
• pp.328-335
• /
• 2019

Nb-doped $TiO_2$(NTO) coated NiCrAl alloy foam for hydrogen production is prepared using ultrasonic spray pyrolysis deposition(USPD) method. To optimize the size and distribution of NTO particles based on good physical and chemical stability, we synthesize particles by adjusting the weight ratio of the Nb precursor solution(5 wt%, 10 wt% and 15 wt%). The morphological, chemical bonding, and structural properties of the NTO coated NiCrAl alloy foam are investigated by X-ray diffraction(XRD), X-ray photo-electron spectroscopy(XPS), and Field-Emission Scanning Electron Microscopy(FESEM). As a result, the samples of controlled Nb weight ratio exhibit a common diffraction pattern at ${\sim}25.3^{\circ}$, corresponding to the(101) plane, and have chemical bonding(O-Nb=O) at 534 eV. The NTO particles with the optimum weight ratio of N (10 wt%) show a uniform distribution with a size of ~18.2-21.0 nm. In addition, they exhibit the highest corrosion resistance even in the electrochemical stability estimation. As a result, the introduction of NTO coated NiCrAl alloy foam by USPD improves the chemical stability of the NiCrAl alloy foam by protecting the direct electrochemical reaction between the foam and the electrolyte. Thus, the optimized NTO coating can be proposed for excellent protection of NiCrAl alloy foam for hydrocarbon-based steam methane reforming(SMR).

• Korean Journal of Materials Research
• /
• v.8 no.12
• /
• pp.1158-1164
• /
• 1998

Aluminium sulfate solution was prepared by sulfuric acid treatment from gibbsite. Aluminium sulfate hydrate [$Al_2(SO_4)_3$ · $nH_2O$] was precipitated from aluminium sulfate solution by adding it into ethylalcohol. From XRD analysis as-prepared $Al_2(SO_4)_3$ · $nH_2O$ was confirmed to have mixed-crystalization water(n=18, 16, 12, 6). The average water of crystalization calculated from thermogravimetry(TG) was 14.7. Aluminium sulfate hydrate [$Al_2(SO_4)_3$ · $nH_2O$] was thermally decomposed and converted to $Al_2(SO_4)_3$ at $800^{\circ}C$, $\gamma-Al_2O_3$ at $900-1000^{\circ}C$, and $\alpha-Al_2O_3$ at $1200^{\circ}C$. Ni-doped $\gamma-Al_2O_3$, was synthesized from the slurry of as-prepared $\gamma-Al_2O_3$, with the ratio of [Ni]/[Al]=0.5. The reaction conditions of synthesis were determined as initial pH 9.0 and temperature $80^{\circ}C$ The basicity(pH) of slurry was controlled by using urea and $NH_4OH$ solution. Urea was also used for deposition-precipitation. For determining termination of reaction, the data acquisition was performed by oxidation reduction potential(ORP), conductivity and pH value in the process of reaction. Termination of the reaction was decided by observing the reaction steps and rapid decrease in conductivity. On the other hand, BET(Brunauer, Emmett and Teller) and thermal diffusity of Ni- doped $\gamma-Al_2O_3$, with various content of Ni were measured and compared. Thermal stability of Ni- doped $\gamma-Al_2O_3$ at $1250^{\circ}C$ was confirmed from BET and XRD analysis. The surface state of Ni-doped $\gamma-Al_2O_3$ was investigated by X-ray photoelectron spectroscopy(XPS). The binding energy at $Ni2P_{3/2}$ increased with increasing the formation of $NiAl_2O_4$ phase.

• Applied Microscopy
• /
• v.45 no.1
• /
• pp.32-36
• /
• 2015

The microstructural features of FeCoCrNi, FeCoCrNiAl and FeCoCrNiSix (x=0, 5, 10, 15, 20) alloys have been investigated in the present study. The microstructure of FeCoCrNi alloy changes dramatically with equiatomic addition of Al. The fcc irregular shaped grain structure in the as-cast FeCoCrNi alloy changes into the bcc interconnected structure with phase separation of Al-Ni rich and Cr-Fe rich phases in the as-cast FeCoCrNiAl alloy. The microstructure of FeCoCrNi alloy changes with the addition of Si. With increasing the amount of Si, the fcc structure of the grains is maintained, but new phase containing higher amount of Si forms at the grain boundary. As the amount of Si increases, the fraction the Si-rich grain boundary phase increases.