• 연구논문집
• /
• s.28
• /
• pp.183-192
• /
• 1998

The wear and oxidation resistance of two phase nickel aluminides was investigated. Wear tests of various heat-treated specimens at room temperature and at $500^{\circ}C$ were performed under no lubricant condition in air by using a ball-on-disk type tribotester. Isothermal oxidation tests were made at $1100^{\circ}C$ in air flowing at the rate of 70cc/min and at $1000^{\circ}C$ in air by using TGA. Experimental results from wear tests showed that nickel aluminide with a higher content of Al had an improved wear resistance at both temperatures. Also the examination of the wear tracks after wear test at both room temperature and $500^{\circ}C$ indicated that regardless of the alloy compositions the wear tracks of the two phase nickel aluminides showed an abrasive type wear The improved oxidation resistance observed in the Ni-34at%Al alloy could to be attributed to the microstructural difference between the aluminides. An accelerated oxidation along the thin layer of $Ni_3AL$ along the grain boundary observed in the microstructure of the Ni-32at%Al aluminide could be attributed to the poor oxidation resistance.

• Korean Journal of Materials Research
• /
• v.12 no.3
• /
• pp.220-224
• /
• 2002

The oxide scales formed on $Ni_3Al$-7.8%Cr-1.3%Zr-0.8%Mo-0.025%B after oxidation at 900, 1000 and 110$0^{\circ}C$ in air were studied using XRD, SEM, EPMA and TEM. The oxide scales consisted primarily of $NiO,\; NiAl_2O_4,\;{\alpha}-Al_2O_3,\; monoclinic-ZrO_2,\; and \;tetragonal-ZrO_2$. The outer layer of the oxide scale was rich in Ni-oxides, whereas the internal oxide stringers were rich in Al-oxides and $ZrO_2$. Within the above oxide scales, Cr and Mo tended to exist as dissolved ions.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.11a
• /
• pp.279-282
• /
• 1997

The propose of this study is research and improvement of LiNiO$_2$as cathode material for Lithium secondary batteries. LiNiO$_2$is prepared by heating LiOH . $H_2O$ and Ni(OH)$_2$(mole ratio 1 : 1) on various heat condition. In the result of XRD mesurement, all LiNiO$_2$prepared at this study showed hexagonal structure. In Cyclic Voltammetry, LiNiO$_2$is not conspicous about oxidation peak but oxidation curve change steeply over 3.8V and reduction peak discover at 3.6V. In discharge capacities, specific capacity is higher $O_2$than air when preliminary heated and 75$0^{\circ}C$ than $700^{\circ}C$, 80$0^{\circ}C$ when heated. Therefore, when preliminary heat at $650^{\circ}C$ $O_2$and heat at 75$0^{\circ}C$ carried out, discharge property is the best.

• 한국전기화학회:학술대회논문집
• /
• 2002.10a
• /
• pp.3-4
• /
• 2002

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.2
• /
• pp.98-103
• /
• 2013

The alumina substrates that Ni electrode was printed on and the multi-layered PTCR thermistors of which composition is $(Ba_{0.998}Ce_{0.002})TiO_3+0.001MnCO_3+0.05BN$ were fabricated by a thick film process, and the effect of re-oxidation temperature on their resistivities and resistance jumps were investigated, respectively. Ni electroded alumina substrate and the multi-layered PTC thermistor were sintered at $1150^{\circ}C$ for 2 h under $PO_2=10^{-6}$ Pa and then re-oxidized at $600{\sim}850^{\circ}C$ for 20 min. With increasing the re-oxidation temperature, the room temperature resistivity increased and the resistance jump ($LogR_{290}/R_{25}$) decreased, which seems to be related to the oxidation of Ni electrode. The small sized chip PTC thermistor such as 2012 and 3216 exhibits a nonlinear and rectifying behavior in I-V curve but the large sized chip PTC thermistor such as 4532 and 6532 shows a linear and ohmic behavior. Also, the small sized chip PTC thermistor such as 2012 and 3216 is more dependent on the re-oxidation temperature and easy to be oxidized in comparison with the large sized chip PTC thermistor such as 4532 and 6532. So, the re-oxidation conditions of chip PTC thermistor may be determined by considering the chip size.

• Korean Journal of Materials Research
• /
• v.33 no.2
• /
• pp.77-86
• /
• 2023

High-temperature oxidation of a Ni-based superalloy was analyzed with samples taken from gas turbine blades, where the samples were heat-treated and thermally exposed. The effect of Cr/Ti/Al elements in the alloy on high temperature oxidation was investigated using an optical microscope, SEM/EDS, and TEM. A high-Cr/high-Ti oxide layer was formed on the blade surface under the heat-treated state considered to be the initial stage of high-temperature oxidation. In addition, a PFZ (γ' precipitate free zone) accompanied by Cr carbide of Cr₂₃C₆ and high Cr-Co phase as a kind of TCP precipitation was formed under the surface layer. Pits of several ㎛ depth containing high-Al content oxide was observed at the boundary between the oxide layer and PFZ. However, high temperature oxidation formed on the thermally exposed blade surface consisted of the following steps: ① Ti-oxide formation in the center of the oxide layer, ② Cr-oxide formation surrounding the inner oxide layer, and ③ Al-oxide formation in the pits directly under the Cr oxide layer. It is estimated that the Cr content of Ni-based superalloys improves the oxidation resistance of the alloy by forming dense oxide layer, but produced the σ or µ phase of TCP precipitation with the high-Cr component resulting in material brittleness.

• Journal of Electrochemical Science and Technology
• /
• v.13 no.1
• /
• pp.128-137
• /
• 2022

For this study, the sol gel method was used to synthesize the spinel LiNi_0.5Mn_1.5O₄ (LNMO) electrode material. Structural, morphological, electrochemical, and kinetic aspects of the LNMO have been characterized. The synthesized LNMO was indexed with the Fd3m cubic space group. The excellent capacity retention indicates that the spinel framework of LNMO has the ability to withstand high rate charge-discharge throughout long cycle tests. The Li diffusion coefficient (D_Li) changes non-monotonically across three orders of magnitude, from 10^-9 to 10^-12 cm² s^-1 determined from GITT method. The variation of D_Li seemed to be related to three oxidation reactions that happened throughout the charging process. A small dip in D_Li at the beginning stage of Li deintercalation is correlated with the oxidation of Mn³⁺ to Mn⁴⁺. While two pronounced D_Li minima at 4.7 V and 4.75 V are due to the oxidation of Ni²⁺/Ni³⁺ and Ni³⁺/Ni⁴⁺ respectively. The depletion of D_Li at the high voltage region is attributed to the occurrence of two successive phase transformation phenomena.

• Korean Journal of Materials Research
• /
• v.8 no.6
• /
• pp.538-544
• /
• 1998

The spallation of a thermal barrier coating layer depends on the formation of brittle spinels. thermal expansion mismatch between ceramic and metal. the phase transformation of a ceramic layer and residual stress of coating layer. In this work. the formation mechanism of oxide scale formed by oxidation treatment at 90$0^{\circ}C$ was investigated in order to verify oxidation behavior at the interface between E-beam coated $Zr0_2$-7wt.% $Y_20_3$ and plasma sprayed CoNiCrAIY. Some elements distributed in the bond coating layer were selectively oxidized after oxidation. At the initial time of oxidation. AI-depletion zone and $\alpha$-$Al_O_3$,O, were formed at the bond coating layer by the AI-outward diffusion. After layer grew until critical thickness. spinels. $Cr_20$, and $C0_2CrO_4$ by outward diffusion of Co. Cr, Ni were formed. It was found that the formation of spinels may be related to the spallation of $Zr0_2$-7wt.% $Y_20_3$ during isothermal oxidation.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2000.04a
• /
• pp.111-111
• /
• 2000

In order to form a uniform oxidation layer and spinel crystalline phase that has been help strong bonding in Kovar(Fe-29Ni-17Co)-to-glass sealing, the humidified nitrogen and nirtogen/hydrogen mixture was used as an oxidation atmosphere. Kovar oxidation was diffusion-controlled reaction and the activation energy was 25~32 kcal/mol at $600~900^{\circ}C.$ After oxidation at $600^{\circ}C, $ the oxidation layer was under 1 $\mu\textrm{m}$ thickness and crystalline phase was spinel which was found to be suitable for the Kovar-to-glass sealing. The Kovar-to-glass seal was carried out at $1010^{\circ}C$ and humidified nitrogen/hydrogen mixture atmosphere. Sealing properties were tested by Leak tester and SEM.

• Bulletin of the Korean Chemical Society
• /
• v.23 no.5
• /
• pp.669-673
• /
• 2002

Ni catalyst (Ni: 15 wt%) supported on precalcined SiO2 has been investigated in reforming reactions of methane to synthesis gas. The catalyst exhibited fairly good activity and stability in partial oxidation of methane (POM), whereas it deactivated in steam reforming of methane (SRM). Pulse reaction results of CH4, O2, and CH4/O2 revealed that Ni/SiO2 has high capability to dissociate methane. The results also revealed that both CH4 and O2 are activated on the surface of metallic Ni, and then surface carbon species react with adsorbed oxygen to produce CO and CO2 depending on the bond strength of the oxygen species on the catalyst surface.