• Resources Recycling
• /
• v.12 no.6
• /
• pp.57-63
• /
• 2003

In this study, the separation of neodymium was investigated from NdFeB permanent magnet scrap. Decomposition and leach-ing process of NdFeB permanent magnet scrap by oxidation roasting and sulfuric arid leaching were examined. Neodymium could be separated from iron by double salt precipitation using sodium sulfate. The optimum conditions established for decom-position and leaching are as follows: oxidation roasting temperature is $500^{\circ}C$ for sintered scrap and $700^{\circ}C$ for bonded scrap, concentration of sulfuric acid in leaching solution is 2.0 M, leaching temperature and time is $50^{\circ}C$ and 2 hrs, and pulp density is 15%. The leaching yield of neodymium and iron was 99.4% and 95.7% respectively. The optimum condition for separation of neodymium by double-salt precipitation was 2 equivalents of sodium sulfate and $50^{\circ}C$ The yield of neodymium was above 99.9%.

• Resources Recycling
• /
• v.13 no.6
• /
• pp.43-48
• /
• 2004

For the separation of neodymium from NdFeB permanent magnet scrap, the scrap was roasted for oxidizing, and leached with acetic acid followed by fractional crystallization for selective separation. From the analysis results of the leached solution, the optimum condition for the recovery of neodymium was found that leaching temperature, leaching time and pulp density are 80$^{\circ}C$, 3 hours, and 35%, respectively. At this optimum condition, more than 90% of neodymium could be recovered. Concentration of neodymium acetate in acetic acid. The optimum condition for the recovery of neodymium acetate crystal from the leached solution was that the initial leaching solution was evaporated until the remaining volume was about 1/5 of the initial volume. At this condition, 67.5% of neodymium was recovered from the leached solution. The neodymium remaining in the concentrated solution was recovered by reacting it with oxalic acid.

• Proceedings of the Korean Institute of Resources Recycling Conference
• /
• 2004.05a
• /
• pp.191-195
• /
• 2004

• Clean Technology
• /
• v.28 no.2
• /
• pp.110-116
• /
• 2022

In this study, iron oxide (FeO_x) nanoparticles were synthesized using iron (Fe) by-products recovered from NdFeB permanent magnet scraps, and the effect of heat-treatment temperature on the physical properties of the FeO_x nanoparticles was investigated. In order to prepare the FeO_x nanoparticles, 2.0 M ammonia (NH₄OH) solution was added to an iron by-product solution diluted to c.a. 10 wt% in D.I. water, which led to the precipitation of the iron oxide precursor. Then, the FeO_x nanoparticles were synthesized by heat-treatment at 300 ℃, 400 ℃, 500 ℃ and 600 ℃. After that, the physical properties of the FeO_x nanoparticles were investigated in order to understand the effect of the heat-treatment temperature. The results of the X-ray diffraction (XRD) analysis showed that the diffraction peak in accordance with the <104> direction increased as the heat-treatment increased, and a diffraction peak indicating the α-Fe₂O₃ crystal structure was detected at heat-treatment temperatures above 500 ℃. The BET specific surface area analysis revealed that the specific surface area decreased as the heat-treatment temperature increased to above 400 ℃. Observation with a high resolution transmission electron microscope (HRTEM) showed that rod-shaped nanoparticles were formed, and the size of the nanoparticles showed a tendency to increase as the heat-treatment temperature increased.