• Journal of Magnetics
• /
• 제16권2호
• /
• pp.145-149
• /
• 2011

The coercivity $H_c$ of $Nd_2Fe_{14}B$ magnets and $Nd_2Fe_{14}B/(Nd_{0.7}Dy_{0.3})_2Fe_{14}B$ composite magnets were calculated by computer simulation based on the micromagnetic theory under assumptions that $Nd_2Fe_{14}B$ and $(Nd_{0.7}Dy_{0.3})_2Fe_{14}B$ grains have magnetically deteriorated layers on their surfaces and diffusion of Dy from $(Nd_{0.7}Dy_{0.3})_2Fe_{14}B$ grains to $Nd_2Fe_{14}B$ ones through the contacting boundaries recovers the magnetic anisotropy of the deteriorated layers of $Nd_2Fe_{14}B$ grains. $H_c$ of $Nd_2Fe_{14}B/(Nd_{0.7}Dy_{0.3})_2Fe_{14}B$ composite magnets increased by the diffusion of Dy from $(Nd_{0.7}Dy_{0.3})_2Fe_{14}B$ grains to $Nd_2Fe_{14}B$ ones and the resultant recovery of the anisotropy field of deteriorated layers of $Nd_2Fe_{14}B$ grains. The $H_c$ vs fraction of $(Nd_{0.7}Dy_{0.3})_2Fe_{14}B$ grains curve were convex for the magnets with the degree of alignment between 0.94 and 0.99, which suggests that the above composite magnets have larger $H_c$ values than the alloy-magnets with the same Dy content, and that we can save the consumption of Dy by using these composite magnets.

• 한국자기학회지
• /
• 제12권2호
• /
• pp.57-63
• /
• 2002

Nd-Fe-B계 소결자석의 특성을 향상시키기 위해서는 Nd-Fe-B계 합금의 조성 및 제조공정을 조절하여 자성분말의 입도 및 입도분포, 강자성상인 N $d_2$F $e_{14}$B상의 분율, 자성분말의 배향도, 산소 함량, grain size 등과 같은 factor들을 최적화 하여야 한다. 본 연구에서는 실험실 규모로 Nd-Fe-B계 합금 조성 및 공정 조절을 통하여 Nd-Fe-B계 소결자석을 제조하는 연구를 수행하였으며, 분쇄매체 분쇄시간 및 ball size에 따른 Nd-Fe-B계 소결자석의 자기적특성을 분석하여 최적의 분쇄조건을 조사하였다. 또한 분쇄공정 중 FeGa합금을 첨가하여 잔류자속밀도의 감소없이 Nd-Fe-B계 소결자석의 보자력을 향상시킬 수 있었다. 이와 같은 분쇄 조건의 연구, FeGa 합금에 의한 보자력 향상, 건식분쇄 방법 및 powder blending 공정을 적용하여 잔류자속밀도( $B_{r}$,) : 14.4kG, 보자력($_{i}$ $H_{c}$) : 9.4kOe, 최대자기에너지적((BH)$_{\max}$) : 47 MGOe의 자기적 특성을 갖는 Nd-Fe-B계 소결자석을 제조하였다.

• 한국자기학회지
• /
• 제2권1호
• /
• pp.37-43
• /
• 1992

Pr, Nd-Fe-B계 합금을 주조 및 열간압축한 후 직류자화측정기와 진동시료형 자속계를 이용하여 자기적 특성을 측정하였다. 이 결과로부터 제 2상과 보자력과의 관계를 조사하였다. 주조시 $Pr_{17}Fe_{76.5}B_{5}Cu_{1.5}$계 합금에는 ${\alpha}-Fe$가, $Nd_{14}Dy_{1}Fe_{78.5}B_{5}Cu_{1.5}$계 합금에는 $Nd_{2}Fe_{17}$상이 각각 생성 되었다. 생성된 제 2상은 R(R=Pr, Nd)-Fe-B계 주조합금의 자기적 특성을 저하시킨다. 주조합금을 열처리하면 열자기분석 곡선에서 ${\alpha}-Fe$, $Nd_{2}Fe_{17}$상이 확인되지 않았다. 열처리 시 이와 같은 연자성상이 제거됨에 따라 열처리된 Pr, Nd-Fe-B계 주소합금의 자기적 특성은 증가하였다. Nd-Fe-B-Cu계 열간압축 자석에서의 보자력의 온도계수($\beta$)는 0.48로, 이를 Nd-Fe-B계 소결자석의 ${\beta}=0.86$, Nd-Fe-Co-B계 소결자석의 ${\beta}=0.5$와 비교해 보면 열간압축된 자석이 우수한 열적안정성을 나타냄을 알 수 있었다.

• 한국자기학회지
• /
• 제22권3호
• /
• pp.85-90
• /
• 2012

$Nd_2Fe_{14}B$ 화합물 결정의 산화 및 미세 $Nd_2Fe_{14}B$ 결정입자의 보자력에 미치는 산화의 영향을 조사하였다. $Nd_2Fe_{14}B$ 화합물 결정의 산화속도는 $Nd_{15}Fe_{77}B_8$ 합금 잉곳 중의 과잉 성장시킨 $Nd_2Fe_{14}B$ 결정립을 이용하여 조사하였다. $Nd_2Fe_{14}B$ 화합물 결정의 산화는 이 결정상의 ${\alpha}$-Fe, $Fe_3B$, 및 Nd 산화물 복합상으로의 분해에 의해 일어 났다. $Nd_2Fe_{14}B$ 화합물 결정의 산화속도는 결정 방위와는 무관하였다. 산화반응 속도 식은 단순한 직선관계로 나타났다. $Nd_2Fe_{14}B$ 화합물 결정의 산화에 대한 활성화에너지는 약 26.8 kJ/mol로 계산되었다. HDDR 처리한 $Nd_{15}Fe_{77}B_8$ 합금을 볼밀링하여 임계단자구 크기에 유사한 미세한 $Nd_2Fe_{14}B$ 결정입자를 제조하고, 이 입자들을 이용하여 보자력에 미치는 산화의 영향을 조사하였다. 임계단자구 크기에 유사한 미세한 $Nd_2Fe_{14}B$ 결정입자(${\fallingdotseq}0.3\;{\mu}m$)는 9 kOe 이상의 높은 보자력을 가졌다. 그러나, 이 보자력은 공기 중에서 온도 상승에 따라 급격하게 저하하였다($200^{\circ}C$에서 2 kOe 이하). 이러한 급격한 보자력의 감소는 산화에 의해 미세 입자의 표면에 형성된 연자성 ${\alpha}$-Fe 및 $Fe_3B$ 상 때문으로 판단되었다.

• 한국분말재료학회지
• /
• 제20권3호
• /
• pp.169-173
• /
• 2013

High-coercive (Nd,Dy)-Fe-B magnets were fabricated via dysprosium coating on Nd-Fe-B powder. The sputtering coating process of Nd-Fe-B powder yielded samples with densities greater than 98%. $(Nd,Dy)_2Fe_{14}B$ phases may have effectively penetrated into the boundaries between neighboring $Nd_2Fe_{14}B$ grains during the sputtering coating process, thereby forming a $(Nd,Dy)_2Fe_{14}B$ phase at the grain boundary. The maximum thickness of the Dy shell was approximately 70 nm. The maximum coercivity of the Dy sputter coated samples(sintered samples) increased from 1162.42 to 2020.70 kA/m. The microstructures of the $(Nd,Dy)_2Fe_{14}B$ phases were effectively controlled, resulting in improved magnetic properties. The increase in coercivity of the Nd-Fe-B sintered magnet is discussed from a microstructural point of view.

• 한국자기학회지
• /
• 제8권4호
• /
• pp.210-215
• /
• 1998

Ball Mill을 이요하여 Ar 분위기에서 기계적합금법으로 Nd15Fe77B8과 Nd16Fe76B8 분말을 제조하고, 제조된 분말을 연속 진공열처리 시킨 후 열처리온도에 따른 상변화 및 자기적 성질을 조사하엿다. 450시간 볼밀도처리한 Nd15Fe77B8과 Nd16Fe76B8 합금 분말에서 Nd와 B의 피크는 보이지 않고 전체적으로 $\alpha$-Fe 결정상만 존재하고 있었으며, 이를 $700^{\circ}C$에서 30분간 열처리를 시키면 고상반응에 의하여 Nd2Fe14B와 소량의 NdB6이 흔재된 상을 얻을 수 있었다. $700^{\circ}C$로 열처리 한 Nd16Fe76B8 합금 분말은 iHc9.9kOe, Bs, 12.9 KG, (BH)max 10.1 MGOe의 자기적 성질을 나타내었다.

• Journal of Magnetics
• /
• 제13권3호
• /
• pp.102-105
• /
• 2008

This study examined the feasibility of the combining HDDR-process (hydrogenation, disproportionation, desorption and recombination) with mechanical milling to prepare single domain $Nd_2Fe_{14}B$ particles from a Nd-Fe-B alloy ingot. The $Nd_{15}Fe_{77}B_8$ alloy was HDDR-treated and then subjected to a roller-milling. In the HDDR-treated $Nd_{15}Fe_{77}B_8$ alloy, very small $Nd_2Fe_{14}B$ grains comparable to their critical single domain size(0.3 ${\mu}m$) were observed. These fine individual grains were separated successfully along the grain boundaries by a roller-milling. The separated $Nd_2Fe_{14}B$ grains were found to be single domain particles. These results suggest that single domain particles of the $Nd_2Fe_{14}B$ phase can be prepared from a Nd-Fe-B ingot alloy by combining a HDDR-process with mechanical milling.

• 한국자기학회지
• /
• 제1권2호
• /
• pp.60-68
• /
• 1991

급속냉각기술로 제조된 $Nd_{14}Fe_{76}Co_{4}B_{6}$ 및 $Nd_{10.5}Fe_{79}Co_{2}Zr_{15}B_{7}$ 자성분말을 사용하여 성형체와 본드자석을 제조하였다. 자기특성, 최적충진률 등의 분말입도 및 형상비에 따른 거동은 합금조성에 따라 달리 나타난다. Co/Fe 비가 작은 저밀도의 $Nd_{10.5}Fe_{79}Co_{2}Zr_{1.5}B_{7}$ 합금이 같은 성형압력에서 성형체의 성형밀도 및 최적충진률이 높아 자기특성이 우수하였으나 반면에 분말입도에 따라 자기특성이 변화하였다. 성형밀도(p)와 성형압력(P) 사이 에는 ${\phi}(g/cm^{2})=5.2~5.6{\times}P^{0.045~0.065}(ton/cm^{2})$의 관계식이 성립된다. 높은 Nd/Fe 비를 갖는 급속냉각된 $Nd_{14}Fe_{76}Co_{4}B_{6}$ 합금의 초미세립(50~60 nm)으로써 높은 보자력($iH_{c}=14~15kOe$)을 보유하나, Nd/Fe비가 낮은 $Nd_{10.5}Fe_{79}Co_{2}Zr_{1.5}B_{7}$ 합금은 결정립이 조대하고(150~400 nm)Nd-rich한 입경계상의 발달이 부진하여 자벽고착기구가 주 보자력 기구 로 판명된 두 합금에서 고착지점으로서의 역할이 불충분하여 보자력이 낮은 것으로 판명되었다.

• 한국자기학회지
• /
• 제7권1호
• /
• pp.44-48
• /
• 1997

약 30 nm의 미세결정립으로 구성된 ( .alpha. -Fe)-(Nd$_{2}$Fe$_{14}$B$_{1}$)형 저 Nd함유 Nd-Fe-B계 합금이 급속응고법으로 제조된 비정질상으로 부터 결정화하여 제조되었다. Nd$_{4}$Fe$_{82}$B$_{10}$Mo$_{3}$Cu$_{1}$ 조성에 Ga의 첨가는 각형성 개선효과와 함께 잔류자화를 1.29 T까지 증가시킨다. Nd의 함유량을 증가시킨 초미세결정립 Nd$_{5}$Fe$_{81}$B$_{9}$Mo$_{3}$Cu$_{1}$Ga$_{1}$ 합금의 Nd$_{2}$Fe$_{81}$B$_{9}$Mo$_{3}$Cu$_{1}$Ga$_{1}$ 합금의 잔류자화, 보자력 및 최대자기에너지적은 각각 1.24 T, 257.4 kA/m(3.23 kOe), and 100.3 kJ/m$^{3}$(12.6 MGOe)이다.다.

• 한국자기학회지
• /
• 제5권1호
• /
• pp.38-41
• /
• 1995

$\alpha$-Fe를 주상으로 하는 새로운 Nd-Fe-B계 합금을 개발하기 위하여 Nd 함유량을 4at.%로 고정시킨 Nd-Fe-B 초미세결정립합금의 제조 및 자기특성이 조사되었다. 급속응고법으로 제조된 $Nd_{4}Fe_{85.5}B_{10.5}$ 비정질합금은 결정화하여 $\alpha$-Fe 기지상에 $Nd_{2}Fe_{14}B$이 형성되나 자기특성${_{i}H_{c}=95.5kA/m(1.2kOe),\;Br=1.2T}$은 열화된다. Nb 및 Cu를 첨가한 $Nd_{4}Fe_{82}B_{10}Nb_{3}Cu_{1}$ 합금은 $\alpha$-Fe 결정립미세화(<30nm)로 보자력이 207kA/m(2.6 kOe)로 증가하나 잔류자화는 개선되지 않았다. 이 합금조성에 8at.% Co 첨가는 결정립을 더욱 미세화시키며 자기특성을 개선 시킨다. 최적열처리조건에서 $Nd_{4}Fe_{74}Co_{8}B_{10}Nb_{3}Cu_{1}$ 합금의 잔류자화, 보자력 및 최대에너지적이 각각 1.34 T, 219 kA/m (2.75kOe) 및 $95.5kJ/m^{3}$(12MGOe) 이다.