분석시료에 일정량의 표준물을 첨가한 후 희석제로 묽히는 방법을 이용하여 주석슬랙중의 $Ta_2O_5$,$Nb_2O_5$ 및 $SnO_2$를 X-선 분광 분석법으로 정량하였다. 희석제로는 $SiO_2$와 $Fe_2O_3$를 사용하였으며 첨가시료와 1:1의 비로 희석 시켰다. $Ta_2O_5$와 $SnO_2$ 의 분석결과는 $Fe_2O_3$보다 $SiO_2$로 희석시킨 것이 표준 검정곡선법에 의해 얻은 분석값과 더 잘 일치하고, $Nb_2O_5$는 이와 반대로 $SiO_2$보다 $Fe_2O_3$로 희석시킨 것이 더 잘 일치함을 보여주었다.

• Bulletin of the Korean Chemical Society
• /
• 제31권12호
• /
• pp.3679-3683
• /
• 2010

Niobium oxide ($Nb_2O_5$) and phosphated $Nb_2O_5$ were synthesized and used as catalysts for sorbitol dehydration to isosorbide. The characterization results of $N_2$ adsorption, XRD and $NH_3$-TPD revealed that the phosphoric acid modification could well prevent the crystallization of $Nb_2O_5$. And the amorphous phosphated $Nb_2O_5$ catalysts kept the relatively large surface area and stable acidity at high calcination temperature. The catalytic results showed that the selectivity to isosorbide could be dramatically enhanced over phosphated $Nb_2O_5$. The excellent catalytic performance with 100.0% sorbitol conversion and 62.5% isosorbide selectivity were obtained over the 0.8P/NBO-400 catalyst. Comparing with $Nb_2O_5$ catalysts, phosphated $Nb_2O_5$ catalysts regenerated through a simple calcination process showed no significant activity loss after recycling three runs.

• 한국결정성장학회지
• /
• 제12권1호
• /
• pp.27-30
• /
• 2002

Liquid phase epitaxy(LPE)법을 이용하여 ZnO co-doped Er:$LiNbO_3$, 단결정 박막을 $LiNbO_3$ (001) 기판 위에 성장시켰다. ZnO co-doped Er:$LiNbO_3$박막 성장의 초기 융액은 첨가제 $Er_2O_3$ 농도를 1 mol%로 고정시키고 ZnO 농도를 3,5 mol%로 조절하였다. ZnO co-doped Er :$LiNbO_3$박막의 결정성은 $LiNbO_3$ 기판보다 더 우수하였다. ZnO 5mol% 첨가한 경우 박막의 표면에는 수직한 방향과 평행한 방향으로 모두 압축응력이 작용하고 있었다. 또한 ZnO 3mol% 첨가된 Er :$LiNbO_3$박막의 표면은 원래의 $LiNbO_3$기판보다 더 평탄하였다

• 한국세라믹학회지
• /
• 제38권4호
• /
• pp.308-313
• /
• 2001

We report the effects of the V$_2$O$_{5}$ additive on the sintering behavior and microwave dielectric properties of ZnNb$_2$O$_{6}$ ceramics. Densification temperatures of V$_2$O$_{5}$-doped ZnNb$_2$O$_{6}$ samples are lowered to the range of 875-9$25^{\circ}C$ because of the liquid phase sintering. Doped samples are composed of a Zn(Nb,V)$_2$O$_{6}$ solid solution and second phases. Up to 5 wt% V$_2$O$_{5}$ is the only second phase, however, V$_2$O$_{5}$ also exists as the second phase for 10 wt% V$_2$O$_{5}$ addition. In comparison with reported values of undoped ZnNb$_2$O$_{6}$ ceramics, microwave properties of V$_2$O$_{5}$-doped ZnNb$_2$O$_{6}$ samples are seriously degraded, which is confirmed to originate from the second phases. The optimum microwave properties (Q$\times$f=13,800, $\varepsilon$$_{r}$=23, $\tau$$_{f}$=-66ppm/$^{\circ}C$) are obtained from ZnNb$_2$O$_{6}$ with the addition of 5 wt% V$_2$O$_{5}$ sintered at 90$0^{\circ}C$.90$0^{\circ}C$.EX>.

• 한국에너지공학회:학술대회논문집
• /
• 한국에너지공학회 1995년도 춘계학술발표회 초록집
• /
• pp.45-52
• /
• 1995

광 촉매로 널리 알려진 TiO$_2$의 광 분해 거동의 변화를 관찰하기 위하여 Nb$_2$O$_{5}$를 첨가하여 sol-gel 용법으로 제조한 후 DCA(dichloroacetic acid) 의 광분해 효율을 측정하였다. Sol-gel process 과정에서 첨가된 Nb$_2$O$_{5}$의 농도 및 열처리 온도변화에 따른 광분해 효율을 관찰한 결과, Nb$_2$O$_{5}$를 첨가한 후 40$0^{\circ}C$에서 한시간 동안 열처리 한 광 촉매의 광분해 효율이 가장 높게 나타났다. 또한 열처리 온도와 무관하게 Nb$_2$O$_{5}$의 양이 증가할수록 광분해 효율은 감소하는 것으로 관찰되었다. 이는 excess electron 의 증가로 환원 반응 혹은 recombination rate기 증가하기 때문이라고 사료된다. 분해 대상 물질의 pH가 낮을수록 광분해 효율이 증가하는 것을 알 수 있었다.알 수 있었다.

• Transactions on Electrical and Electronic Materials
• /
• 제8권5호
• /
• pp.201-205
• /
• 2007

Low temperature sintering behavior and microwave dielectric properties of the $BiNbO_{4^-}$ and the $ZnNb_2O_{6^-}zinc$ borosilicate glass(ZBS) systems were investigated with a view to applying the composition to LTCC technology. The addition of $10{\sim}30$ wt% ZBS in both systems ensured successful sintering below $900^{\circ}C$. For the $BiNbO_{4^-}ZBS$ system, the sintering was completed when 15 wt% ZBS was added whereas 25 wt% ZBS was necessary for the $ZnNb_2O_{6^-}zinc$ system. Secondary phase was not observed in the $BiNbO_{4^-}ZBS$ system but a small amount of $ZnNb_2O_6$ with the willemite structure as the secondary phase was observed in the $ZnNb_2O_{6^-}ZBS$ system. In terms of dielectric properties, the application of the $BiNbO_{4^-}$ and the $ZnNb_2O_{6^-}ZBS$ systems sintered at $900^{\circ}C$ to LTCC were shown to be appropriate; $BiNbO_{4^-}15$ wt% ZBS($\varepsilon_r=25,\;Q{\times}f\;value=3,700GHz,\;\tau_f=-32ppm/^{\circ}C$) and $ZnNb_2O_{6^-}25$ wt% ZBS($\varepsilon_r=15.8,\;Q{\times}f\;value=5,400GHz,\;\tau_f=-98ppm/^{\circ}C$).

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 추계학술대회 논문집
• /
• pp.291-294
• /
• 2000

The crystallization behavior and dc Conductivities of CuO-P$_2$O$_{5}$ -Nb$_2$O$_{5}$ -V$_2$O$_{5}$ glasses prepared by quenching on the copper plate were investigated. The conductivities of the glasses were range from 10$^{-5}$ s.$cm^{-1}$ / at room temperature, but the conductivities of the glass-ceramics were 10$^{-3}$ s.$cm^{-1}$ / increased by 10$^2$order. The crystalline product in the glass-ceramics was CuV$_2$O$_{6}$ . The linear relationship between in($\sigma$T) and T$^{-1}$ suggested that the electrical conduction in the present glass-ceramics would be due to a small polaron hopping mechanism.

• 한국전기전자재료학회논문지
• /
• 제14권6호
• /
• pp.475-480
• /
• 2001

Glasses in he system CuO-P$_2$O$_{5}$ -Nb$_2$O$_{5}$ -Nb$_2$O$_{5}$ -V$_2$O$_{5}$ were prepared by a press-quenching method on the copper plate. the glass-ceramics from these glasses were obtained by post-heat treatment, and the crystallization behavior and DC conductivities were determined. The conductivities of the glasses were range from 10$^{-6}$ s.$cm^{-1}$ / at room temperature ,but the conductivities of the glass-ceramics were 10$^{-3}$ s.$cm^{-1}$ / increased by 10$^3$ order. The crystalline product in the glass-ceramics was CuV$_2$O$_{6}$ . the crystal growth of CuV$_2$O$_{6}$ phase increased with heat-treatment conditions. The linear relationship between il($\sigma$T) and T$^{-1}$ suggested that the electrical conduction in the present glass-ceramics would be due to a small polaron hopping(SPH) mechanism.

• 한국결정성장학회지
• /
• 제7권3호
• /
• pp.377-383
• /
• 1997

이트리아 안정화 지르코니아(Y-TZP)에 5가 산화물$(Ta_2O_5,\;Nb_2O_5)$을 첨가하여 $1500^{\circ}C$온도에서 상압소결한 삼성분계중 quasi-binary system인 $ZrO_2-YTa(Nb)O_4$의 조성영역안에서 상 안정성을 관찰하기 위해 상태도를 작성하였으며, 결정립 크기나 annealing 온도에 상관없이 상 안정성을 유지하는 non-transformable $t-ZrO_2$ solid solution$(NT_{ss}$ )영역을 확인하고 안정화 mechanism을 조사하였다. $NT_{ss}$ 의 상 안정성은 정방정 fergusonite 구조를 갖는 $YTa(Nb)O_4$의 안정화로 상 변태를 억제하여 우수한 상 안정성을 유지하는 것으로 추정되었다. 기계적 특성을 향상시키기 위해 상 변태율이 가장 좋은 transformable-TZP $(T_{ss/})$ 를 에 첨가하여 조사한 결과 mixture의 조성이 $NT_{ss}$ 영역밖의 $NT_{ss}$영역에 위치하여도 상 안정성과 우수한 기계적 특성을 갖는다는 것이 발견되었다.

• 한국재료학회지
• /
• 제8권10호
• /
• pp.956-960
• /
• 1998

XPS와 glancing angle XRD, AES 및 AFM을 사용하여 $330^{\circ}C$-$800^{\circ}C$사이의 진공분위기에서 열처리할 때, Co/Nb이중층과 $SiO_2$기판 사이의 계면반응을 조사하였다. $600^{\circ}C$에서 Co와 Nb는 서로 활발하게 확산하여, $700^{\circ}C$이상에서는 두 층사이의 충역전이 완전히 일어났다. 그 때 Nb 중간층과 $SiO_2$기판 사이의 반응에 의하여 계면에 일부 NbO가 형성되었으며, 표면에서는 분위기 중의 산소에 의하여 $Nb_2O_5$가 생성되었다. Nb와 기판간의 반응에 의하여 유리된 Si는 $600^{\circ}C$이상에서 잔류 Co 및 Nb와 반응하여 실리사이드를 형성하였다. Co/Nb 이중층 구조는 $800^{\circ}C$에서 열처리한 후 면저항이 급증하기 시작하였는데, 이것은 Co층이 기판과 바로 접하게 되어 계면에너지를 줄이기 위해 응집되기 때문이다.