• Electrical & Electronic Materials
• /
• v.9 no.6
• /
• pp.605-615
• /
• 1996

In this paper, the effect of alkaline oxide addition such as Li$_{2}$O and Na$_{2}$O on the microstructure and humidity sensitivity of V$_{2}$O$_{5}$(2 mol%)-doped TiO$_{2}$(98 mol%) was investigated as a function of amount (0, 1, 2, 5, 10 mol%) of Li$_{2}$O and Na$_{2}$O additives. The pores in the alkaline free sample were distributed mostly in the range between 0.16 and 1.0.mu.m in diameter and its porosity was 23.29%. Li$_{2}$O caused grain overgrowth and reduced the porosity with a narrow distribution of the pore size, leading to poor humidity sensitivity. Na$_{2}$O helped to enlarge the distribution of the pore size through the formation of small soluble phases. The pore sizes of the sample containing Na$_{2}$O 2mol% were distributed mostly in the range between 1.0 and 2.5.mu.m in diameter and its porosity and intrusion volume of mercury were 31.13 % and 0.1155 mL/g respectively, which consequently improved the humidity sensing characteristics such as the sensitivity and temperature-stability. Especially, the addition of 2mol% of Na$_{2}$O improved the humidity-sensing characteristics such as sensitivity and linearity in the whole range between 30 and 90 %RH (Percentage Relative Humidity)y)

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.17 no.3
• /
• pp.383-392
• /
• 2015

In subsea tunnelling, prediction of the fractured zone (or water bearing zone) ahead of tunnel face saturated by seawater with high water pressure has been a key factor for safe construction. This study verified the feasibility of utilizing induced polarization (IP) survey at tunnel face for predicting the ground condition ahead of the subsea tunnel face. A pore model was proposed to compute chargeability in granular material, and the relationship correlating chargeability with the variables affecting the chargeability was derived from the model. Parametric study has been performed on the variables to figure out the most influential factors affecting the chargeability. The results of the parametric study show that the size of narrow pores ($r_1$) and the salinity of pore water are the most influential factors on chargeability. Laboratory tests were conducted on various types of ground condition by changing the salinity of pore water, the thickness of the fracture zone and the existence of gouge (weathered granite) within the joints of the fractured zone to figure out the effect of the ground characteristics on the IP phenomenon. Test results show that the chargeability of the fractured zone saturated by seawater increases if the joints in the fractured zone are filled with gouge since the infilled gouge will decrease the size of narrow pores ($r_1$).

• The Korean Journal of Ceramics
• /
• v.3 no.1
• /
• pp.52-56
• /
• 1997

The Pt doped $TiO_2$ composite membranes were prepared by the sol-gel process. The Pt doped titania sol was peptized with hydrochloric acid in the pH range of 1.23 to 1.32 at 5$0^{\circ}C$. The average particle size of the Pt doped titania sol was shown to be below 15nm and well dispersed in the solution. XPS show the Pt elements continuous and homogeneous dispersed in the $TiO_2$ membrane. The mean particle size of the Pt doped $TiO_2$ composite membrane has smaller than that of the undoped $TiO_2$ composite membrane. The average pore size of the Pt doped $TiO_2$ composite membrane was increased from 58 to 193 $\AA$ with firing temperature changed from 550 to 85$0^{\circ}C$. It was observed that the Pt doped $TiO_2$ composite membranes showed crack-free and homogeneous microstructue as well as narrow particle size distribution up to above 75$0^{\circ}C$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.27 no.7
• /
• pp.448-451
• /
• 2014

Anodic aluminum oxides (AAO) fabricated by the two-step anodizing process have attracted much attention for the fabrication of nano template because of pore structure with high aspect ratio, low cost process and ease of fabrication. AAOs are characterized by a homogeneous morphology of parallel pores that grow perpendicular to the template surface with a narrow distribution of diameter, length and inter-pores spacing, all of which can be easily controlled by suitably choosing of the anodizing parameters such as pH of the electrolyte, anodizing voltage and duration of anodizing. In this study, AAO templates were characterized by X-ray diffraction and field-emission scanning electron microscope (FE-SEM). The dependence of the pore size change according to the amount of addition of phosphoric acid, which was used to remove the initial alumina oxide layer, was not observed.

• Journal of the Korean Ceramic Society
• /
• v.25 no.1
• /
• pp.59-65
• /
• 1988

To develop porous glass membranes used for a effective membrane-separation process, porous glasses and glass membranes were prepared from the sodium borosilicate parent glass by the phaseseparation technique and effects of heat-treatment and leaching conditions on their characteristics were investigated. The crack-free glass membranes could be fabricated from the 9.4 Na2-O-30.7 B2O3-59.2 SiO2-0.7 Al2O3(wt%) parent glass by heat-treatment at the lower temperature(550-570$^{\circ}C$) and for longer than 45 hrs for the phase separation, followed by leaching with 3N-HCl＋60% ethylene glycol solution at 90$^{\circ}C$ over 25 hrs. Porous glasses prepared in this work showed large specific surface areas(400㎡/g) and narrow pore size distribution with the mean pore radius of 14${\AA}$ enough for the application as reverse osmosis membranes. The salt-rejection efficiency and product-flux of the glass membranes heat-treated at 570$^{\circ}C$ for 80 hrs were found to be 51.8% and 270cc/㎡. hr, respectively. This result suggests that the porous glass membranes fabricated in this study could be applied for the reverse osmosis process.

• Carbon letters
• /
• v.1 no.1
• /
• pp.6-11
• /
• 2000

Coal tar pitch was chemically modified with 10 wt% benzoquinone (BQ) to raise the softening point of isotropic pitch precursor and the precursor was melt-spun into pitch fibers, stabilized, carbonized and activated with steam at $900^{\circ}C$. The weight loss of carbon fiber-benzoquinone (CF-BQ) increased with the increase of activation time like other fibers, but was lower than those of Kureha fiber at the same activation time in spite of larger geometric surface area. Those adsorption isotherms fitted into 'Type I' according to Brunauer, Deming, Deming and Teller classification. However, there was very thin low-pressure hysteresis that lower closure points of the hysteresis are about 0.42-0.45. From the pore size distribution curves, there might be some micropores having narrow-necked bottle; a series of interconnected pore is more likely than discrete bottles. FT-IR studies showed that the functional groups such as carboxyl, quinone, and phenol were introduced to ACFs-BQ surface after steam activation. Methylene blue decolorization and iodine adsorption capacity of ACF-BQ increased linearly with the increase of specific surface area and was larger than that of ACF-Kureha at the same specific surface area.

• Composites Research
• /
• v.31 no.5
• /
• pp.267-275
• /
• 2018

A facile method for the preparation of nitrogen-doped microporous carbon via the pyrolysis of poly(vinylidene fluoride) (PVDF) using polypyrrole (PPy) as a selective nitrogen source was developed. A PVDF/PPy-800 sample (carbonized at $800^{\circ}C$) with a 1:0.5 ratio of PVDF and PPy exhibited the highest micropore volume. The activated microporous carbon materials obtained from PVDF/PPy-800 prepared at $800^{\circ}C$ with KOH possessed a large specific surface area and narrow pore-size distribution. They were characterized using $N_2$ adsorption at 77 K and argon (Ar) adsorption at 87 K, which allowed for the characterization of the narrow microporosity of the prepared materials due to the absence of interactions between Ar and the sample surface. In addition, the activated microporous carbon material with a KOH/carbon ratio of 2:1 was found to exhibit the largest specific surface area ($1296m^2g^{-1}$ in $N_2$ at 77 K) and microporosity, and a high specific capacitance ($122.8F\;g^{-1}$).

• Journal of Powder Materials
• /
• v.25 no.3
• /
• pp.203-207
• /
• 2018

Plastic pollution is threatening human health and ecosystems, resulting in one of the biggest challenges that humanity has ever faced. Therefore, this study focuses on the preparation of macroporous carbon from biowaste (MC)-supported manganese oxide ($MnO_2$) as an efficient, reusable, and robust catalyst for the recycling of poly(ethylene terephthalate) (PET) waste. As-prepared $MnO_2/MC$ composites have a hierarchical pore network and a large surface area ($376.16m^2/g$) with a narrow size distribution. $MnO_2/MC$ shows a maximum yield (98%) of bis(2-hydroxyethyl)terephthalate (BHET) after glycolysis reaction for 120 min. Furthermore, $MnO_2/MC$ can be reused at least nine times with a negligible decrease in BHET yield. Based on this remarkable catalytic performance, we expect that $MnO_2$-based heterogeneous catalysts have the potential to be introduced into the PET recycling industry.

• Korea-Australia Rheology Journal
• /
• v.20 no.2
• /
• pp.65-71
• /
• 2008

Pressure filtration technique was used to obtain defect-free microstructure of green cast ceramic bodies. Stable alumina suspensions of desired rheology (<5 Pa s at $1\;s^{-1}$) containing 60-80 mass. % solid loading were prepared in the alkaline region (at $pH{\approx}9$) with an optimum amount of 0.5 dmb % of Tiron added. Acidic region (at $pH{\approx}4$) enabled the preparation of 60 mass. % suspensions with addition of 1.5 dmb % of Tiron. The best quality slip was processed from an 80 mass.% suspension with 63% of theoretical density. The homogeneity of particle packing and the absence of defects in microstructure were proven by narrow pore size distribution (ranging from 32 to 64 nm, with up to 85% abundance), confirming advantages of the wet consolidation route.

• The Korean Journal of Ceramics
• /
• v.5 no.1
• /
• pp.73-77
• /
• 1999

Capsule free hot isostatic pressing (HIPing) of 12 mol% $CeO_2-88 mo% ZrO_2 (12CeO_2-88ZrO_2)$ powder was conducted at 1100~$1200^{\circ}C$ using the powder crystallized in supercritical methanol followed by supercritical drying. Porous $12CeO_2-88ZrO_2$ ceramics with ~35% open porosity, micropore diameter of ~23 nm and a narrow pore size distribution were fabricated by capsule free hot isostatic pressing at $1100^{\circ}C$. The porosity increased with decrease in HIPing temperature and was accompanied by a steady decrease in fracture strength.