• Transactions on Electrical and Electronic Materials
• /
• v.16 no.4
• /
• pp.206-211
• /
• 2015

We investigated the formation of a nanopyramidal structure and fabricated nanotextured Si solar cells using an Ag metal-assisted chemical etching process. The nanopyramidal structure was formed on a Si flat surface and the nanotexturing process was performed on the p-type microtextured Si surface. The nanostructural formation shows a transition from nanopits and nanopores to nanowires with etching time. The nanotextured surfaces also showed the photoluminescence spectra with an enhanced intensity in the wavelength range of 1,100~1,250 nm. The photoreflectance of the nanotextured Si solar cells was strongly reduced in the wavelength range of 337~596 nm. However, the quantum efficiency is decreased in the nanotextured samples due to the increased nanosurface recombination. The nanotexturing process provides a better p-n junction impedance of the nanotextured cells, resulting in an enhanced shunt resistance and fill factor which in turn renders the possibility of the increased conversion efficiency.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.280-280
• /
• 2014

We report the fabrication and electroluminescent characteristics of GaN/InxGa1-xN microdonut-shaped light-emitting diode (LED) microarrays as variable-color emitters. The diameter, width, height, and period of the GaN microdonuts were controlled by their growth parameters and the geometrical factors of the growth mask patterns. For the fabrication of microdonut LEDs, p-GaN/p-AlxGa1-xN/u-GaN/u-InxGa1-xN heteroepitaxial layers were coated on the entire surface of n-GaN microdonuts. The microdonut LED arrays showed strong light emission, which could be seen with the unaided eye under normal room illumination. Additionally, magnified optical images of microdonut LED arrays exhibited microdonut-shaped light emissions having spatially resolved blue and green colors. Their electroluminescence spectra had two dominant peaks at 460 and 560 nm. With increasing applied voltage, the intensity of the blue emission peak increased much faster than that of the green emission peak, indicating that the color of the LEDs is tunable. We also demonstrated that EL spectra of the devices could be controlled by changing the size of microdonut LEDs. What we want to emphasize here with the microdonut LEDs is that they have additional inner sidewall facets which did not exist for other typical three-dimensional structures including nanopyramids and nanorods, and that InxGa1-xN single quantum well formed on the inner sidewall facets had unique thickness and chemical composition, which generated additional EL color. The origin of the electroluminescence peaks was investigated by structural characterizations and chemical analyses.