• Korean Journal of Materials Research
• /
• v.21 no.7
• /
• pp.396-402
• /
• 2011

In this study, by using tin chloride solution as a raw material, a nano-sized tin oxide powder with an average particle size below 50 nm is generated by a spray pyrolysis process. The properties of the generated tin oxide powder depending on the inflow speed of the raw material solution are examined. When the inflow speed of the raw material solution is 2 ml/min, the majority of generated particles appear in the shape of independent polygons with average size above 80-100 nm, while droplet-shaped particles show an average size of approximately 30 nm. When the inflow speed is increased to 5 ml/min, the ratio of independent particles decreases, and the average particle size is approximately 80-100 nm. When the inflow speed is increased to 20 ml/min, the ratio of droplet-shaped particles increases, whereas the ratio of independent particles with average size of 80-100 nm decreases. When the inflow speed is increased to 100 ml/min, the average size of the generated particles is around 30-40 nm, and most of them maintain a droplet shape. With a rise of inflow speed from 2 ml/min to 5 ml/min, a slight increase of the XRD peak intensity and a minor decrease of specific surface area are observed. When the inflow speed is increased to 20 ml/min, the XRD peak intensity falls dramatically, although a significant rise of specific surface area is observed. When the inflow speed is increased to 100 ml/min, the XRD peak intensity further decreases, while the specific surface area increases.

• Membrane and Water Treatment
• /
• v.10 no.4
• /
• pp.287-298
• /
• 2019

Lotus leaf has a special dual micro and nano surface structure which gives its highly hydrophobic surface characteristics and so-called self cleaning effect. In order to endow PVDF hollow fiber membrane with this special structure and improve the hydrophobicity of membrane surface, PVDF hollow fiber composite membranes was obtained through the immersion coating of poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) dilute solution on the outside surface of PVDF support membrane. The prepared PVDF composite membranes were used in the vacuum membrane distillation (VMD) for the desalination. The effects of PVDF-HFP dilute solution concentration in the dope solution and coating time on VMD separation performance was studied. Membranes were characterized by SEM, WCA measurement, porosity, and liquid entry pressure of water. VMD test was carried out using $35g{\cdot}L^{-1}$ NaCl aqueous solution as the feed solution at feed temperature of $30^{\circ}C$ and the permeate pressure of 31.3 kPa. The vapour flux reached a maximum when PVDF-HFP concentration in the dilute solution was 5 wt% and the coating time was kept in the range of 10-60 s. This was attributed to the well configuration of micro-nano rods which was similar with the dual micro-nano structure on the lotus leaf. Compared with the original PVDF membrane, the salt rejection can be well maintained which was greater than 99.99 % meanwhile permeation water conductivity was kept at a low value of $7-9{\mu}S{\cdot}cm^{-1}$ during the continuous testing for 360 h.

• Textile Coloration and Finishing
• /
• v.32 no.3
• /
• pp.167-175
• /
• 2020

In this study, the optimum conditions for manufacturing PVDF nano web according to various electrospinning conditions such as solution concentration and applied voltage conditions were confirmed. The optimum spinning conditions were studied by analyzing the changes in the radioactivity of PVDF/TiO₂ nano web according to the TiO₂ content and the content of β-phase closely related to the piezoelectric properties under established conditions. As a result, it was confirmed that the concentration of the spinning solution was 20 wt%, the applied voltage was 25 kV, and the TiO₂ content was 5 phr. PVDF nano web and PVDF/TiO₂ nano web were observed morphologies through Scanning Electron Microscope(SEM) analysis. Formation of β-phase by electrospinning was confirmed by Fourier transform infrared spectroscopy(FT-IR) and X-ray Diffractometer(XRD), and the effect of the trapped nano web structure on the piezoelectric properties was investigated.

• Advances in environmental research
• /
• v.9 no.2
• /
• pp.135-150
• /
• 2020

Many industries, such as textiles, chemical refineries, leather, plastics and paper, use different dyes in various process steps. At the same time, these industrial sectors are responsible for discharging contaminants that are harmful and toxic to humans and microorganisms by introducing synthetic dyes into wastewater. Of these dyes, methylene blue dye, which is classified as basic dyes, is accepted as a model dye. For this reason, methylene blue dye was selected in the study and its removal from the water was studied. In this study, two efficient biosorbents were developed from chitosan and sunflower waste, an agro-industrial waste and modified using iron nanoparticles. The biosorption efficiency was evaluated for methylene blue (MB) dye removal from aqueous solution under various parameters such as treating agent, solution pH, biosorbent dosage, contact time, initial dye concentration and temperature. We investigated the kinetic properties of dye removal from water for Chitosan-Sunflower (CS), Chitosan-Sunflower-Nanoiron (CSN). When the wavelength of MB dye was spectrophotometrically scanned, the maximum absorbance was determined as 660 nm. For the core shell biosorbents we obtained, we found that the optimum time for removal of MB from wastewater was 60 min. The pH of the best pH was determined as 5 in the studied pH. The most suitable temperature for the experiment was determined as 30℃. SEM-EDAX, TEM, XRD, and FTIR techniques were used to characterize biosorbents produced and modified in the experimental stage and to monitor the change of biosorbent after dye removal. The interactions of the paint with the surface used for removal were explained by these techniques. It was calculated that 80% of CS and 88% of CSN removed MB in optimum conditions. Also, the absorption of MB dye onto the surface was investigated by Langmiur and Frendlinch isotherms and it was determined from the results that the removal was more compatible with Langmiur isotherm.

• Journal of Powder Materials
• /
• v.15 no.3
• /
• pp.234-238
• /
• 2008

Al-Cu alloy nano powders have been produced by the electrical explosion of Cu-plated Al wire. The porous nano particles were prepared by leaching for Al-Cu alloy nano powders in 40wt% NaOH aqueous solution. The surface area of leached powder for 5 hours was 4 times larger than that of original alloy nano powder. It is demonstrated that porous nano particles could be obtained by selective leaching of alloy nano powder. It is expected that porous Cu nano powders can be applied for catalyst of SRM (steam reforming methanol).

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2005.10a
• /
• pp.83-86
• /
• 2005

In this study, SAM (self-assembled monolayer) was applied as an anti-adhesion layer in the nano molding process, to reduce the surface energy between the nano-stamper and the moldeded polymeric nano patterns. Before depositing SAM on the stamper, the nickel stamper was pretreated to remove oxide on the nickel stamper surface. Then, using the solution deposition method, alkanethiol SAM as an anti-adhesion layer was deposited on nickel surface. To examine the effectiveness of the SAM deposition on the metallic nano stamper, the contact angle and the lateral friction force were measured at the actual processing temperature and pressure for the case of nano compression molding and at the actual UV dose for the case of nano UV molding. The surface energy due to SAM deposition on the nickel nano stamper markedly decreased and the high hydrophobic quality of SAM on the nickel stamper maintained under the actual molding environments.

• Korean Journal of Materials Research
• /
• v.12 no.1
• /
• pp.89-93
• /
• 2002

To investigate the effect of properties of pores in anodic alumina template(AAT) on the formation and characteristics of metal nano wires, Cu and Ni nano wires were manufactured using anodic alumina template formed in various electrolytes. The characteristics of prepared metal nano wires using AAT could be replicated from those of pores in AAT. The diameters of nano wires could be controlled by the widening process of anodic porous film in $H_3PO_4$ solution. The shape ratio of the nano wire was shown to be $170{\pm}30$ for Ni nano wire formed by AAT made in sulfuric acid.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.12a
• /
• pp.123-125
• /
• 2006

The $TiO_2$ sol was prepared hydrothermally in an autoclave from aqueous $TiOCl_2$ solutions as a starting precursor. Hollow fibers were obtained when the sol-gel-derived $TiO_2$ sol was treated chemically with a NaOH solution and subsequently heated in the autoclave under various conditions. A systematic analysis of the influence of different NaOH concentrations on the formation of nanotubes was carried out. The details of the nanotubular structure were investigated by using transmission electron microscopy (TEM), scanning electron microscopy (SEM) and X-ray diffraction (XRD). From the TEM images, the outer and the inner diameters of the tubes were measured to be about 8 and 4 nm, respectively, the lengths were measured to be several hundreds of nanometers.

• Bulletin of the Korean Chemical Society
• /
• v.31 no.8
• /
• pp.2413-2415
• /
• 2010

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.40 no.2
• /
• pp.29-36
• /
• 2008

In order to give pulp surfaces anti-bacterial functionality and photo-catalytic deodorant ability, functional pulps was made using a surface modification method with Ag nano-colloidal solution and $TiO_2$ filler. Hygiene paper was made with the specially modified pulp, and anti-bacterial and deodorant tests were carried out. The Ag nano-colloidal solution was coated on the surface of the pulp using the high pressurized gas phase squirt through the spray nozzle mounted on the hybridization system. The surface modified functional pulp was hybridized with the optimum ratio of $TiO_2$(fine particle) to pulp(core particle) under the condition of $6,000{\sim}10,000$ rpm for $3{\sim}7$ minutes in the system. The anti-bacterial functionality of the hygiene paper was confirmed by the halo test in which the formation of the clear zone around the hygiene paper sample was observed. The inhibition growth test using MIC bioscreen C showed the inhibition growth effect of the bacteria as the reaction time was increased. The photo-catalytic effect measurement of the $TiO_2$ for 4 hours of the reaction showed $50{\sim}60%$ of decomposition rate, reaching over 60% for 5 hours of the reaction.