• The Korean Journal of Ceramics
• /
• v.5 no.4
• /
• pp.375-378
• /
• 1999

In tho XRD study of $56ZrF_4 \cdot34BaF_2 \cdot4AIF_3 \cdot(6-x)LaF_3 \cdotxLnF_3$ glassdLn=Ce, Nd, Gd, Th), halo pattern charactarktic fo an amorphous sample appeared. When the halo peak angle ($\theta_p$) was converted into a wavenumber with $Qp=4\pi sinG\pi/\lambda(\lambda$ is the wavolongth of the radialion used), it was found that the Qp values varied almost liuearly with the concentration 01 $LnF_3$. The emissiou spect1.a of $Ce^{3-}$-containing fluoride glasses nnder 273 nm excitation had a peak maximum at ea. 300 nm $(Ce^{3+}$ 5d-4f- transition). The maximal intensity of the fluorescence was observed when the $CeF_3$, content was extremely low (ca. 1 mol%j. DTA measurement revealed tbat these fluoride glasses had two crystallization temperatures. In $56ZrF_4. 34BaF_2. 4NF_3. (6-x)LaF_3 .xNdF_3$ glasses, the actmation energies of crystallization obtained from a Kssinger plot were 1.7 and 5.0 eV for the glass with x=2, and 1.9 and 5.6 eV for the glass with x=4.

• Korean Journal of Materials Research
• /
• v.32 no.12
• /
• pp.560-564
• /
• 2022

In this study, lanthanum boron silicate glasses were prepared with a composition of x Li₂O-(60-x)B₂O₃-5CaO-5BaO-7ZnO-10SiO₂-10La₂O₃-3Y₂O₃ where x = 1,3,5,7, and 9 mol%. Each composition was melted in a platinum crucible under atmospheric conditions at 1,400 ℃ for 2 h. Clear glasses with a transmittance exceeding 85 % were fabricated. Their optical, thermal, and physical properties, such as refractive index, Abbe number, density, glass transition (T_g) and Knoop hardness were studied. The results demonstrated that refractive index was between 1.6859 and 1.6953 at 589.3 nm. The Abbe number was calculated using an equation for 589.3 nm (nd), 656.3 nm (nf) and 486.1 nm (nc) and was observed to be in the range from 57.5 to 62.6. As the Li₂O content increased, the glass transition temperature of the optical glass decreased from 608 ℃ to 564 ℃. If glass mold pressing is performed using a material with a low transition temperature and high mechanical strength, then the optical glasses developed in this study can be completely commercialized.