• Proceedings of the KIEE Conference
• /
• 2006.07c
• /
• pp.1418-1419
• /
• 2006

PZT(80/20) powder was prepared by a sol-gel method and PZT thick films were fabricated by the screen-printing method on the alumina substrates. The coating and drying procedure was repeated 4 times. And then the PZT(20/80) precursor solution was spin-coated on the multilayered thick films. A concentration of a coating solution was 0.5 mol/L and the number of coating was repeated from 0 to 6. The porosity of the thick films was decreased with increasing the number of coatings and the PZT thick films with 6-times coated showed the dense microstructure and thickness of about 60-65 ${\mu}m$. All PZT thick films showed the typical XRD patterns of a typical perovskite polycrystalline structure. The relative dielectric constant and the dielectric loss of the PZT-6 thick film were 275 and 3.5, respectively. And the PZT-6 film shows the remanent polarization of 22.1 $C/cm^2$ and coercive field of 13.7 kV/cm.