• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.152-153
• /
• 2006

We demonstrate the methodology of engineering the multi-component ceramic nanopowder with precise morphology by nanoblast calcinations decomposition of preliminary engineered nanoreactors. Multiple explosions of just melted $C_3H_6N_6O_6$ embedded into preliminary engineered nanoreactors break apart the agglomerates due to the highly energetic impacts of the blast waves. Also, the solid-solubility of one component into the other is enhanced by the extremely high local temperature generated during each nano-explosion in surrounding area. This methodology was applied for production of agglomeratefree nano-aggregates of $Gd_{20}Ce_{80}O_{1.95}$ with an average size of 42 nm and $LaSrGaMgO_{3-x}$ nanopowder with an average aggregate size of 83 nm.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.440-441
• /
• 2006

Several titanate powders ($Al_2TiO_5,\;SrTiO_3$, etc.) were synthesized by an ethylene glycol solution route. Titanium isopropoxide and nitrate salts were dissolved in stoichiometric proportions in liquid-type ethylene glycol without any precipitation. The parent precursor sols were dried to porous gels, and then the gels were calcined and crystallized. All synthesized titanate powders had stable crystallization behavior at low temperature and high specific surface area after a simple ball-milling process. A three-component PZT $(Pb(Zr_{0.52}{\cdot}Ti_{0.48})O_3)$ powder was also synthesized successfully by the ethylene glycol method. In this study, the characteristics of the multi-component titanate powders by the ethylene glycol method are examined.

• 한국표면공학회지
• /
• 제40권4호
• /
• pp.175-179
• /
• 2007

An Fe-Ni-Co based superalloy Incoloy 909 (Incoloy 909) has been used for gas turbine engine component material. This alloy is susceptible to high temperature oxidation and corrosion because of the absence of corrosion resistant Cr. For the improvement of durability of the component of Incoloy 909 aluminizing-chromate coating by pack cementation process has been investigated at relatively low temperature of about $550^{\circ}C$ to protect the surface microstructure and properties of Incoloy 909 substrate. As a previous study to aluminizing-chromate coating by pack cementation of Incoloy 909, the optimal aluminizing process has been investigated. The size effects of source Al powder and inert filler $Al_O_3$ powder and activator selection have been studied. And the dependence of coating growth rate on aluminizing temperature and time has also been studied. The optimal aluminizing process for the coating growth rate is that the mixing ratio of source Al powder, activator $NH_4Cl$ and filler $Al_O_3$ are 80%, 1% and 19% respectively at aluminizing temperature $552^{\circ}C$ and time 20 hours.

• 광물과 암석
• /
• 제36권3호
• /
• pp.213-220
• /
• 2023

본 연구에서는 고압 환경에서 합성된 결정 입자의 크기에 원시료(starting materials)의 상(phase)이 미치는 영향을 확인했다. 상이 다른 두 가지 원시료인 비정질 시료와 나노파우더 시료를 이용해 알루미늄이 부화된 고압의 환원환경에서 삼원계 시스템인 브리지마나이트-페리클레이스-칼슘 페라이트(calcium ferrite)상의 MgAl₂O₄을 합성했다. 시료는 40 GPa 2000 K의 압력온도 조건에서 20 시간 동안 가열하여 합성했다. 합성된 시료는 비정질 시료를 이용한 경우 입자 크기가 50-200 nm였으며, 나노파우더를 이용한 경우 ~500 nm로 나타났다. 이러한 차이는 1) 시료가 합성된 2000 K의 온도가 낮아 비정질 시료의 경우 결정 성장보다 결정핵 성장이 더 우세하게 나타났거나 2) 시료에 존재할 수 있는 산화 환원반응 상태의 차이로 생각된다. 추후 다원계 시스템에 대한 고압 실험을 수행할 때 비정질 시료보다 나노파우더를 원시료로 이용하는 것이 결정 성장에서 더 유리할 것으로 생각된다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2012년도 제43회 하계 정기 학술대회 초록집
• /
• pp.415-415
• /
• 2012

ICP (RF) 열 플라즈마 분말 합성법은 초고온 열플라즈마(~10,000 K) 속으로 원료물질을 투입한 뒤, 용융, 기화 및 재합성의 과정을 거쳐 초미분(<1 ${\mu}s$)을 합성하는 방법으로 고출력 시스템의 경우 고온/고 엔탈피 열 유동을 통한 고융점 및 저융점 복합물질의 동시 기화에 의한 물질 조성이 제어된 나노 복합체의 대량 합성이 가능할 것으로 기대되고 있다. 본 연구에서는 전북대학교 고온플라즈마 응용연구센터의 60&200 kW의 고출력 ICP (RF) 열 플라즈마 시스템을 이용하여 LTO (Lithium Titanium Oxide)와 IZTO (Indium Zinc Tin Oxide), Barium Borosilicate Glass (K2O-BaO-B2O3-SiO2)의 다성분계 나노 복합체를 합성하였으며, FE-SEM, TEM, XRD, ICP-OES를 이용하여 그 특성을 분석하였다.