• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2008년도 추계학술대회 초록집
• /
• pp.55-55
• /
• 2008

반사방지막은 태양전지 셀 제작에 적용되고 있으며, 효율을 향상시키기 위하여 $SiO_2$, $TiO_2$를 이용한 Multi-layer 반사방지막을 적용하였다. Multi-layer의 효과가 기존의 SiN 반사방지막에 비하여 광수집의 향상에 영향을 주었음을 알 수 있었다.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2004년도 Asia Display / IMID 04
• /
• pp.450-452
• /
• 2004

This paper analyzes some important achievements in Ergonomics field in CRT industry. After introducing principal regulatory requirements for CRTs, including ISO 9241 and TCO standards, the paper indicates some theoretical research in ergonomics of the display devices, such as new contrast parameter for appraising the display devices and effects of environment on visual performance at the ergonomic. Then, as the pivot of this paper, some practical progress, in the ergonomics field in CRT manufacturing , are described, such as vacuum sputtering process for advanced CRTs, new developed wet process for getting the multi-coating layers on surface of the panel.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2013년도 춘계학술대회 논문집
• /
• pp.106-106
• /
• 2013

C/C Composite는 비교적 낮은 온도에서 산화되어 고유의 특성을 쉽게 잃어버리게 된다. 본 연구에서는 Plasma Spray 코팅방법을 사용하여 다층 코팅층을 형성 시킨 후 $1600^{\circ}C$의 온도에서 열충격 저항성을 평가하였다.

• 한국표면공학회지
• /
• 제48권4호
• /
• pp.169-173
• /
• 2015

$CuInSe_2$ thin films which have been widely used for thin solar cells as a light absorber were prepared by hydrazine solution processing, and their microstructural properties were investigated. Hydrazine $CuInSe_2$ precursor solutions were prepared by dissolving $Cu_2S$, S, $In_2Se_3$ and Se powder in hydrazine solvent. Multilayer $CuInSe_2$ chalcopyrite phase thin films were prepared by repeating spin-coating process using the precursor solution. Unfortunately, the presence of the interfaces between each $CuInSe_2$ layer formed by multi-layer coating impeded grain growth across the interface. Here, by doing simple interface engineering to solve the limited grain growth issue, the large grained (${\sim}1{\mu}m$) $CuInSe_2$ thin films were obtained.

• 한국표면공학회지
• /
• 제52권6호
• /
• pp.321-325
• /
• 2019

Triso-type coating layers of silicon carbide and graphite on UO₂ paticulate nuclear fuel were prepared by using fluidized bed type chemical vapor deposition and self-propagating high temperature synthesis methods to make a coated nuclear fuel of a power plant for hydrogen mass-production. The source and carrier gases were the mixture of methyltrichlorosilane and propane, and inert argon. Chemical analysis and microstructure observation showed that the coated layers were inner graphite, middle silicon carbide and outer graphite. The elastic modulus and nano-hardness of the silicon carbide layer were 503 [GPa] and 36 [GPa], respectively.

• 한국표면공학회지
• /
• 제45권4호
• /
• pp.162-167
• /
• 2012

Ni-P/C multi-layer was synthesized by electroless plating and paste coating for better corrosion and surface conductance as a metallic bipolar plate. The Ni-P layer could be synthesized with the range of 2.6~22.4 at.% P contents and it's surface morphology and corrosion resistance depend on content of P. Corrosion resistance of the Ni-P layer in sulfuric acid by electrochemical test is similar with pure Ni. Surface resistance of pure Ni after corrosion was increased about 8% compared to pure Ni. On the other hand, that of the Ni-P/C composite with 20% carbon content was increased only 1%.

• 한국분말재료학회지
• /
• 제24권1호
• /
• pp.46-52
• /
• 2017

Fecralloy coating layer with large surface area is suitable for use as a filter media for efficient removal of hot gaseous pollutants exhausted from combustion processes. For uniform preparation of a Fecralloy coating layer with large surface area and strong adhesion to substrate, electrospray coating and thermal treatment processes are experimentally optimized in this study. A nano-colloidal solution with 0.05 wt% Fecralloy nanoparticles is successfully prepared. Optimized electrospraying conditions are experimentally discovered to prepare a uniform coating layer of Fecralloy nano-colloidal solution on a substrate. Drying the electrospray coated Fecralloy nano-colloidal solution layer at $120^{\circ}C$ and subsequent heating at $600^{\circ}C$ are the best post-treatment for enhancing the adhesion force and surface roughness of the Fecralloy coating layer on a substrate. An electrospray coating system, consisting of several multi-groove nozzles, is also experimentally confirmed as a reasonable device for uniform coating of Fecralloy nano-colloid on a large area substrate.

• 한국해양공학회지
• /
• 제32권6호
• /
• pp.502-510
• /
• 2018

In order to accumulate data to lower the friction coefficient of a press mold, tribological tests were performed before and after coating SM45C with a PVC/PO film and plasma coating (CrN, concept). The ultrasonic nanocrystal surface modification (UNSM)-treated material had a nano-size surface texture, high surface hardness, and large and deep compressive residual stress formation. Even when the load was doubled, the small amount of abrasion, small weight of the abrasion, and width and depth of the abrasion did not increase as much as those of untreated materials. A comparison of the weight change before and after the tribological test with the CrN and the concept coating material and that of the untreated material showed that the wear loss of the concept coating material and P-UNSM treated material (that is, the UNSM treated material treated with the concept coating) showed a tendency to decrease by approximately 55-75%. Concept 100N had a lower friction coefficient of about 0.6, and P-UNSM-30-100N showed almost the same curve as concept 100N and had a low coefficient of friction of about 0.6. The concept multilayer coating had a thickness of $5.32{\mu}m$. In the beginning, the coefficient of friction decreased because of the plasma coating, but it started to increase from about 250-300 s. After about 350 s, the coefficient of friction tended to approach the friction coefficient of the SM45C base metal. The SGV-280F film-attached test specimen was slightly pushed back and forth, but the SM45C base material was not exposed due to abrasion. The friction coefficient was 0.22, which was the lowest, and the tribological property was the best in this study.

• Composites Research
• /
• 제24권1호
• /
• pp.45-50
• /
• 2011

자체-감지능 있는 다기능성 나노복합소재를 위해, 투명하고 전도성 있는 카본나노튜브 (CNT)로 코팅된 폴리에틸렌 테레프탈레이트(PET)를 함침 방법으로 제조하였다. CNT 코팅의 전기적 광학적 특정의 변화는 함침 횟수와 CNT용액의 농도에 주로 의존하였다. 결과적으로, CNT 코팅의 표면저항과 투과도는 제조공정의 변수들에 따라 예민하게 조절되었다. CNT 코팅의 표면저항은 4점법과 이중 배열법에 의해 측정되었으며, 광학적 투과도는 UV 스펙트럼을 사용하여 평가하였다. CNT 코팅의 표면특성을 측정한 정적 및 동적 접촉각은 상호 일치함을 보여주었다. 함침 코팅수가 증가함에 따라, CNT코팅한 PET의 표면저항은 현저하게 저하했으나, 투명도는 CNT 네트워크의 특성으로 거의 감소하지 않았다. CNT와 인듐틴옥사이드 (ITO)의 계면 및 전기적 특성들은 피로 시험을 통하여 비교하였다. CNT는 2000회 반복 후에도 표면저항의 변화가 없는 반면에, ITO는 1000회 반복까지 표면저항의 급격한 증가를 보여주었다가 안정화하였다. 이는 형상비가 큰 CNT는 전기 접촉점을 계속 유지하는 반면에, 취성이 있는 ITO는 미세 균열이 발생하여 전지 접촉점을 많이 상실하기 때문이다.

• Tribology and Lubricants
• /
• 제28권6호
• /
• pp.283-288
• /
• 2012

In this study, a new sliding contact problem involving an elastomeric seal, a spherical particle and a hard coated steel counterface was modeled to investigate the detailed wear mechanisms related to the sealing surface. The model was also used to design the optimum coating conditions. A three-dimensional finite element contact problem was modeled and analyzed using the nonlinear finite element code, MARC. The deformed steel surface and stress distributions are presented for different coating layers and thicknesses. When the coating thickness is relatively small, the entrapped particle produces surface plastic deformations such as groove and torus. In addition, the sealing surface can be damaged by abrasive wear as well as fatigue wear. For a relatively thick and multi-layered coating, on the other hand, surface plastic deformation does not occur, and the amount of abrasive and fatigue wear is reduced. Therefore, the proposed contact model and results can be used in the design of various sealing systems, further intensive studies are required.