• 한국재료학회지
• /
• 제14권5호
• /
• pp.368-373
• /
• 2004

To improve the conventional cathode-supported tubular solid oxide fuel cell (SOFC) from the viewpoint of low cell power density, expensive fabrication process and high operation temperature, the anode-supported tubular solid oxide fuel cell was investigated. The anode tube of Ni-8mol% $Y_2$O$_3$-stabilized $ZrO_2$ (8YSZ) was manufactured by extrusion process, and, the electrolyte of 8YSZ and the multi-layered cathode of $LaSrMnO_3$(LSM)ILSM-YSZ composite/$LaSrCoFeO_3$ were coated on the surface of the anode tube by slurry dip coating process, subsequently. Their cell performances were examined under gases of humidified hydrogen with 3% water and air. In the thermal cycle condition of heating and cooling rates with $3.33^{\circ}C$/min, the anode-supported tubular cell showed an excellent resistance as compared with the electrolyte-supported planar cell. The optimum hydrogen flow rate was evaluated and the air preheating increased the cell performance due to the increased gas temperature inside the cell. In long-term stability test, the single cell indicated a stable performance of 300 mA/$\textrm{cm}^2$ at 0.85 V for 255 hr.

• 한국세라믹학회지
• /
• 제37권1호
• /
• pp.96-101
• /
• 2000

Comparative studies on microstructure, and mechanical and anti-oxidation properties between TiN and Ti-Si-N films were performed. The Ti-Si-N films were deposited on high-speed steel and silicon wafer substrates by plasma-assisted chemcial vapor deposition(PACVD) technique. The Si addition to TiN film caused to change the microstructure such as grain size refinement, randomly multi-oriented microstructure, and nano-sized codeposition of silicon nitride in the TiN matrix. The Ti-Si-N film, contains Si content of ∼7 at.%, showed the micro-hardness value of ∼3400 HK, which was higher than the pure TiN film whose hardness was ∼1500HK. The Ti-Si(7 at.%)-N film also showed much improved anti-oxidation properties compared with those of the pure TiN film. These properties were also related to the microstructure of Ti-Si(7 at.%)-N film was formed and retarded further oxidation of the nitridelayer. These properties were also related to the microstructure of Ti-Si(7 at.%)-N film which was characterized by nano-sized precipitates of silicon nitride phase in the TiN matrix and randomly oriented grains.

• 한국군사과학기술학회지
• /
• 제15권4호
• /
• pp.502-506
• /
• 2012

In order to find the structural characteristics of the thin films of group II-VI semiconductor compounds compared with those of powder materials, films were made of 4 powders of ZnS, CdS, CdSe, and CdTe(Aldrich), each with 99.99 % purity. For the ZnS/CdS multi-layers, the ZnS layer was coated over the CdS layer on an $AlO_x$ membrane, which served as a protective layer within a vacuum at the average speed of 1 ${\AA}$/sec. After studying the structures of the group II-VI semiconductor thin films by using X-ray spectroscopy, we found that the ZnS, ZnS/CdS, CdS, and CdSe films were hexagonal and exhibited some degree of preferred orientation. Also, the particles of the thin films of II-VI semiconductor compounds proved to be more homogeneous in size compared to those of the powder materials. These results were further verified through scanning electron microscopy(SEM), EDX analysis, and powder and thin film X-ray diffraction.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2007년도 제38회 하계학술대회
• /
• pp.1900-1901
• /
• 2007

한의학에서 혀는 인체 내 생리, 병리적 변화를 반영하여 진단에 있어 중요한 지표자료로 사용하고 있다. 하지만 설진은 진단환경에 의한 영향을 많이 받게 되어 객관적이고 정량화된 결과를 얻기 힘들며, 그로 인해 한의사의 진단에 대한 신뢰성도 낮아 널리 활용되지 못하고 있다. 이를 해결하기 위해 본 연구에서는 제한된 측정환경을 제공하는 디지털 설진 시스템을 통해 한의사로부터 황태라 진단받은 48명과 백태라 진단받은 14명의 설 영상을 획득하고, 설태의 컬러벡터값을 구하여 백태와 황태를 구분하는데 유의한 변수를 도출하였으며, 이를 이용하여 한의사의 설태 진단과 일치율이 높은 판별함수를 도출하였다. 이와같은 연구방법은 백태, 황태 뿐 아니라 회태나 흑태 또는 후태나 박태를 구분하는 데에도 유용하게 쓰일 수 있을 것이며 앞으로 한의사의 설진과정을 객관화, 과학화하는 과정에 기여할 수 있을 것이다.

• 한국초전도ㆍ저온공학회논문지
• /
• 제21권1호
• /
• pp.1-5
• /
• 2019

The pulsed field magnetization of the short-circuited soldered double pancake coil made of stabilized commercial high-Tc superconductor (HTS) tape is experimentally studied. The evolution of the shielding current induced by the pulsed field and the trapped field after the pulsed magnetization was measured at 77 K. It is shown that the trapped field in the coil is close to the value reached in the field cooling process and reduces weakly at 5-fold increasing of pulsed field amplitude. The current relaxation at t~2 ms after the pulse is defined by the current sharing between the tape's copper coating and the $YBa_2Cu_3O_{7-d}$ layer. In the intermediate time scale (1 s < t < 100 s) the flux creep in HTS layer dominates. At t > 100 s the current's relaxation is defined by the resistance of soldered joint between tapes.

• Current Applied Physics
• /
• 제18권11호
• /
• pp.1388-1392
• /
• 2018

Metal thin films are used widely to solve the vibration problem. However, damping mechanism is still not clear, which limits the further improvement of the damping properties for film and the development of multi-functional damping coating. In this paper, Damping microscopic mechanism of porous metal films was investigated at both macroscopically and microscopically mixed levels. Molecular dynamics simulation method was used to model and simulate the loading-unloading numerical experiment on the micro-pore and vacancy model to get the stress-strain curve and the microstructure diagram of different defects. And damping factor was calculated by the stress-strain curve. The results show that dislocations and new vacancies appear in the micro-pores when metal film is stretched. The energetic consumption from the motion of dislocation is the main reason for the damping properties of materials. Micro-mechanism of damping properties is discussed with the results of in-situ experiment.

• 폴리머
• /
• 제32권4호
• /
• pp.322-327
• /
• 2008

본 연구에서 제조한 다중층 펠렛은 수팽윤성 고분자를 포함하는 시드층, 모델 약물인 독사조신을 함유한 약물층, 약물의 방출을 제어하는 다공성막 그리고 지질층으로 구성되어 있으며, 유동층 코팅 방법을 이용하여 제조하였다. 펠렛을 구성하는 각각의 층에 다양한 특성을 가지는 고분자들의 블렌딩에 따른 독사조신의 약물방출 거동을 확인하기 위하여 히드록시프로필메틸셀룰로오스(HPMC)와 에틸셀룰로오스(EC)의 양을 달리하여 약물층을 제조하였고, 셀룰로오스 아세테이트(CA)와 $Eudragit^{(R)}$ RS의 비율을 달리하여 다공성막을 제조하였다. 그리고 지질층에 의한 방출 거동을 확인하고자 피마자유의 두께를 다르게 하여 펠렛을 제조한 결과, 대략 $1500{\mu}m$의 균일한 크기를 가지는 구형의 펠렛을 얻었다. 수용액에서 용출시험을 통하여 시간에 따른 약물방출량을 확인한 결과, 약물층에 첨가된 고분자 중, EC의 비율과 다공성막에서 CA의 비율이 증가하고, 피마자유층의 두께가 두꺼워지면 약물의 방출이 감소함을 알 수 있었다. 그리고 약물방출을 제어하는데 가장 큰 역할을 하는 다공성막의 다공형성거동 역시 SEM을 통해 확인하였다.

• 한국결정성장학회지
• /
• 제11권2호
• /
• pp.49-55
• /
• 2001

sol-gel방법에 의해서 p-형 Si(100)웨이퍼와 ITO glass, quartz glass기판 위 ZnO박막을 형성시켰으며 출발 물질은 zinc acetate dihydrate를 사용하였다. Zinc acetate dihydrate를 2-methoxyethanol-monoethanolamine(MEA)용액에 녹여 :균질하고 안정된 용액을 만들었다. ZnO박막은 2800rpm에서 25초 동안 spin-coating하고 $250^{\circ}C$의 hot plate에서 10분 동안 중간 열처리한 후 이를 반복하여 형성시켰고 결정화를 위한 열처리는 $400^{\circ}C$~$800^{\circ}C$공기 분위기에서 1시간 동안 시행하였다. X-ray diffraction(XRD), scanning electron microscopy(SEM), UV-vis 투과 스펙트럼, IR 투과 스펙트럼, photoluminescence(PL)스펙트럼 등의 측정 결과로부터 박막의 구조적 특성과 광학적 성질에 대해서 논의하였다. 제조된 ZnO막은 (002)면으로 정렬되어 있으며 380nm파장에서 예리한 흡수단이 있고 가시광선 영역에서 투명(투과율 70% 이상)하였는데 이 흡수단은 ZnO의 밴드 갭(3.2eV)과 잘 일치한다. 저온에서의 띠끝 PL스펙트럼은 속박된 엑시톤 복합체와 포논 복제에 의한 다중선 구조를 보인다.

• 한국산학기술학회논문지
• /
• 제17권12호
• /
• pp.482-487
• /
• 2016

파장 400 nm 이하의 자외선은 눈 건강에 매우 해롭다. 특히 UVA (315 nm ~ 400 nm)는 백내장, 설안염, 초자체경화 등을 유발할 수 있고, UVB (280 nm ~ 315 nm)는 결막염, 각막염 및 설안염 등을 일으킬 수 있다. 따라서 폴리머 안경렌즈를 사용함에 있어서 자외선의 차단 기능과 가시광선 영역에서 투과되는 빛을 증가시키고, 안경렌즈 표면에서 형성되는 허상을 방지하는 반사방지 기능은 매우 중요하다. 본 연구에서는 m-자일릴렌 디이소시아네이트 모노머와 2,3-Bis-1-propanethiol 모노머 및 벤조트리아졸 UV 흡수제 (SEESORB 709), 안료 혼합물, 이염화 이부틸 주석 촉매제, 알킬인산 에스터 이형제 등의 혼합물을 인젝션 몰드 방법으로 열중합 공정을 적용하여, 굴절률 1.67의 고굴절률 폴리머 안경렌즈를 제조하였다. 폴리머 안경렌즈 표면에서의 반사를 줄이기 위하여 렌즈 양면에 다층박막 반사방지 코팅을 E-beam 증착 시스템으로 코팅하였다. 자외선 차단 폴리머 안경렌즈의 광학적 특성을 UV-visible spectrometer로 분석하였고, 반사방지층을 구성하는 박막의 굴절률, 표면거칠기 등과 같은 박막소재 특성을 각각 Ellipsometry 및 원자힘 현미경으로 분석하였다. 분석 결과 제조된 안경렌즈는 395 nm 파장 이하의 자외선을 99% 이상 완벽하게 차단하였다.

• 한국재료학회지
• /
• 제5권7호
• /
• pp.835-841
• /
• 1995

Si$_3$N$_4$가 추진기관 연소조건 하에서 흑연의 산화와 마모를 효과적으로 방지하는 다층 코팅재료로 쓰일 수 있도록 하기 위하여 저압화학기상증착법(LPCVD)으로 Si$_3$N$_4$를 코팅할 때의 증착특성에 대해 연구하였다. 흑연 위에 pack cementation방법으로 SiC를 코팅하고 그 위에 저압화학기상증착법으로 Si$_3$N$_4$를 코팅 하였으며, 증착온도와 반응기체입력비를 변화시키면서 이에 따른 증착속도와 표면형상의 변화를 관찰하였다. 증착속도는 증착온도가 높아짐에 따라 처음에는 증가하다가 최대값을 나타낸 후 감소하는 경향을 나타냈으며, 그레인의 크기는 증착온도가 높아짐에 따라 작아지는 경향을 보였다. 한편, 반응기체의 입력비가 20$\leq$NH$_3$/SiH$_4$$\leq$40인 조건에서는 증착속도의 변화나 표면형상의 변화를 관찰할 수 없었다. 증착온도 800~130$0^{\circ}C$ 범위에서 증착된 Si$_3$N$_4$가 비정질상인 것을 XRD로 확인할 수 있었으며 130$0^{\circ}C$, 질소 분위기에서 2시간 동안 열처리하여 결정상인 Si$_3$N$_4$를 인을 수 있었다.