• Korean Journal of Materials Research
• /
• v.17 no.3
• /
• pp.147-151
• /
• 2007

Cu-free multi-component sol, of which final oxide composition becomes $Bi_{1.9}Pb{0.35}SrCaO,\;Bi_{1.8}Pb_{0.2}SrCaO\;and\;Bi_{1.5}SrCaO$, respectively, was prepared through sol-gel route and coated on a bare Cu substrate. Starting materials were metal-alkoxides as follows.; [$Bi(OC_{2}H_{5})_{3}\;Pb(O^{1}C_{3}H_{7})_{2},\;Sr(O^{i}C_{3}H_{7})_{2},\;Ca(OC_{2}H_{5})_{2}$] as a reagent grade. Transparent light yellowish sol was obtained in the case of $Bi_{1.9}Pb_{0.35}SrCaO\;and\;Bi_{1.8}Pb_{0.2}SrCaO$ composition and $Bi_{1.5}SrCaO$ composition's sol was light greenish. Each sol was repeatedly dip-coated on Cu substrate four times and pre-heated at $400^{\circ}C$ and finally heat-treated in the range of $740{\sim}900^{\circ}C$. In the results, crystalline phases confirmed by XRD were (2201) orthorhombic and monoclinic phases. However, only $Bi_{1.9}Pb_{0.35}SrCaO_{x}$ composition showed pseudo-superconductive behavior after heat-treatment at $900^{\circ}C$ for 12 seconds and then onset temperature was 77 K, even though it did not exhibit zero resistance below Tc.

• Macromolecular Research
• /
• v.10 no.5
• /
• pp.253-258
• /
• 2002

The multi-wall carbon nanotubes (MWNTs) with graphite crystal structure were synthesized by the catalytic decomposition of a ferrocene-xylene mixture in a quartz tube reactor to use as the conductive filler in the binary polymer matrix composed of poly(vinylidene fluoride) (PVdF) and poly(vinyl pyrrolidone) (PVP) for the EMI (electromagnetic interference) shielding applications. The yield of MWNTS was significantly dependent on the reaction temperature and the mole ratio of ferrocene to xylene, approaching to the maximum at 800 $^{\circ}C$ and 0.065 mole ratio. The electrical conductivity of the MWNTs-filled PVdF/PVP composite proportionally depended on the mass ratio of MWNTs to the binary polymer matrix, enhancing significantly from 0.56 to 26.7 S/cm with the raise of the mass ratio of MWNTs from 0.1 to 0.4. Based on the higher electrical conductivity and better EMI shielding effectiveness than the carbon nanofibers (CNFs)-filled coating materials, the MWNTs-filled binary polymer matrix showed a prospective possibility to apply to the EMI shielding materials. Moreover, the good adhesive strength confirmed that the binary polymer matrix could be used for improving the plastic properties of the EMI shielding materials.

• Membrane Journal
• /
• v.23 no.2
• /
• pp.176-184
• /
• 2013

To investigate the performance of VOC separation, composite hollow fiber membrane was prepared which composed of poly (ether imide) support prepared by phase separation method and poly (dimethylsiloxane) coating active layer. The performances of the membranes for the application of recovery process in terms of their morphology, gas permeance test for $N_2$ and $O_2$ gases. Durability against benzene, toluene and xylene was also investigated. And permeation test for multi-component VOCS through the membrane with different feed concentration and stage-cut were investigated. Permeance of PEI supported membrane and the membranes coated with PDMS decreased from 45,000 GPU to 63 GPU and 49,450 to 30 GPU for $N_2$ and $O_2$, respectively. Recovery efficiency and concentration of VOCs in permeate increased with decreasing stage-cut. VOCs concentration in permeate proportionally increased with increasing feed concentration but concentration ratio and recovery efficiency showed any noticeable changes with feed concentration change.

• Journal of the Korean institute of surface engineering
• /
• v.47 no.3
• /
• pp.109-115
• /
• 2014

High power impulse magnetron sputtering (HIPIMS), also known as the technology is called peak power density in a short period, you can get high, so high ionization sputtering rate can make. Higher ionization of sputtered species to a variety of coating materials conventional in the field of improving the characteristics and self-assisted ion thin film deposition process, which contributes to a superior being. HIPIMS at the same power, but the deposition speed is slow in comparison with DC disadvantages. Since recently as a replacement for HIPIMS modulated pulse power (MPP) has been developed. This ionization rate of the sputtered species can increase the deposition rate is lowered and at the same time to overcome the problems to be reported. The differences between the MPP and the HIPIMS is a simple single pulse with a HIPIMS whereas, MPP is 3 ms in pulse length is adjustable, with the full set of multi-pulses within the pulse period and the pulse is applied can be micro advantages. In this experiment, $In_2O_3$ : $SnO_2$ composition ratio of 9 : 1 wt% target was used, Ar : $O_2$ flow rate ratio is 4.8 to 13.0% of the rate of deposition was carried out at room temperature. Ar 40 sccm and the flow rate of $O_2$ and then fixed 2 ~ 6 sccm was compared against that. The thickness of the thin film deposition is fixed at 60 nm, when the partial pressure of oxygen at 9.1%, the specific resistance value of $4.565{\times}10^{-4}{\Omega}cm$, transmittance 86.6%, mobility $32.29cm^2/Vs$ to obtain the value.

• Journal of the Semiconductor & Display Technology
• /
• v.16 no.1
• /
• pp.40-44
• /
• 2017

The effect of weak dielectric silicone dioxide($SiO_2$) embedded in polyfluorene(PFO) emitting layer of polymer-based multi structure OLED was investigated. Indium tin oxide(ITO)/poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PEDOT:PSS)/poly(9,9-di-n-octylfluorenyl-2,7-diyl)(PFO)/2,2,2"-(1,3,5-benzinetriyl)-tris(1-phenyl-1-H-benzimidazole) (TPBi)/aluminum(Al) structure OLED was fabricated by spin-coating method. Applied electric field causes some effect on $SiO_2$ in PFO layer. Thus, interaction between polymers and affected $SiO_2$ might generate electrical and luminance properties change. Experimental results, show the reduced threshold voltage of 6 V(from 23 V to 17 V). The maximum current density was rather increased from $71A/m^2$ to $610A/m^2$ and maximum brightness was also increased from $7.19cd/m^2$ to $41.03cd/m^2$, 9 and 6 times each. Additionally we obtained colour broadening result due to the increasing of blue-green band emission. Consequently we observed that electrical and luminance properties are enhanced by adding $SiO_2$ and identified the possibility of controlling the emission colour of OLED device according to colour broadening.

• Journal of Korean Society of Environmental Engineers
• /
• v.32 no.9
• /
• pp.857-861
• /
• 2010

Recently photochemical smog has become a serious urban air pollution. And VOC is the major pollutant for it. With the advance of industrialization and urbanization, MSWI fly ash and sewage sludge and melting slag were generated. It is necessary to de-toxificate ashes, because they contain many toxic constituents and probably lead to contaminate the environment. The objective of this research was to prepare multi-functional brick which is able to remove VOCs in ambient air. The bricks were made of MSWI fly ash, sewage sludge and slag. The benzene adsorption experiment by brick was acted to evaluate its adsorptivity. And also photocatalyst material was coated to enhance its adsorptivity and the endurance on the brick. According to the result, the benzene showed 74~96%. The removal efficiency was increased and the breakpoint time was lengthened by coating a brick.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1994.04c
• /
• pp.6-6
• /
• 1994

Har dmaterials such as cemented carbides with or without coated layer, cermets, ceramics and diamond or c-BN high pressure sintered compact are used for cutting tools, wear -resistant parts, rock drilling bits and/or high pressure vessels. These hardmaterials contain not only hard phase, but also second consituent as the element for forming ductile phase and/or sintering aid, and the mechanical properties of each material depend on (1) the amount of the second constituent as well as (2) the grain size of the hard phase. The hardness of each material mainly depends on these two factors. The fracture strength, however, largely depends on other microstructur a1 factors as well as the above two factors. For all hardmaterials, the fracture strength is consider ably affected by (3) the size of microstructur a1 defect which acts as the fracture source. In cemented carbides, the following factors which are generated mainly due to the addition of the second constituent are also important; (4) the variation of the carbon content in the normal phase region free from V-phase and graphite phase, (5) the precipitation of $Co_3$ during heating at about $800^{\circ}C$,(6) the domain size of binder phase, and (7) the formation of ${\beta}$-free layer or Co-rich layer near the surface of sintered compacts. For cemented carbides coated with thin hard substance, the important factors are as follows; (8) the kind of coated substance, (9) the formation of ${\eta}$-phase layer at the interface between coated layer and substrate, (10) the type of residual stress (tension or compression) in the coated layer which depends on the kind of coating method (CVD or PVD), and (11) the properties of the substrate, and (12) the combination, coherency and periodicity of multi-layers. In the lecture, the details of these factors and their effect on the strength will be explained.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.3
• /
• pp.307-315
• /
• 2016

The properties of AlTiN films by a cathodic arc deposition process have been studied. Oblique angle deposition has been applied to deposit AlTiN films. AlTiN films have been deposited on stainless steel (SUS304) and cemented carbide (WC) at a substrate temperature of $500^{\circ}C$. AlTiN films were analyzed by scanning electron microscopy, glow-discharge light spectroscopy, micro-vickers hardness, and nanoindenter. When applying a current of 50 A to the cathodic arc source, it showed that the density of macroparticle of AlTiN films was 5 lower than other deposition conditions. With the increase of the bias voltage applied to the substrate up to -150 V, the density of macroparticle was decreased. The change of the $N_2$ flow rate during coating process made no influence on the film properties. For the multi-layered films, the film prepared at oblique angle of $60^{\circ}$ showed the highest hardness of 28 GPa and $H^3/E^2$ index of 0.18. AlTiN films have been shown a good oxidation resistance up to $800^{\circ}C$.

• Journal of the Korean institute of surface engineering
• /
• v.38 no.3
• /
• pp.95-99
• /
• 2005

Quaternary Ti-Cr-Si-N coatings were synthesized onto steel substrates (SKD 11) using a hybrid method of arc ion plating (AIP) and sputtering techniques. For the Syntheses of Ti-Cr-Si-N coatings, the Ti-Cr-N coating process was performed substantially by a multi-cathodic AIP technique rising Cr and Ti targets, and Si was added by sputtering Si target during Ti-Cr-N deposition. In this work, comparative studies on microstructure and evaluation of mechanical properties between Ti-Cr-N and Ti-Cr-Si-N coatings were conducted. As the Si was incorporated into Ti-Cr-N coatings, the Ti-Cr-Si-N coatings showed largely increased hardness value of approximately 42 GPa than one of 28 GPa for Ti-Cr-N coatings. The average friction coefficient of Ti-Cr-N coatings largely decreased from 0.7 to 0.35 with increasing Si content up to 20 at. $\%$. In addition, wear behavior of Ti-Cr-N coatings against steel ball was much improved with Si addition due to the surface smoothening effect and tribe-chemical reaction.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.10a
• /
• pp.354-361
• /
• 2005

In high speed cutting process, due to the friction between the tool and workpiece, a temperature rise of contacting part is serious. It need to develop cutting tool for overcoming such a poor condition. So now, some studies, the optimization of tool shapes, the fine grains of tool material, multi-layer coating of tools are processing. If mirror finishing on the tool is processed, there is advantage of relation between chip and tool, because of less friction, and also tool's lift would be increased. As a result mirror like finishing is expected efficient enhancement of tool. Generally, it is too difficult to process by a general way for tools of complex shapes, it is required a new method to process such complex shape tools. The magnetic fluid polishing technique can polish the workpiece of complex shape, because the polishing method which polishes as compress the workpiece by the magnetism abrasives to arrange to the linear according to the line of magnetic force. In this paper, We polished the surface of the high speed cutting tool using the magnetic fluid polishing technique, to enhance the performance of the high speed cutting tool.