• Korean Chemical Engineering Research
• /
• v.60 no.1
• /
• pp.139-144
• /
• 2022

This study reports a microfluidic approach to produce monodisperse hydrogel microparticles in a simple and highly efficient manner. Specifically, we produce double emulsion drops with a thin oil shell surrounding an aqueous prepolymer solution, which is solidified via UV-induced free radical polymerization. When they are dispersed in an aqueous solution, the oil shell is dewetted due to the absence of surfactants, resulting in production of highly uniform hydrogel microparticles (C.V.=1%). Results show that production of monodisperse hydrogel microparticles with controllable size and composition can be achieved with minimal use of oil unlike water-in-oil (w/o) single emulsion-based approach. Furthermore, in-depth study of flow patterns in microfluidic device using a phase diagram exhibits a crucial relationship among relative flow rates while providing windows of readily controllable parameters for reliable manufacturing of hydrogel microparticles.

• Clean Technology
• /
• v.23 no.3
• /
• pp.270-278
• /
• 2017

This study introduces a method to easily fabricate highly monodisperse pectin hydrogel microfibers in a microfluidic device by using partial gelation. The hydrodynamic parameters between the pectin aqueous solution and the calcium ions containing oil solution are precisely controlled to form a stable elongation flow of the pectin aqueous solution, and partial gelation of the pectin aqueous solution is performed by the chelating of the calcium ions at the interface between the two phases. The partially gelled pectin aqueous solution is phase-separated from the oil solution in an aqueous calcium chloride solution outside the microfluidic device and is completely gelled to produce monodisperse pectin hydrogel microfibers. The thickness of the pectin hydrogel microfiber is controlled in a reproducible manner by controlling the volumetric flow rate of the initially injected pectin aqueous solution. The pectin hydrogel microfibers were 200 to 500 micrometers in diameter and had a coefficient of variation below 5% under all thickness conditions, indicating that the pectin hydrogel microfibers produced by partial gelation are highly monodisperse. In addition, biomaterials can be immobilized to the pectin hydrogel microfibers produced by a single process, demonstrating the possibility that our pectin hydrogel microfiber can be used as carriers for biomaterials or tissue engineering.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2007.05a
• /
• pp.121.2-121.2
• /
• 2007

• Bulletin of the Korean Chemical Society
• /
• v.32 no.11
• /
• pp.4113-4116
• /
• 2011

• Proceedings of the Korean Magnestics Society Conference
• /
• 2015.05a
• /
• pp.146-146
• /
• 2015

• Proceedings of the Korean Ceranic Society Conference
• /
• 2002.10a
• /
• pp.120.2-120
• /
• 2002

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.10a
• /
• pp.175.1-175
• /
• 2003

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.10a
• /
• pp.174.2-174
• /
• 2003

• Proceedings of the Korean Magnestics Society Conference
• /
• 2005.12a
• /
• pp.162-163
• /
• 2005

• Applied Chemistry for Engineering
• /
• v.21 no.1
• /
• pp.34-39
• /
• 2010

Methacryloxypropyltrimethoxysilane (MPTMS) was used for the surface modification of silica nanoparticles in the toluene dispersion system for 8 h (MPSN). Then, methacryloxypropyl-modified silica nanoparticles were successfully prepared by solutioun polymerization in the ethanol solution at $60^{\circ}C$ for 14 h with adding AIBN initiator. The modification of ultra-fine particles (SiOx-PAA nanospheres) was investigated via EA, XPS, FTIR, TGA, SEM and TEM. The mean diameter of the bare silica nanoparticles, MPSN and SiOx-PAA monodisperse nanoparticles was about 25, 30 and 35 nm, respectively.