• Journal of the Korean Society for Precision Engineering
• /
• v.19 no.8
• /
• pp.100-107
• /
• 2002

The extruder screw is a part for extruding material in a injection molding machine. The screw's geometrical shape can mathematically be described by a sweep surface which is constructed by sweeping a section curve composed of a few circular arcs, along a helical guide curve. In the paper we developed a dedicated CAD system which basically is parametric in a sense that the system initially takes several design parameters to construct the geometric elements including the final sweep surface of the screw as well as section & guiding curves, along with feasibility check of the input parameter values, without further user interaction. The system has been developed as a built-in module onto a commercial CAD system, which can further incorporate additional NC-out functions with ease.

• Textile Coloration and Finishing
• /
• v.31 no.4
• /
• pp.354-362
• /
• 2019

In order to apply thermoplastic composites using PETG resin to various industrial fields such as bicycle frames and industrial parts, it is necessary to verify the impact resistance, durability and mechanical properties of the manufactured composite materials. To improve the mechanical properties, durability and impact resistance of PETG resin, an amorphous resin, in this study, compound and injection molding process were carried out using various additives such as TiO2, carbon black, polyolefin elastomer, and PETG amorphous resin. The thermal and mechanical properties of the thermoplastic composites, and the Charpy impact strength. The analysis was performed to evaluate the characteristics according to the types of additives. DSC and DMA analyzes were performed for thermal properties, and tensile strength, flexural strength, and tensile strength change rate were measured using a universal testing machine to evaluate mechanical properties. Charpy impact strength test was conducted to analyze the impact characteristics, and the fracture section was analyzed after the impact strength test. In the case of POE material-added thermoplastic composites, thermal and mechanical properties tend to decrease, but workability and impact resistance tend to be superior to those of PETG materials.

• Proceedings of the KAIS Fall Conference
• /
• 2010.11b
• /
• pp.824-827
• /
• 2010

본 논문은 전동형 모터의 Rotor의 자동 성형을 위한 자동화된 주조기 개발에 대한 결과이다. 개발된 자동화된 Rotor 전용 주조기는 수평형에 비해 금형의 크기가 약 1/2정도 이므로 금형 체결력이 반감되고, 기계 구조는 매우 작아진다. 그리고 Al용탕이 사출되는 과정에서 Spool -> Runner -> Gate -> Cavity(제품)에 이르기까지의 Runner를 최소화하여 재용융을 위한 에너지의 비용 절감을 할 수가 있다. 금형 구조가 간단하므로 금형비가 저렴하여 다품종 소량생산에 매우 유리하다. 개발제품은 수직형 구조로 알루미늄 용탕의 윗면의 공기가 금형의 유로 상측에 위치하므로 공기(gas)가 먼저 배출되어 사출(주조)후 Rotor 성형부에 남아 있는 기포가 최소화된다. 그러므로 충진도가 높아진다. Rotor 코아(규소강)가 크더라도 수직형은 금형내에 삽입(Inset)하기가 쉽고 또한, 제품의 착탈 부위와 사출부위가 다르기 때문에 작업성, 안전성이 우수하고 생산성이 매우 높다. 수직형은 충진 밀도가 매우 높고 밀도가 균일하기 때문 Rotor의 회전 소음, 진동에 대한 품질이 매우 우수하다. 따라서 고효율, 고품질의 전동모터 Rotor 제품 생산에 매우 효과적인 장비라 할 수 있다.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.13 no.1
• /
• pp.48-54
• /
• 2004

This paper describes the development of automatic shape design program for spur gear. It produces automatically third-dimensional surface and solid model used in CAD/CAM system with inputting simple measurements. This program can maximize user's convenience and get surface and solid model quickly as accepting GUI(graphic user interface). Automatic shape design program for spur gear was developed by Visual LISP, a developer program. Besides, a geometrical method and a mathematical algerian are used in this program. Use frequency of a fine spur gear is on the increase recently and manufacture process of this gear is heat treatment after press processing with molding. In this press processing, the upper punch portion of a fine spur gear shape is drafted by CAM. Therefore, estimated that surface and solid model of spur gear used to CAM are needed in this research. In this research, after 2 ㎜ gear was modeled by auto shape design program, the upper punch portion of a fine spur gear was manufactured as giving third-dimensional model to CAM software and then, displayed the result as applying to press process.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.18 no.2
• /
• pp.130-136
• /
• 2009

Semi-solid casting(SSC) of magnesium alloys is increasingly being used to produce high quality components. This process is similar to the injection molding of plastics and is called thixomolding. Using this process, higher strength, thinner wall sections and tighter tolerances without porosity are obtained. The high strength and low weight characteristics of magnesium alloys render the high-precision fabrication of thin-walled components with large surface areas. They are widely used for the IT, auto and consumer electronics industries. However, warpage of the thin-walled sections degrade quality of the parts produced in the SCC process. To produce thin-walled magnesium alloy parts, the geometry of gating system on the quality of the finished products should be clearly studied. In this paper, to minimize warpage of the thin-walled sections, Taguchi method is applied to the optimal design of the gate geometry in the thixomolding process. Width, height, length and angle of the gating system are selected for the robust design parameters. Effectiveness of the robust design is verified through the CAE software.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2004.10a
• /
• pp.294-297
• /
• 2004

RTP(Rapid Thermal Pressing) is to fabricate desired pattern on polymer substrate by pressing patterned mold against the substrate heated around glass transition temperature. For a successful RTP process, the whole process including heating, molding, cooling and demolding should be conducted 'rapidly' as possible. As the RTP process is effective in replicating patterns on flat large surface without causing shape distortion after cooling, it is being widely used for fabricating various micro/bio application components, especially with channel-type microstructures on surface. This investigation finally aims to develop a RTP process machine for mass-producing micro/bio application components. As a first step for that purpose, we intended to examine the technological difficulties for realizing mass production by RTP process. Therefore, in the current paper, 4 kinds of RTP machines were examined and then the RTP process was conducted experimentally for PMMA film by using one of the machines, HEX 03. The micro-patterned molds used for RTP experiment was fabricated from silicon wafer by semi-conduct process. The replicated micro patterns on PMMA films were examined using SEM and the causes of defect observed in the replicated patterns were discussed.

• Journal of Fashion Business
• /
• v.9 no.4
• /
• pp.94-112
• /
• 2005

This study focuss on the futurism expressed in Paco Rabanne's works. Paco Rabanne, who has created experimental and prophetic avant-garde fashion by cutting edge techniques and revolutionary new materials, is known as one of the most influential fashion designer of modern times. First, Light, one of the most important element in Paco Rabanne's fashion design, shows some influence of medieval symbols of love and salvation. Second, the artistic trends which influenced on Paco Rabanne's fashion include surrealism, op art and kinetic art. His use of new materials and avant-garde style represents the influence of surrealism. His experimental use of waving plastics and glittering metal during his early period is especially related with op art and kinetic art in the early 1960's which emphasize the artistic effect of light and movement. Third, the characters of Paco Rabanne's works are the harmony of technology and the beauty oh machine by the geometrical figures like triangles, rectangles, and circles and represent and movement,and the innovational creative methods, voluptuous beauty.

• Journal of the Korean Society of Industry Convergence
• /
• v.23 no.4_1
• /
• pp.531-539
• /
• 2020

When injection mold is repeatedly used for mass production, fatigue phenomenon due to cyclic stress may occur. The surface and interior of structure might be damaged due to cyclic stress or strain. The objective of this study was to analyze failure of SCM435 high-tension bolts connecting upper and lower parts of a three-stage injection molding machine. These bolts have to undergo an accurate heat treatment to prevent the formation of chromium carbide and the action of dynamic stresses. Bolts were fractured by cyclic bending stress in the observation of ratchet marks and beach marks. Damaged specimen showed an acicular microstructure. Impurity was observed. Chromium carbide was observed near the crack origin. Both shape parameters of the Vickers hardness were similar. However, the scale parameter of the damaged specimen was about 20% smaller than that of the as-received specimen. Much degradation occurred in the damaged specimen. Bolts should undergo an accurate heat treatment to prevent the formation of chromium carbide. They must prevent the action of dynamic stresses. Bolts need accurate tightening and accuracy of heat treatment and screws need compression residual stress due to peening.

• Journal of Power System Engineering
• /
• v.20 no.5
• /
• pp.5-13
• /
• 2016

This study is on wear damage of the material for a molding machine that be used at finally cutting of metal beam made in roll forming process of vehicle bump beam process line. SKD11 steel was used with the material for cutting mold jig. In the cutting mold jig, Ti diffusion heat treatment after vacuum heat treatment was carried out for upgrade of surface hardness and anti-wear. Also, the heat treatments by various methods were performed to compare the wear damage degree against above the existing heat treatment. Wear loss and friction coefficient were obtained from wear test. And, micro Vickers hardness values were compared with damaged parts or not of cutting mold jig. Micro Vickers hardness value appeared higher at the undamaged part by Ti diffusion heat treatment. The micro Vickers hardness well followed a two-parameter Weibull probability distribution.

• Journal of the Semiconductor & Display Technology
• /
• v.18 no.3
• /
• pp.52-59
• /
• 2019

Styrene-butadiene rubber (SBR) composites, incorporated with graphene, molybdenum disulfide and their hybrid in different filling ratio, were fabricated by a two roll-mill. The dispersion states of all the samples' matrix were employed by carbon black dispersion tester. The curing properties of the pre-vulcanized rubber composites were investigated, after molding by heating press machine, the tensile strength, storage modulus, friction coefficient, the swelling property had also been tested according to ASTM. The composite G1M10 (filling with 1 phr graphene and 10 phr molybdenum) showed the best mechanical properties and viscoelastic properties in this research with a better filler dispersion state and more compact matrix structure.