• The Journal of Korean Academy of Prosthodontics
• /
• v.49 no.2
• /
• pp.114-119
• /
• 2011

The aim of this study was to investigate effect of specimen preparation method on the microtensile bond strength of veneering ceramic to zirconia core. Materials and methods: Cylindrical Lava zirconia block (3M ESPE, Seefeld, Germany) was cut into discs using a diamond disc. After sintering, the core specimens were placed in an adjustable mold and veneered with Lava ceram (3M ESPE, Seefeld, Germany). The disc shaped specimen of group 1 was cut into microbars ($1{\times}1{\times}7\;mm^3$) using a low speed diamond disc under water cooling (n = 15). The specimen of group 2 was cut into microbars ($1.2{\times}1.2{\times}7\;mm^3$) in the same way. Whereafter the microbars were trimmed ($1{\times}1{\times}7\;mm^3$) using a thick diamond disc under water cooling (n = 15). The microtensile bond strength was tested in a microtensile tester (Instron 8848, $Instron^{(R)}$ Co., Norwood, USA). Fractured microtensile specimens were analyzed under a stereomicroscope (MZ6, Leica Microsystems GmbH, Wetzlar, Germany) at magnification ${\times}30$. Results: The microtensile bond strength of group 1 ($28.8{\pm}7.0\;MPa$) was significantly higher than group 2 ($11.0{\pm}33\;MPa$) (P=.00). Conclusion: It appears advisable to avoid the trimming action, especially high strength ceramic specimens.

• Korean Journal of Materials Research
• /
• v.8 no.12
• /
• pp.1165-1169
• /
• 1998

A single crystal cast blade was manufactured by CMSX 6, one of the first generarion nickel based single crystal superalloys by the selector method in a vacuum furnace. The single crystal has been grown with cooling rate of 2.5 mm/min, after pouring the molten alloy of 163$0^{\circ}C$ to the mold heated to 150$0^{\circ}C$. The cast structure could be classified into matrix (dendrite) and eutectic regions in ${\gamma}$'shape and size. The eutectic region showed higher Ti content. As the additional results of ${\gamma}$'precipitates by EPMA and CBED analysis the ${\gamma}$'size was less than 0.5~0.7$\mu\textrm{m}$, showing the chemical composition close to Ni$_3$Al of Ll$_2$ lattice structure. But ${\gamma}$'size has increased to bigger than 1.0$\mu\textrm{m}$, being near to eutectic region, changing its shape to bar or huge block types. These showed the chemical structure near to Ni$_3$Ti of D $O_{24}$ lattice structure. Therefore, ${\gamma}$'morphology of dendrite and eutectic regions depends absolutely on its chemical composition and lattice structure.