• E2M - 전기 전자와 첨단 소재
• /
• 제10권2호
• /
• pp.141-149
• /
• 1997

L $a_{0.7}$S $r_{0.3}$Mn $O_{3}$ powders were prepared by both GNP(Glycine-Nitrate Process) and solid state reaction method in various of calcination temperature(800-1000.deg. C) and time in air. Also, L $a_{0.7}$S $r_{0.3}$Mn $O_{3}$ cathode contacts on YSZ(Yttria-Stabilized Zirconia) substrate were prepared by screen printing and sintering method as a function of sintering temperature(1100-1450.deg. C) in air. Sintering behaviors have been investigated by SEM(Scanning Electron Microscope) and porosity measurement. Compositional and structural characterization were carried out by X-ray diffractometer and ICP AES(Inductively Coupled Plasma-Atomic Emission Spectrometry) analysis. Electrical characterization was carried out by the electrical conductivity with linear 4 point probe method. As the calcination period increased in solid state reaction method, L $a_{0.7}$S $r_{0.3}$Mn $O_{3}$ phase increased. Although L $a_{0.7}$S $r_{0.3}$Mn $O_{3}$ single phase was obtained only for 48hrs at 1000.deg. C, in GNP method it was easy to get single and ultra-fine L $a_{0.7}$S $r_{0.3}$Mn $O_{3}$ powders with submicron particle size at 650.deg. C for 30min. The particle size and thickness of L $a_{0.7}$S $r_{0.3}$Mn $O_{3}$ cathode contact by solid state reaction method did not change during the heat treatment, while those by GNP method showed good sintering characteristics because initial powder size fabricated from GNP method is smaller than that fabricated from solid state reaction method. Based on enthalpy change from thermodynamic data and ICP-AES analysis, it was suggested to make cathode contact in composition of (L $a_{0.7}$S $r_{0.3}$)$_{0.91}$ Mn $O_{3}$ which have little second phase (L $a_{2}$Z $r_{2}$ $O_{7}$) for high efficient solid oxide fuel cells applications. As (L $a_{0.7}$S $r_{0.3}$)$_{0.91}$Mn $O_{3}$ cathode contact on YSZ substrate was sintering at 1250.deg. C the temperature that liquid phase sintering did not occur. It was possible to obtain proper cathode contacts with electrical conductivity of 150(S/cm) and porosity content of 30-40%.m) and porosity content of 30-40%.

• Journal of Information Display
• /
• 제2권3호
• /
• pp.13-17
• /
• 2001

The manganese-doped magnesium tin oxide with spinel structure was selected as a green phosphor for FED application and was synthesized by the solid state reaction. Its luminescence properties were investigated under low-voltage electron excitation. The $Mg_2SnO_4$:Mn phosphor showed green emission with the spectrum centered at 500 nm due to energy transfer from $^4T_1$ to $^6A_1$ of $Mn^{2+}$ ion. Optimum Mn concentration was 0.6 mole % and the decay time was shorter than 10 ms.

• 한국세라믹학회지
• /
• 제45권8호
• /
• pp.493-496
• /
• 2008

Composite electrodes consisting of $CoMnO_2$ and carbon nanofibers(vapor grown carbon nanofiber, VGCF) with high electrical conducivity($CoMnO_2$/VGCF) were prepared on a porous nickel foam substrate as a current collector and their supercapacitive properties were investigated using cyclic voltammetry in 1 M KOH aqueous solution. The $CoMnO_2$/VGCF electrode exhibited high specific capacitance value of 630 F/g at 5 mV/s and excellent capacitance retention of 95% after $10^4$ cycles, indicating that the used VGCF played the important roles in reducing the interfacial resistance in the composite electrode to improve supercapacitive performance.

• 한국결정학회지
• /
• 제15권1호
• /
• pp.44-50
• /
• 2004

Spinel structured lithium managanese oxide $(LiMn_2O_4)$ powder with well defined facetted morphology was prepared by precipitation-evaporation method. {111}, {110}, and {100} planes are mainly observed in the $LiMn_2O_4$ powder. And powder shape of tetradecahedron and octahedron was observed depending on the calcinations temperature. The observed powder morphology observed seemed to be related to the nonstoichiometry of the oxygen in the $LiMn_2O_4$ spinel structure. Oxygen nonstoichiometry might be responsible for the Jahn-teller effect and structure transition which in turn affects the surface energy of the {111}, {110}, and {100} planes. Powder shape transition from tetradecahedron to octahedron seemed to be related to the surface energy of the {111}, {110}, and {100} planes with oxygen nonstoichiometry.

• 한국표면공학회지
• /
• 제30권1호
• /
• pp.57-62
• /
• 1997

Green-emitting $ZnGa_2O_4$ : Mn phosphors were synthesized by a thermal method and their low-voltage cathodoluminescent characteristics were examined for the field emitter display (FED) application. Low efficiency of $ZnGa_2O_4$ : Mn phosphors could be ascribed to the low penetration depth of into phosphors, which might results in charge accumulation on the phosphors screen. For increasing cathodoluminescent of $ZnGa_2O_4$ : Mn under low voltage excitation, wide band-gap oxide materials were added to the $ZnGa_2O_4$: Mn powder. It is found that the luminance can be increased by 20%. Measurement of leakage current on the phosphor screen shows that the enhancement of low-voltage cathodoluminescent by additive materials is mainly due to the consumption of surface charges on the phosphor.

• 열처리공학회지
• /
• 제13권3호
• /
• pp.158-162
• /
• 2000

The high temperature oxidation behavior and the surface defect in Fe-25Mn-1.5A1-0.5C steel was investigated by XRD (X-ray Diffractin) and electron microscopy. The intra- and inter-granular oxides were formed by the selective oxidation of manganese and aluminum, which were identified to MnAl2O4 phase. Aluminum nitride (AlN) was formed in front of these oxides. The ${\gamma}$-matrix was transformed to ${\alpha}$- and ${\varepsilon}$- phases by the selective oxidation of manganese. The surface defect, micro-scab was induced by the difference of the high temperature ductility between the matrix and the inter-granular oxide.

• 한국표면공학회지
• /
• 제48권1호
• /
• pp.27-32
• /
• 2015

Advanced high strength steels undergo recrystallization annealing in reducing gas atmosphere before galvanizing to improve mechanical properties. The selective oxidations of elements such as Mn, Si, Cr and Al during annealing decrease wettability of liquid zinc, resulting in bare spots and other defects. In this work, Fe-3wt%Mn steel sheet was annealed at $780^{\circ}C$ for 1200 sec. in 5% $H_2-N_2$ atmosphere and then dipped into zinc bath held at $460^{\circ}C$, which contained 0.2wt% dissolved Al. MnO crystallines in the average size of 200 nm were formed on the surface after annealing. It is estimated that MnO has been detached into bath with the formation and growth of inhibition layer with longer immersion time during galvanizing. No evidence of aluminothermic reduction of MnO has been found in this study.

• 광물과 암석
• /
• 제34권4호
• /
• pp.241-253
• /
• 2021

유라시아 대륙 주변부 북극해의 천해에서도 태평양이나 인도양의 심해저에서와 같이 많은 망가니즈단괴가 발견되고 있지만, 이에 관한 자세한 연구는 많이 수행되고 있지 않다. 아라온호의 북극해 탐사를 통하여 동시베리아해에서 채취한 망가니즈단괴는 Mn/Fe 비가 매우 높아 Mn 자원으로서의 가능성이 매우 크다. 이번 연구에서는 북극 동시베리아해에서 산출되는 망가니즈단괴 중 약 7%를 차지하는 비구형 단괴를 외부형태에 따라 구분하고, 크기와 무게, 내부조직을 관찰하였으며, X선회절분석 그래프의 피크 면적비를 이용한 산화망가니즈광물의 반정량 분석과 지화학분석을 실시하여, 그 결과를 구형 단괴와 비교하였다. 비구형 망가니즈단괴는 외부형태에 따라 5가지로 구분되며, 타원체형, 판상형과 불규칙형이 대부분을 차지하며, 장경과 무게는 비례하는 경향이 있다. 비구형 단괴는 모두 핵을 가지며, 핵 성분은 이질 퇴적물이 주를 이룬다. 산화망 가니즈광물의 평균 함량은 버네사이트, 부서라이트, 토도로카이트 순으로 감소하며, 함량비는 외부형태, 내부조직이나 핵 성분과는 상관관계가 없지만, 단괴의 내부에서 외부로 갈수록 토도로카이트와 부서라이트는 감소하고, 버네사이트가 증가하는 경향이 있다. 북극해의 다른 천해는 물론 태평양이나 인도양의 심해저의 단괴에 비하여 Mn 함량이 많고, Mn/Fe 비가 높다. 비구형 단괴는 구형 단괴에 비하여 크기가 크고 무겁고, Mn 함량이 적고 Mn/Fe 비는 낮지만, 광물조성이나 내부조직에서는 큰 차이가 없다. 동시베리아해에서 채취된 모든 망간단괴는 Mn/Fe 비가 5 이상으로 높으므로 대부분 속성작용에 의하여 형성된 것으로 여겨진다.

• 자원리싸이클링
• /
• 제11권5호
• /
• pp.21-23
• /
• 2002

A new process based on the co-precipitation method was developed fer removing harmful impurities during Mn-Zn ferrite production such as $SiO_2$ and P from waste pickle liquor. By this process a final result of less than 100 ppm of $SiO_2$ and less than 10 ppm of P content in the ferric oxide is easily attained. Though Ca cannot be removed by this process, water rinsing of the ferric oxide is effective fer reducing Ca content to less than 100 pm. For further purification, the origins of each impurity must be investigated and then taken away.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2015년도 자성 및 자성재료 국제학술대회
• /
• pp.150-150
• /
• 2015