Methane direct cracking can be utilized to produce $CO_x$ and $NO_x$-free hydrogen for PEM fuel cells, oil refineries, ammonia and methanol production. We present the results of a systematic study of methane direct cracking using a mixed conducting oxide, Y-doped $BaZrO_3$ ($BaZr_{0.85}Y_{0.15}O_3$), membrane. In this paper, dense $BaZr_{0.85}Y_{0.15}O_3$ membrane with disk shape was successfully sintered at $1400^{\circ}C$ with a relative density of more 93% via addition of 1 wt% ZnO. The ($BaZr_{0.85}Y_{0.15}O_3$) membrane is covered with Pd as catalyst for methane decomposition with an DC magnetron sputtering method. Reaction temperature was $800^{\circ}C$ and high purity methane as reactant was employed to membrane side with 1.5 bar pressure. The $H_2$ produced by the reaction was transported through mixed conducting oxide membrane to the outer side. In addition, it was observed that the carbon, by-product, after methane direct cracking was deposited on the Pd/ZnO-$BaZr_{0.85}Y_{0.15}O_3$ membrane. The produced carbon has a shape of sphere and nanosheet, and a particle size of 80 to 100 nm.

• 한국수소및신에너지학회논문집
• /
• 제22권6호
• /
• pp.759-764
• /
• 2011

Mixed-conducting oxide powders, $BaCe_{0.9}Y_{0.1}O_{2.95}$ (BCY) and $SrCe_{0.9}Y_{0.1}O_{2.95}$ (SCY) powders have been prepared by a solid-state reaction method. Xray diffraction patterns of the prepared powders showed the sharp peaks of the $BaCe_{0.9}Y_{0.1}O_{2.95}$ and $SrCe_{0.9}Y_{0.1}O_{2.95}$ phases. The oxide powders that were prepared by attrition milling showed rather large particles and severe necking between particles in FE-SEM images as well as residual reactant ($BaCO_3$) and secondary phases ($SrCeO_3$ and $CeO_2$) in XRD patterns. The oxide powders prepared using ball milling showed particles under approximately 500 nm and typical XRD patterns of the $BaCe_{0.9}Y_{0.1}O_{2.95}$ and $SrCe_{0.9}Y_{0.1}O_{2.95}$ phases. Ceramic membranes of the $BaCe_{0.9}Y_{0.1}O_{2.95}$ and $SrCe_{0.9}Y_{0.1}O_{2.95}$ phases were fabricated by the aerosol deposition method using the oxide powders synthesized.

• 한국수소및신에너지학회논문집
• /
• 제21권2호
• /
• pp.117-122
• /
• 2010

BCY($Ba(Ce_{0.9}Y_{0.1})O_{3-\delta}$) oxide, shows high protonic conductivity at high temperatures, and are referred to as hydrogen separation membrane. For high efficiency of hydrogen separation ($H_2$ flux and selectivity) and low fabrication cost, ultimate thin and dense BCY-Ni layer have to be coated on a porous substrate such as $ZrO_2$. Aerosol depostion (AD) process is a novel technique to grow ceramic film with high density and nano-crystal structure at room-temperature, and would be applied to the fabrication process of AD integration ceramic layer effectively. XRD and SEM measurements were conducted in order to analyze the characteristics of BCY-Ni membrane fabricated by AD process.

• 에너지공학
• /
• 제19권2호
• /
• pp.73-80
• /
• 2010

고체산화물연료전지(SOFC)는 청정에너지기술로써 화학에너지를 전기에너지로 직접 전환한다. SOFC는 열병합발전과 결합하여 80%이상의 효율을 올릴 수 있으며 천연가스와 바이오가스 등 연료에 대한 융통성이 폴리머전해질막연료전지(PEMFC)보다 높다. YSZ전해질과 함께 SOFC에 주로 채용되는 공기극 재료는 아직까지 Sr이 첨가된 $LaMnO_3$(LSM)이다. LSM 이외에, 혼합전도성을 가지는 페로브스카이트로서 Sr첨가 $LaCoO_3$(LSCo), $LaFeO_3$(LSF), $LaFe_{0.8}Co_{0.2}O_3$(LSCF)는 공기극 임피던스가 LSM에 비해 현저히 낮아 연구가 증가하고 있다. 그러나 SOFC전극의 소결온도에서 YSZ과 고체반응을 일으키는 문제점과 열팽창 계수가 YSZ와 격차가 크게 나는 문제점 때문에 전극 제조가 복잡하다. 따라서 전해질과의 화학적 안정성 및 유사한 열팽창계수(TEC)를 가지면서 우수한 전기화학활성을 제공하는 것이 해결해야할 중요한 문제로 남는다.

• 전기화학회지
• /
• 제6권1호
• /
• pp.59-64
• /
• 2003

고상 반응법을 이용하여 $La_{0.7}Sr_{0.3}Ga_{0.6}Fe_{0.4}O_{3-\delta}$ 분말을 합성하고 소결하여 혼합전도성 분리막을 제조하였다. 제조된 분리막들은 페롭스카이트 단일상 결정구조를 나타내었으며, $95\%$, 이상의 상대밀도를 나타내었다. 산소이온 변환 능력을 향상시키기 위해 $La_{0.7}Sr_{0.3}Ga_{0.6}Fe_{0.4}O_{3-\delta}$의 양 표면에 $La_{0.6}Sr_{0.4}CoO_{3-\delta}$ paste를 스크린 프린팅 방법으로 코팅한 결과, 코팅되지 않은 분리막에 비해 산소투과 유속이 크게 증가하여 $950^{\circ}C,\; {\Delta}P_{o_2}=0.21 atm$에서 약 $0.5ml/min{\cdot}cm^2$의 값을 나타내었다. 이러한 산소투과 유속은 표면 코팅층이 다공성일수록, $La_{0.7}Sr_{0.3}Ga_{0.6}Fe_{0.4}O_{3-\delta}$의 결정립 크기가 증가할수록 증가하는 경향을 나타내었다. 제조된 디스크 형상의 소결체를 이용하여 $950^{\circ}C$에서 메탄부분산화반응을 행한 결과 $40\%$ 이상의 메탄전환율과 합성가스의 수율을 얻을 수 있었으며, CO의 선택도는 $100\%$를 나타내었다 또한, $950^{\circ}C$의 메탄분위기에서 600시간의 장기부분산화반응을 통해 상의 안정성을 확인하였다.