• Journal of the Korea Institute of Building Construction
• /
• v.14 no.1
• /
• pp.37-44
• /
• 2014

Recently, many efforts related to the utilization of industrial by-products have been made to reduce carbon dioxide emissions in the construction industry. Of these various efforts, concrete incorporating ground granulated blast furnace slag (BFS) provides many advantages compared to conventional concrete, such as high long-term compressive strength, improved durability and economic benefits because of its latent hydraulic property, and low compressive strength at early curing age. This paper investigates the compressive strength of high-activated ground granulated blast furnace slag blended mortar with slag by-product S type(SBP-S). The results of the experiment revealed that incorporating high-activated ground granulated blast furnace slag would affect the compressive strength of mortar. It was found that increasing the Blaine fineness and replacement ratio of slag by-product S type shows high compressive strength of mortar at early curing age because of its high $SiO_2$ and CaO contents in the slag. It is confirmed that an increase of curing age does not affect the compressive strength of mortar made with slag by-product S type at a high curing temperature. Moreover, it is possible to develop and design concrete manufactured with high-activated ground granulated blast furnace slag as binder considering the acceleration curing conditions and mix proportions.

• International Journal of Highway Engineering
• /
• v.18 no.6
• /
• pp.97-104
• /
• 2016

OBJECTIVES : The objective of this research is to develop additives for the modification of Solvent DeAsphalting Residue (SDAR) to be used as pavement materials, and evaluate the performance of asphalt mixture manufactured using the SDAR modified by developed additives. METHODS : The SDAR generally consists of more asphaltenes and less oil components compared to the conventional asphalt binder, and hence, the chemical/physical properties of SDAR are different from that of conventional asphalt binder. In this research, the additives are developed using the low molecular oil-based plasticizer to improve the properties of SDAR. First, the chemical property of two SDARs is analyzed using SARA (saturate, aromatic, resin, and asphaltene) method. The physical/rheological properties of SDARs and SDARs containing additives are also evaluated based on PG-grade method and dynamic shear-modulus master curve. Second, various laboratory tests are conducted for the asphalt mixture manufactured using the SDAR modified with additives. The laboratory tests conducted in this study include the mix design, compactibility analysis, indirect tensile test for moisture susceptibility, dynamic modulus test for rheological property, wheel-tracking test for rutting performance, and direct tension fatigue test for cracking performance. RESULTS : The PG-grade of SDARs is higher than PG 76 in high temperature grades and immeasurable in low temperature grades. The dynamic shear modulus of SDARs is much higher than that of conventional asphalt, but the modified SDARs with additives show similar modulus compared to that of conventional asphalt. The moisture susceptibility of asphalt mixture with modified SDARs is good if, the anti-stripping agent is included. The performance (dynamic modulus, rutting resistance, and fatigue resistance) of asphalt mixture with modified SDARs is comparable to that of conventional asphalt mixture when appropriate amount of additives is added. CONCLUSIONS : The saturate component of SDARs is much less than that of conventional asphalt, and hence, it is too hard and brittle to be used as pavement materials. However, the modified SDARs with developed additives show comparable or better rheological/physical properties compared to that of conventional asphalt depending on the type of SDAR and the amount of additives used.

• Journal of Distribution Science
• /
• v.14 no.2
• /
• pp.57-63
• /
• 2016

Purpose - The present study aimed to investigate the difference between entity theorists and incremental theorists in the extent of attributing efforts and traits of consumers for the realization of pursued goals. Furthermore, the present study was conducted to determine the difference depending on circumstances. In this regard, the circumstances where consumers felt pride were divided into those in which important goals and ordinary life goals were achieved. Research design, data, and methodology - An empirical study was performed, which was divided into group 1 and 2. Group 1 is the experimental group concerned with the important goal achievement, and group 2 is the control group related to daily ordinary goal achievement. 80 college students were assigned to each group, respectively. The empirical study for each of the two groups was performed respectively by means of questionnaire survey. In the experimental group, t-test was used to verify the hypotheses for the empirical study. In the circumstances of the control group, t-test was also used to examine whether the results were same as those shown from the analysis of experimental group data or not. Results - According to the group 1 and 2, the t-test of the empirical study showed that entity theorists tended to attribute the achievements of goals to their traits more than incremental theorists did, whereas the incremental theorists tended to attribute achievements of goals to their efforts more than entity theorists did in the important goals-achieved circumstance. In the circumstance of daily life goals-achieved, additional questionnaire survey and analysis were conducted, however, there was no difference between incremental and entity theorists in regard to attributing realization of goals to their efforts, and it leads to assess the difference in the meaning of invested efforts between important goal and ordinary goal achievement. Conclusions - Considering that the feeling of consumers has been regarded as one of the significant factors in marketing mix management, the results of this study are considered as significant implications for management. The implications can be said that when incremental consumers feel authentic pride in the important goals-achieved circumstance, marketers are requested to emphasize the fact that the efforts of consumers have contributed to realization of the important goals. By contrast, when consumers feel hubristic pride in both circumstances, marketers are requested to approach to entity-oriented consumers by way of trait. Authentic and hubristic pride are pervasive and engendered by important events or daily routines, and they could have effect on delaying making decisions. Therefore, it is necessary for future research to examine the unexplored difference of effect between incidental authentic and hubristic pride on consumer's self-control. In particular, future researches are related to the extent of difference in attributing efforts and traits. The consumers'realization for the previously pursued goals between entity theorists and incremental theorists affects their present or long distant decisions in self-control dilemmas. The consumers are faced with choosing one between virtuous long term- related option and vice immediate option.

• Journal of the Korea Concrete Institute
• /
• v.18 no.1 s.91
• /
• pp.57-64
• /
• 2006

The crack presented in concrete structures causes a structural defect, the durability decrease, and external damages etc. Therefore, it is necessary to improve durability through the effort to control the crack. Fluosilicic acid($H_2SiF_6$) is recovered as aqueous solution which absorbs $SiF_4$ produced from the manufacturing of industrial-graded $H_3PO_4$ or HF. Generally, fluosilicates prepared by the reaction between $H_2SiF_6$ and metal salts. Addition of fluosilicates to cement endows odd properties through unique chemical reaction with the fresh and hardened cement. Mix proportions for experiment were modulated at 0.45 of water to cement ratio and $0.0{\sim}2.0%$ of adding ratio of fluosilicate salt based inorganic compound. To evaluate correlation of concrete strength and adding ratio of fluosilicate salt based inorganic compound, the tests were performed about design strength(21, 24, 27 MPa) with 0.5% of adding ratio of fluosilicate salt based inorganic compound. Applications of fluosilicate salt based inorganic compound to reduce cracks resulted from plastic and drying shrinkage, to improve durability are presented in this paper. Durability was evaluated as neutralization, chloride ion penetration depth, freezing thawing resistant tests and weight loss according reinforcement corrosion. It is ascertained that the concrete added fluosilicate salt based inorganic compound showed m ability to reduce the total area and maximum crack width significantly as compared non-added concrete. In addition, the durability of concrete improved because of resistance to crack and watertightness by packing role of fluosilicate salt based inorganic compound obtained and pozzolanic reaction of soluble $SiO_2$ than non-added concrete.

• Journal of the Korea Concrete Institute
• /
• v.16 no.6 s.84
• /
• pp.777-783
• /
• 2004

In this study, for improving of concrete properties, those are used ground granulated blast slag(GGBS) and fly ash(FA). There are some advantage to add the GGBS and FA in plain concrete. The objective of this study is to find the characteristics of fresh and hardened antiwashout underwater concrete which is followed by blended ratio of GGBS and FA. Experimental parameters were chosen that W/C was 50%, S/a was 40% and as the blended ratio of GGBS was set at 0, 10, 20, 30, 40, 50, 60% and FA was set at 0, 10, 15, 20, 25, 30, 35% in order to prove the properties of antiwashout underwater concrete can be changed by blended ratio of GGBS md FA. It was measured pH, suspension and slump flow of fresh antiwashout underwater concrete and compressive strength of hardened antiwashout underwater concrete in age of 7 days, 28 days and 56 days. The experimental results of fresh concrete show that pH, suspension and slump flow were all satisfied with KSCE (Korea Society of Civil Engineering) standard value and mix design standard value. To synthetically consider, the optimum blended ratio is about 30% of GGBS and FA.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.4
• /
• pp.95-103
• /
• 2012

Precast concrete method is known to have advantages of minimizing works in the construction, controlling concrete quality easily and saving construction period due to only fabrication work in the construction field, but it needs to apply steam curing to accelerate early concrete strength. In the meanwhile, the oil cost for steam curing has been continuously increased because of political instability in the middle East and international economic shaky. Thus, this study addresses the development of precast/ prestressed concrete which has over 14MPa at 1 day age and specified concrete strength of 40MPa at low temperature, not applying steam curing. Tests were carried out in terms of material characteristics in fresh concrete and compressive strength using 3 types of cement such as Type I, Type III and rapid hardening compound cement. As results of tests, it is found that cements for rapid hardening had disadvantages with respect to slump, slump loss, and air content, but showed higher compressive strength than specified one, especially the highest value when using rapid hardening compound.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.4 no.3
• /
• pp.250-258
• /
• 2016

Until now, the construction material industry has been recognized as a typical environmental destruction industry. However, recently, in order to reduce $CO_2$ emission, the main cause of environmental problems, lots of studies have been done about recycling industrial by-products and construction wastes. Therefore, the purpose of this study is to confirm whether it is possible to use as an alternative material in cement production process as a part of the development of recycled cement using an inorganic construction waste. For this study, the inorganic construction wastes was collected and analyzed each chemical component by XRF(X-ray Fluorescene). Also, the inorganic construction wastes were combined based on the chemical component of the cement, to perform this analysis. As a result, when the inorganic construction wastes was properly combined, it is possible to consider the development of the recycled cement used the inorganic construction wastes.

• Tunnel and Underground Space
• /
• v.17 no.4
• /
• pp.266-284
• /
• 2007

Recently, many efforts have been made to construct the first unlined tunnel, without in-situ concrete lining, in Korea. However, the lack of reliability in the performance of shotcrete as permanent tunnel support prevented from its realization. Shotcrete has been regarded to have significant problems in field application and long term performance because of unsatisfactory strength level and durability compared to those of European countries. In this study, the high strength shotcrete satisfying compressive strength over 40 MPa and flexural strength over 4.5 MPa was developed from optimized mix design. The type of accelerators and the amount of silica fume were selected as the main factors in mixing process and the analyses were carried out up to the elapsed time of 2 years. In order to evaluate the short term durability of shotcrete, an array of laboratory test consisting of freeze-thaw, carbonation chloride penetration and permeability test was performed. For long-term durability tests, specimens have been put in an operated highway tunnel to expose them to the similar environment when they are actually used as an unlined tunnel support. From the strength and durability tests, it was found that only alkali-free based accelerator satisfied the target strength of this study and also, the developed shotcrete showed very high performance in its durability.

• Asian-Australasian Journal of Animal Sciences
• /
• v.24 no.9
• /
• pp.1268-1273
• /
• 2011

The present study was conducted to determine a feasible method of protein concentrate extraction from rice bran (RBPC) and its effect as a substitution for skim milk in early weaning pig diets. An investigation to extract protein concentrate from full fat rice bran was undertaken to determine the best ratio of water and rice bran, the amount of NaOH and a HCl solvent to use in a simple paddle-type mixer with modified spinning to produce RBPC. The results stated that the best ratio for water mixing in the RBPC extraction process was 1:5 with 20 g NaOH and 30 min in a paddle-type mixer at 300 rpm. A mix of 250 ml 0.2 N HCl was optimum for neutralization and protein precipitation. After the fluid was spun out with a washing machine, the sediment was left for 12-14 hours to complete the filtration. One kilogram of rice bran could produce an average of 324.5 gram RBPC and it contained 3.40% ash, 496.48 kcal of GE/100 gram, 1.94% crude fiber, 28.20% ether extract, 7.64% moisture and 16.66% crude protein, respectively. A total of 45 crossbred piglets, weaned at 3 weeks of age were allotted into control diet (A) and dietary treatments formulated with a four different rates of RBPC substitution for skim milk at a percentage of 25 (B), 50 (C), 77 (D) and 100 (E) respectively, in a randomized complete block (RCB) design. All piglets had free access to feed and water until 8 week of age when the experiment ended. Feed intake, average daily gain, growth rate and feed efficiency were not affected by dietary treatments. Blood test parameters after completion of the growth trial indicated normal health. Even though the mean of cell hemoglobin concentration was significantly different between treatments (p<0.05) it was still within the normal range. The cost difference for BW gain of 100% RBPC substituted for skim milk in the weaning diet was approximately 35% lower than that of the control and the relative cost of production was 96.67, 92.85, 70.75 and 64.48% lower for the replacement of 25, 50, 75 and 100% of skim milk respectively. These results implied that this technology is feasible for use by small scale farmers to improve their self-reliance.

• Journal of the Korea Concrete Institute
• /
• v.17 no.5 s.89
• /
• pp.709-716
• /
• 2005

The objective of this study is to develop a high ductile fiber reinforced mortar, ECC(Engineered Cementitious Composite) with using raw material commercially available in Korea. A single fiber pullout test and a wedge splitting test were employed to measure the bond properties in a matrix and the fracture toughness of mortar matrix respectively, which are used for designing mix proportion suitable for achieving strain-hardening behavior at a composite level. Test results showed that the properties tended to increase with decreasing water-cement ratio. A high ductile fiber reinforced mortar has been developed by employing micromechanics-based design procedure. Micromechanical analysis was initially peformed to properly select water-cement ratio, and then basic mixture proportion range was determined based on workability considerations, including desirable fiber dispersion without segregation. Subsequent direct tensile tests were performed on the composites with W/C's of 47.5% and 60% at 28 days that the fiber reinforced mortar exhibited high ductile uniaxial tension property, represented by a maximum strain capacity of 2.2%, which is around 100 times the strain capacity of normal concrete. Also, compressive tests were performed to examine high ductile fiber reinforced mortar under the compression. The test results showed that the measured value of compressive strength was from 26MPa to 34 MPa which comes under the strength of normal concrete at 28 days.