• Journal of the Korean Applied Science and Technology
• /
• v.33 no.4
• /
• pp.615-626
• /
• 2016

In the paper, mild solvent soluble alkyl group modified epoxy resins were prepared via a three-step method; (1) the condensation reaction of dodecyl phenol (DP) and formaldehyde, (2) the crosslinking reaction of dodecyl phnol novolac compound (DPC) and bisphenol A diglycidyl ether, (3) the dodecyl phenol novolac epoxy resins containing fatty acid (DPFA) was prepared by introducing fatty acid to DPC. Equivalent ratios of DP and formaldehyde were 1.25~1.333/1.0. Equivalent ratio of DPC and bisphenol A diglycidyl ether (YD-128) was 1.0/2.0. Reactivity, viscosity, molecular weight, solvent solubility, and physical properties of DPFA were investigated. The result show that as the number of aromatic ring of DPFA increased, viscosity increased and solvent solubility improved. When we test the properties of coatings by blending the synthesized DPFA with a white pigment, DPFAC-5 using triphenylphosphine (TPP) as a ring-open catalyst showed optical performance for drying time, adhesion, hardness, impact resistance, acid resistance and storage stability.

• Journal of the Korean Applied Science and Technology
• /
• v.33 no.4
• /
• pp.634-646
• /
• 2016

In this work, modified epoxy resins which were well melted in mild solvent were synthesized and solubility assessment was carried out for synthesized epoxy resins. Bisphenol-A type, phenol novolac type and ortho-cresol novolac type epoxy resins were used and fatty acid, dodecyl phenol (DP) and toluene diisocyanate (TDI) were added for synthesis of modified epoxy resins containing fatty acid (MEFA). Composition was epoxy resin/fatty acid = 1.0/0.5 and fatty acid/DP = 0.25/0.25 by equivalent weight and twelve MEFAs were synthesized according to epoxy resins. Viscosity and solubility were measured for twelve MEFAs. As a result, solubility of MEFA was excellent for mild solvent according to increasement of contents of benzene ring, glycidyl group and carbon number of alkyl group. And physical properties were measured for each coating of paints after preparing transparent paints of MEFA to melt well in mild solvent among twelve MEFAs. As a result, they showed an optimal performance on conditions of equivalent ratio of bisphenol-A type epoxy resin/fatty acid/DP/TDI; 1.0/0.25/0.25/0.5 and equivalent ratio of phenol novolac type epoxy resin/fatty acid/DP; 1.0/0.25/0.25 for drying time, adhesion, hardness, impact resistance and alkali resistance.