• The Korean Journal of Ceramics
• /
• 제7권2호
• /
• pp.63-69
• /
• 2001

We investigated strength degradations from cyclic contact fatigue in self-toughened glass-ceramics. Hertzian indentation was used to induce cyclic contact load. Dynamic fatigue was also performed with changing stress rates from 0.01 to 10000 MPa/sec. After that, strength data and fracture origins were analysed. As the number of contact cycles increased or stressing rate decreased, severe strength degradation occurred by as much as 50% because of radial cracks developed from microcrack coalescence.

• 터널과지하공간
• /
• 제21권4호
• /
• pp.307-319
• /
• 2011

교통, 굴착, 발파 등에 의한 반복하중은 오랜 시간에 걸쳐서 암석의 미세균열 성장을 일으키며, 암석의 강도 등에 영향을 미치기 때문에 반복하중에 의한 균열의 성장, 결합은 장시간 안정성 평가에 중요한 영향을 미친다. 본 연구에서는 두 개의 초기 균열을 가지는 모사 암석 시험편에 단조증가 및 반복하중을 가하여 하중 조건에 따른 균열의 성장과 결합유형을 조사하였다. 단조증가하중, 반복하중 시험 모두에서 서로 유사한 날개균열 시작 위치, 날개균열 각도, 균열 성장 순서, 균열 결합 형태가 관측되었다. 본 연구에서 관찰된 균열 결합은 크게 3종류로 전단에 의한 결합, 1개의 날개 혹은 인장 균열에 의한 결합 그리고 2개의 날개 혹은 인장 균열에 의한 결합으로 요약될 수 있다. 피로균열은 반복하중 시험에서만 발생하였으며 성장 방향은 이차균열과 유사하게 초기균열과 같은 방향 혹은 하중방향과 직교인 수평방향으로 관찰되었다.

• Composites Research
• /
• 제12권5호
• /
• pp.1-11
• /
• 1999

본 연구는 단섬유보강 금속복합재료의 피로 및 주기적 거동에 관한 연구로서, 가압용침법을 이용하여 제조된 Al6061과 이를 기지금속으로 사용한 단섬유보강 Al/$Al_2O_3$-15% 복합재료의 주기적변형(cyclic deformation)과 피로거동(fatigue behavior)에 대해서 실험적으로 고찰하였다. Al/$Al_2O_3$ 복합재로의 피로강도는 210MPa로 나타났고 기지금속은 170MPa로 나타났다. 영구소성변형에 의한 합변위는 피로수명 초기 5%이내에서 대부분 발생하며 파단시의 합변위는 복합재료와 기지금속 모두 축적된 소성변형으로 인하여 인장시험에서의 연신율에 비해 작은 값을 가진다. 금속복합재료의 주기적 변위는 보강재가 전위 전파의 저지역할을 함으로써 기지금속에 비하여 다소 감소하는 것으로 나타났다. 파면관찰결과 기지금속의 경우 금속복합재료에 비해 전체 시험편 단면에서 넓은 영역에서 균열전파 형태를 관찰할 수 있었으며, 또한 금속복합재료의 파면에서는 연속적인 피로하중에 의한 기지금속과 보강재간의 분리(debonding)등의 결과로 보강재가 뽑혀나간 흔적이 관찰되고 있다.

• 한국안전학회지
• /
• 제9권1호
• /
• pp.9-18
• /
• 1994

In this study, we conducted experimental tests to evaluate fracture behaviors of fresh-butt welded metal by Acoustic Emission technique. We selected similar welding and dissimilar welding process, the one welded for SM45C, SS41 and SUS304 of each material, the other for SM45C and SS41, SM45C and SUS304 and SS41 and SUS304. The fracturing processes of weld metal were estimatied through the fracture toughness test with compact tension specimens and fractography analysis. In ASTM test method E-399, type I curves for materials of this study were obtained by load-cod diagram of fracture toughness test. and 5% offset load( $P_{5}$) was estimated as the estimated crack initial load( $P_{Q}$), The estimated crack initial load( $P_{Q}$) of similar welding materials generally lower than base matal, and then SM45C appeared greatly in decreasing rate of PB, SS41 and SUS304 appeared in order. $P_{Q}$ of dissimilar welding materials were lower than the similar welding materials. $P_{Q}$ of welding of SM45C and SS41 appeared in small, SUS304 and SS41 appeared greatly in dissimilar welding materials. In fracture toughness test, AE counts increased before the inflection point of the slope, decreased after that. It was found that increasing of AE counts were due to the microcrack formation at the crack tip near the $P_{5}$ point through AE data. For welding materials in this study, both low and high AE amplitude appeared simulataneously. It was confirmed that the low AE amplotude was due to formation of micro void, micro crack or micro dimple, the high AE amplitude was caused by microvoid coalescence and quasi-cleavage fracture through analyses of fractograpy.apy.apy.apy.