• 한국정밀공학회지
• /
• 제27권11호
• /
• pp.7-16
• /
• 2010

In this study, wire was used as the filler material for the laser repair welding, and the phenomenon in which the supplied filler material was melted and beaded down into the specimen was examined with varying laser powers and welding speeds. The optimal processing condition was found to be the laser power of 1,300 W, the welding speed and feed wire supply speed of 0.5 ml/in and the defocused distances of +2mm. At this time, the heat input(E) was $65{\sim}75\;J/mm^2$, and no internal defect occurred. When repair welding was carried out as the optimal processing for the part that had an external defect with the radius of 2mm, the filler metal was melted, resulting in the volume smaller than the defect part and thus causing the part unfilled. Therefore, it was found to be necessary to carry out repair welding two to three times by multiple passes rather than does it only once by single pass.

• 대한치과기공학회지
• /
• 제28권1호
• /
• pp.19-26
• /
• 2006

The effect of Nb on interfacial bonding characteristics of Ni-Cr alloy for porcelain fused to metal crown (PFM) has been studied in order to investigate oxide layer. A specimens of Ni-Cr alloy, which is 0.8mm in thickness, within the porcelain furnace of 1,000$^{\circ}C$ with four tests such as air, vacuum, air for 5 minutes and vacuum for 5 minutes in order to examine an oxide behavior of alloy surface generated by the adding of Nb to be controlled at a rate of 0, 1, 3 and 5. Oxide film was observed form of the fired specimens with scanning electron microscope (SEM), and at the same time it measured Electron Probe Micro Analyzer (EPMA). The result of this study were as follows: 1. Cr oxide film and Nb oxide film were observed from the surface of specimen to be controlled at a rate of Nb 1%. 2. Nb oxide film was observed from the interface of specimens to be controlled at a rate of Nb 1% and 3%. 3. The stability of oxide films that treated in air were more stable than treated under vacuum.

• 동력기계공학회지
• /
• 제21권3호
• /
• pp.102-107
• /
• 2017

A tungsten inert gas (TIG) welding method was used for the bonding of stainless steel. TIG welding using inert gas (He or Ar gas) is a method to prevent oxidation and nitriding of materials and to combine non-ferrous metals. This method has the advantage of obtaining a smooth weld surface. In this study, the welding characteristics of 304 stainless steel welded by TIG welding method were analyzed by using nondestructive technique. Ultrasonic and Acoustic Emission (AE) was applied to evaluate the micro-damage of TIG welded 304 stainless steel. The velocity and damping coefficient of ultrasonic wave showed a slight difference in HAZ, which is the welding part of stainless steel. The AE parameters of average frequency, rise time and event were analyzed for the dynamic behavior of stainless steel during loading. Optimal AE parameters for evaluating the degree of damage to the specimen have been derived. Fractograph and metal structures of 304 stainless steel using SEM and optical microscope were discussed.

• 한국정밀공학회지
• /
• 제18권9호
• /
• pp.122-130
• /
• 2001

Induction surface hardening is widely used to enhance local strength and hardness. However, most research is only to have a focus on fatigue life and fatigue behavior is not so much studied. So, in this study, Cr-Mo steel alloy(SCM440) was used to show the effect of residual stress and micro hole on the fatigue strength fur base metal and induction surface hardened specimen. In addition, the fatigue characteristic between surface hardened and fully hardened steel is somewhat different. It is caused by hardness distribution, residual stress and inclusions etc.. The modification of prediction equation of fatigue strength is proposed and predicted results show very good accuracy. A $textsc{k}$, which is calculated 1.46, is introduced to consider the effect of stationary crack with defect. A new method of modifying residual stress is proposed to examine the mean stress effect under fatigue loading.

• 대한기계학회논문집A
• /
• 제34권10호
• /
• pp.1463-1470
• /
• 2010

미세성형 기술은 다양한 소재의 활용, 높은 생산성과 적은 재료의 손실, 고품질 생산과 같은 기존 소성가공의 장점을 실현할 수 있기 때문에 마이크로 크기의 부품생산에 매우 유망한 기술로 간주되고 있다. 하지만 기존의 매크로 영역에서 축적된 많은 기술과 노하우들은 소재의 크기가 마이크로 단위에 줄어듦에 따라 나타나는 소위 "크기효과"로 인해 미세성형 공정에 그대로 적용될 수는 없다. 따라서, 본 연구에서는 마이크로 영역에서 나타나는 재료거동의 크기효과를 이론적, 실험적 연구를 통하여 고찰하였다. 다양한 두께의 구리시편에 열처리를 실시하여 결정립의 크기를 다양화 하였고, 인장시험을 통하여 시편의 두께와 결정립의 크기가 유동응력에 미치는 영향을 고찰하였다. 또한 이러한 크기효과의 정량적인 분석을 위하여 마이크로 및 매크로 영역에서 적용 가능한 소재의 유동응력 모델을 이론적으로 도출하였다.

• 구강회복응용과학지
• /
• 제22권2호
• /
• pp.125-136
• /
• 2006

Statement of problem. The success of the bonding between electroforming gold and resin is dependent on the surface-conditioning technique but its effective technique has net been studied widely. Purpose. The purpose of the study was to evaluate the bond strength between the electroforming gold and resin with varying the surface-conditioning technique. Materials and methods. Sixty rectangular shaped metal specimens were made and one side of each specimen were gold hard plated. The sand-blasted specimens were divided into four experimental groups with fifteen specimens in each group and were treated as follows. Group 1: Silicoating (Rocatec, 3M ESPE)+ Sinfony (3M ESPE), Group 2: SR Link+ SR Adoro (Ivoclar Vivadent), Group 3: Tin plating (Microtin, Danville Engineering)+ SR Link+ SR Adoro, Group 4: Tin plating (Micro tin, Danville Engineering)+ Silicoating (Rocatec)+ Sinfony. Shear bond strength at metal-resin interface were measured using universal testing machine. Energy Dispersive x-ray analysis was done and scanning electron microscope images were taken and observed. Results and Conclusion. The following conclusions were drawn. 1. The mean shear bond strength values in order were 11.69MPa (Group 2), 22.35MPa (Group 3), 22.40MPa (Group 1) and 27.71MPa (Group 4). There was no significant difference in Group 1, Group 3 and Group 4(P>0.05). 2. In the EDX line analysis, the Au was detected on the surface of all specimen. $SnO_2$ showed on the surface of Group 2 and $SiO_2$ was detected on the surface of Group 1. 3. Increasing of roughness by sandblasting(Group 2), formation of micro-irregularities and tin crystals by electrolytic tin plating(Group 3) and formation of surface irregularities and $SiO_2$ layer(Group 1,4) were observed in SEM photo. 4. Tin plating(Group 3) and Rocatec treatment(Group 1) showed clinically effective shear bond strength(>20MPa), but when the two surface conditioning method were used together higher bond strength were achieved.

• 한국화재소방학회논문지
• /
• 제16권1호
• /
• pp.77-83
• /
• 2002

본 연구의 목적은 UL(미국보험협회)에 규정된 암모니아 대기상태에서 측벽형 스프링클러 헤드 디플렉터의 응력부식균열을 막기 위한 방안을 제시하는 것이다. 성형 후처리로서 성형제품 그대로와 샌드블래스팅 처리한 것, 그리고 풀림 열처리를 한 것 등 3가지에 대하여 부식시험을 실시하였다. 금속현미경으로 시편을 관측한 결과 잔류응력이 부식균열을 일으키는 주요원인이며, 극심한 부식조건에서 발생할 수 있는 잔류응력을 적절한 열처리를 통해 제거하거나 감소시킬 수 있어 파손을 방지할 수 있다는 것을 확인 하였다.

• 한국레이저가공학회지
• /
• 제18권2호
• /
• pp.1-4
• /
• 2015

This study is related to the surface hardening treatment to spheroidal graphite cast iron for die by using high power diode laser. Laser device used in this experiment is capable of real-time laser power control. This is because the infrared temperature sensor (two color pyrometer) attached to the optical system measures the surface temperature of specimen and adjusts the laser power in real time. The surface treatment was carried out with the change of heat treatment temperature at the beam travel speed 3 mm/sec. Hardened width and depth was measured and hardened zone was analyzed by micro vickers hardness test in order to research the optimum condition of heat treatment. The changes in microstructure of the hardened zone also was examined. As a result of hardness measurement and observations on microstructure of hardened zone, hardness increased over three times as compared with base metal because the martensite was formed on the matrix structure.

• Journal of Advanced Marine Engineering and Technology
• /
• 제24권6호
• /
• pp.70-77
• /
• 2000

In this paper, the effect of solution and age heat treatment to the corrosion behavior for the Ti-6Al-4V alloy were studied by cyclic polarization methods. Ti-6Al-4V was solution heat treated at $1,066^{\circ}C$ and $966^{\circ}C$ for 5 hours, and followed by age heat treated at $650^{\circ}C$, $600^{\circ}C$ and $550^{\circ}C$ with 1, 2, 4, 8 and 16 hours under vacuum environment. Test solution was 3.5% NaCl with temperature $25^{\circ}C$. The obtained results were as follows: 1. Base metal was exhibited higher electrical charge than that of solution and aged material. With decrease of solution-treatment temperature from 1066 to $966^{\circ}C$, the electrical charge was increased due to softening of micro structure. 2. The corrosion resistance of specimen that solution treated at $966^{\circ}C$ for 5 hours and age heat treated at 650, 660 and $550^{\circ}C$ were increased with increase of aging time to 4, 8 and 16 hours respectively, and then decreased. 3. In case of 316L stainless steel, measured charge and corrosion potential was 0.0627 coulomb and -614 mV respectively. Corrosion resistance of Ti-6Al-4V was higher than that of 316L.

• 분석과학
• /
• 제13권5호
• /
• pp.565-572
• /
• 2000

파장분산형 엑스선분광분석기에 의한 Xe의 전자탐침미세분석시 표준물질에 대해 기술하였다. 실험결과 순수금속 표준시편을 사용할 수 없는 Cs, I, Ba의 표준물질로는 Csl와 $BaCO_3$가 가장 적당한 것으로 나타났다. 빔전류량 10-30 nA에서 Csl, CsBr로부터 측정한 Cs의 엑스선 세기는 빔전류량에 비례하였다. PET 결정 사용시 In-Nd 원소들의 원자번호 대 엑스선 세기간의 직선성은 가속전압 25-30 kV 범위에서 직선회귀 계수 R=0.99 이상의 좋은 상관성을 보였다. 직선회귀식으로 구한 Xe의 엑스선 세기 표준값은 가속전압 25 kV에서 Te의 엑스선 세기 표준값 보다 1.095배 높게 나타났다.