• 한국전기전자재료학회논문지
• /
• 제17권9호
• /
• pp.960-966
• /
• 2004

On the bases of the results from "Additive Coating of BaTiO$_3$ Powder using Sol Coating Method I", experimental condition was defined. Representative additives for BaTiO$_3$, that is to say, Mg, Ca and Mn were experimented. The sources of the metal ion were used by organometal complex. As added it, the stability of BaTiO$_3$ sol was evaluated. Mg and Ca were stable, however, The solubility limit of Mn-ATH was 0.05 mol ratio in Mn-ATH/sol. The solubility limit of Mg ion in BaTiO$_3$ was lower than 2 mol%. From the x Ray diffraction patterns, lattice parameters were different with temperature and additives, because the solubility of metal ion was varied in BaTiO$_3$. The dielectric constant of BaTiO$_3$ powders which coated with the 1.5 mol% Mg and calcined at 1200$^{\circ}C$ was increased with 20%.

• 한국세라믹학회지
• /
• 제41권12호
• /
• pp.929-932
• /
• 2004

페로브스카이트 단일상의 PMN 계 복합화합물을 제조하기 위하여 일반적으로 소량의 MgO가 과잉으로 사용되며, 잉여 MgO는 주로 입내에 석출되며 소결을 저해하는 것으로 알려져 있다. 본 연구에서는 MgO 대신 $(MgCO_3)_4{\cdot}Mg(OH)_2{\cdot}5H_{2}O$을 사용하여 고상법으로 제조한 PMN-PT-BT(PBT) 전구체 분말을 $500^{\circ}C/1h$에서 열처리한 후, MgO 졸로 표면 개질하여, 과잉의 MgO가 소결 및 물성에 미치는 영향을 조사하였다. 소량의 MgO 졸($0.5{\sim}1.0wt\%$)은 $1000^{\circ}C$ 이하의 온도에서 소결을 크게 촉진시켰다. $0.5wt\%$의 졸이 사용된 PBT 분말은 $900^{\circ}C/2h$ 소결로 소결밀도 $7.62g/cm^3$, 유전율 14800, 유전손실 $1.1\%$를 나타내었으며, 이는 PBT의 $1000^{\circ}C/2h$ 소결체의 물성과 흡사하였다. 또한 MgO 졸로 첨가된 과잉의 MgO는 삼중점과 입계에 주로 석출되어 입성장을 제어함을 알 수 있었다.

• 한국세라믹학회지
• /
• 제32권3호
• /
• pp.305-312
• /
• 1995

Thin films of Pb(Mg, Zn)1/3Nb2/3O3 were fabricated by spin coating the Pb-Mg-Zn-Nb-O complex alkoxide sols on(111) Pt-coated MgO (100) planes. It was observed that the content of H2O and the rheological characteristics of sol greatly influenced the orientation of perovskite grains after thin-film formation. A strong preferential orientation of (100)-type planes of the perovskite grains was obtained for the sol aged for 15 days with the molar ratio of H2O to total metal alkoxides=2. As small angle X-ray scattering experiment in the Porod region was performed to correlate the observed preferential orientation with the network structure of precursors at various stage of aging. It was shown that the degree of branching of the Pb-Mg-Zn-Nb-O precursor chain had a direct effect on the preferred oreintation, and weakly branched precursor systems led to highly oriented grains after thin-film formation.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.281-282
• /
• 2007

$Mg_4Nb_2O_9$ (MN) ceramics have been prepared by a sol-gel method. The powder characteristics, phase evolution, and microwave dielectric properties of the MN were investigated in various processing conditions such as sol-gel compositions, calcination, and sintering temperatures. A Qxfo value of 111,717 GHz with a ${\varepsilon}_r$ of 10.59 and a ${\tau}_f$ of $+1.736\;ppm/^{\circ}C$ was obtained after sintering at $1300^{\circ}C$ for 5 h.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1999년도 추계학술발표강연 및 논문개요집
• /
• pp.34-34
• /
• 1999

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2000년도 추계총회,초청강연,특별강연,연구발표회
• /
• pp.197.2-197
• /
• 2000

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2000년도 추계총회,초청강연,특별강연,연구발표회
• /
• pp.178-178
• /
• 2000

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2002년도 춘계 학술발표강연 및 논문개요집
• /
• pp.41-41
• /
• 2002

• 한국전기전자재료학회논문지
• /
• 제33권3호
• /
• pp.214-218
• /
• 2020

In this study, Mg_xZn_1-xO thin films, which can be applied not only to active layers of light-emitting devices (LEDs), such as UV-LEDs, but also to solar cells, high mobility field-effect transistors, and power semiconductor devices, are fabricated using the sol-gel method. ZnO and Mg_0.3Zn_0.7O solution synthesized by the sol-gel method and the thin film were grown by spin coating on a Si (100) substrate and sapphire substrate. The solutions are synthesized by dissolving precursor materials in 2-methoxyethanol (2-ME) solvent, and then monoethanolamine (MEA) was added to the mixed solution as a sol stabilizer. Zinc acetate dihydrate is used as a ZnO precursor, while Mg nitrate hexahydrate and Mg acetate tetrahydrate are used as an MgO precursor. Then, the optical and structural characteristics of the fabricated thin films are compared. The molar concentration of the Zn precursor in the solvent is fixed at 0.3 M, and the amount of the Mg precursor is 30% of Mg²⁺/Zn²⁺. The optical characteristics are measured using an UV-vis spectrophotometer, and the transmittance of each wavelength is measured. Structural characteristics are measured using X-ray diffraction (XRD) and transmission electron microscopy (TEM). Composition analyses are performed using energy dispersive X-ray spectroscopy (EDS). The Mg_0.3Zn_0.7O thin film was well formed at the ratio of the Mg precursor added regardless of the type of Mg precursor, and the c-axis of the thin film was decreased, while the band gap was increased to 3.56 eV.

• 한국세라믹학회지
• /
• 제39권7호
• /
• pp.687-692
• /
• 2002

단일상 페로브스카이트 PMN-PT 분말 합성 과정에서 전구체 분말의 표면을 소량의 magnesia 졸로 코팅하여 구형의 분말을 제조하고자 시도하였다. 질량 감소가 더 이상 발생하지 않도록 정량의 혼합 분말을 55$0^{\circ}C$/lh 열처리하여 얻은 전구체 분말을 0.3-1.0wt% MgO에 해당하는 magnesia졸과 혼합한 후 80$0^{\circ}C$/lh 하소하여 페로브스카이트 단일상 PMN-PT 분말을 얻었다. MgO(0.3)일 경우는 <0.3$\mu\textrm{m}$와~2$\mu\textrm{m}$의 두 종류 크기의 분말로 나타나나, MgO(0.6)과 MgO(1.0)의 경우는 0.5-0.8$\mu\textrm{m}$의 구형 분말을 응집없이 얻을 수 있었다.