• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2006.04a
• /
• pp.155-155
• /
• 2006

• Transactions of Materials Processing
• /
• v.8 no.5
• /
• pp.482-490
• /
• 1999

7000 series Al alloy with good mechanical properties has been focused with tendency to reduce the components weight of aircraft and automobile. However, it is difficult to manufacture a sound extruded product because of segregation, grain growth, casting defect, surface defect, decreasing extrudability and so on. The objective of this study is to manufacture a new 7000 al alloy more than the extrudability of A7N01 and A7003 through controlling the weight (%) Mg, Zn, Si. Hot extrusion experiments on the axisymmetric rod are performed in 500℃ and also performed analysis of the same process using unmerical analysis method, a coupled rigid-thermoviscoplastic finite element method. Extrusion limit diagram was obtained for the developed alloy by FE-simulation in order to define the relationship of extrusion speed and initial billet temperature.

• Journal of Advanced Marine Engineering and Technology
• /
• v.23 no.3
• /
• pp.360-368
• /
• 1999

The paper describes spectroscopic characteristics of plasma induced in the pulsed YAG laser welding of alloys containing a large amount of volatile elements. The authors have conducted the spectroscopic analyses of laser induced Al-Mg alloys plasma in the air and argon atmosphere. In the air environment the identified spectra were atomic lines of Al, Mg, Cr, Mn, Cu, Fe and Zn and singly ionized Mg lines as well as the intense molecular spectra of ALO and MgO formed by chemi-cal reactions of evaporated Al and Mg atoms from the pool surface with oxygen in the air. In argon atmosphere MgO and AlO spectra vanished but AlH spectrum was detected. the hydrogen source was presumable hydrogen dissolved in the base metals water absorbed on the surface oxide layer or $H_2$ and $H_2O$ in the shielding gas. The resonant lines of Al and Mg were strongly self-absorbed in particular self-absorption of the Mg line was predominant. These results show that the laser induced plasma was made of metallic vapor with relatively low temperature and high density.

• Journal of the Korean Society for Heat Treatment
• /
• v.19 no.2
• /
• pp.96-102
• /
• 2006

Development of Rotation-Cylinder Method(RCM) is given for Mg-Al-Zn-X(X=Sr) alloys, identifying some of the key factors that need to be controlled and indicating subsequent casting processes. Effects of Sr addition on the microstructure and mechanical properties of as-cast and T6 heat-treated Mg-Al-Zn-X alloys fabricated by the RCM were investigated. The microstructural and mechanical characterizations were performed by utilizing optical microscope, scanning electron microscope, transmission electron microscope, hardness test and ultimate tensile test. The solution and aging treatment time was varied to optimize the T6 heat treatment conditions, and experimental results were discussed. The grain size of Sr containing alloys was refined by increasing Sr content, but the tensile and yield strengths were increased by addition up to 1wt% Sr.

• Korean Journal of Materials Research
• /
• v.23 no.10
• /
• pp.574-579
• /
• 2013

The milling and particulate characteristics of Al alloy-$Al_2O_3$ powder mixtures for a reaction-bonded $Al_2O_3$ (RBAO) process were studied. A commercially available prealloyed Al powder with Zn, Mg, Cu and Cr alloying elements (7475 series) was mixed with a calcined sinter-active $Al_2O_3$ powder and then milled in centrifugal milling equipment for ~48 hrs. The Al alloy-$Al_2O_3$ powder mixtures after milling were characterized and evaluated in various ways to reveal their particulate characteristics during milling. The milling efficiency of the Al alloy increased with a longer milling time. Comminution of the Al alloy particles started with its elongation, showing a high aspect ratio. With a longer milling time, the elongated Al alloy particle changed in terms of its shape and size, becoming equiaxially fine particles. Regardless of the milling efficiency of the Al alloy particles, all of the Al alloy particles repeatedly experienced strong plastic deformation during milling, giving rise to higher density of surface defects, such as microcracks, and leading to higher residual microstress within the Al alloy particles. The chemical reactions, oxidation behavior and hydration behavior of the Al alloy particles and the hydrolysis characteristics of their reaction with the environment were also observed during the milling process and during the subsequent powder handling steps.

• Korean Journal of Materials Research
• /
• v.28 no.9
• /
• pp.534-538
• /
• 2018

The annealing characteristics of a cold rolled Al-6.5Mg-1.5Zn alloy newly designed as an automobile material is investigated in detail. The aluminum alloy in the ingot state is cut to a thickness of 4 mm, a total width of 30 mm and a length of 100 mm and then reduced to a thickness of 1 mm (reduction of 75 %) by multi-pass rolling at room temperature. Annealing after rolling is performed at temperatures ranging from 200 to $400^{\circ}C$ for 1 hour. The tensile strength of the annealed material tends to decrease with the annealing temperature and shows a maximum tensile strength of 482MPa in the material annealed at $200^{\circ}C$. The tensile elongation of the annealed material increases with the annealing temperature, while the tensile strength does not, and reaches a maximum value of 26 % at the $350^{\circ}C$ annealed material. For the microstructure, recovery and recrystallization actively occur as the annealing temperature increases. The recrystallization begins to occur at $300^{\circ}C$ and is completed at $350^{\circ}C$, which results in the formation of a fine grained structure. After the rolling, the rolling texture of {112}<111>(Cu-Orientation) develops, but after the annealing a specific texture does not develop.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.322-323
• /
• 2012

This study discussed the formation of phosphate conversion coatings on AZ31 Mg alloy (AZ31) from the zinc phosphating bath with various concentrations of sodium fluoride (NaF). The effects of NaF on the formation, structure, composition and electrochemical behavior of the phosphate coatings were examined using scanning electron microscopy (SEM), X-ray diffraction (XRD) weight balances, open circuit potential (OCP) transients, potentiodynamic polarization curves and immersion test. The coatings were composed of two layers: an outer $Zn_2(PO_4)_3.4H_2O$ (hopeite) crystal layer and an inner amorphous of $MgZn_2(PO_4)_2$. NaF concentration is emphasized to be highly effective in the formation of the hopeite crystal and etching and coating rates. Potentiodynamic polarization and immersion test showed that the coatings formed in the zinc phosphating bath with addition of NaF have much higher corrosion resistance than bare AZ31.

• Journal of the Korean institute of surface engineering
• /
• v.41 no.3
• /
• pp.121-128
• /
• 2008

High strength 7xxx aluminum alloys have been applied to automotive bump back beam of the some limited model for light weight vehicle. The aluminum bump back beam is manufactured through extrusion, bending and welding. The residual stress given on these processes combines with the corrosive atmosphere on the road spreaded with corrosive chemicals to melt snow to occur the stress corrosion cracking. The composition of commercial 7xxx aluminum has Zn/Mg ratio about 3 and Cu over 2 wt% for better strength and stress corrosion cracking resistivity. But this composition isn't adequate for appling to the automotive bump back beam with high resistance to extrusion and bad weldability. In this study the composition of 7xxx aluminum alloy was modified to high Zn/Mg ratio and low Cu content for better extrusion and weldability. To estimate the resistivity against stress corrosion cracking of this aluminum alloy by slow strain rate test, the corrosion atmosphere and strain rate separate the stress corrosion cracking from conventional corrosion must be investigated. Using 0.6 Mol NaCl solution on slow strain rate test the stress corrosion cracking induced fracture was not observed. By adding 0.3% $H_2O_2$ and 0.6M $Na_2SO_4$ to 1M NaCl solution, the corrosion potential and current density of polarization curve moved to active potential and larger current density, and on the slow strain rate test the fracture energy in solution was lower than that in pre-exposure. These mean the stress corrosion cracking induced fracture can be estimated in this 1M NaCl + 0.3% $H_2O_2$ + 0.6M $Na_2SO_4$ solution. When the strain rate was below $2{\times}10^{-6}$, the stress corrosion cracking induced fracture start to be observed.

• Proceedings of the Korean Institute of Industrial Safety Conference
• /
• 1998.11a
• /
• pp.9-14
• /
• 1998

고강도 알루미늄 합금은 기술의 진보에 따라서 이용도가 높은 매우 중요한 재료로서, 잘 알려진 적용분야로서는 항공우주산업, 고속회전체, 항공기용재 등으로 많이 사용되고 있다. 고강도 알루미늄 합금은 Al-Cu-Mg(2000 series)를 기초로 둔것과 Al-Zn-Mg-Cu(7000 series)를 기초로 둔 것등이 있다. (중략)

• Journal of Power System Engineering
• /
• v.15 no.1
• /
• pp.39-44
• /
• 2011

This study was to investigate the effects of stress ratio and anisotropy on Fatigue Crack Propagation(FCP) behavior of rolled magnesium alloy AZ31B. The experimental materials were a Mg-Al-Zn magnesium alloy. The FCP test was conducted on compact tension specimen by a servo-hydraulic fatigue testing machine in air at room temperature. Compact tension specimens were prepared from the extruded parallel and vertical rolling direction. The test condition was frequency of 10Hz and sinusoidal load stress ratios are 0.1 and 0.7. The FCP rates was automatically measured by a compliance method. In the case of the FCP of AZ31B, the FCP of both direction of LT and TL by anisotropy of specimens are almost same value. In lower stress ratio, the FCP of the LT, TL specimens are increased in lower ${\Delta}K$ region but higher ${\Delta}K$ regions are almost same value. Finally, the result of observed the surface crack, it expressed the quasi-cleavage fracture in lower ${\Delta}K$ region and straight mark on the aspect of the facet in high ${\Delta}K$ region.